Development of a Two-Stage Etching Procedure for Grain Analysis of Intermetallic Iron Aluminides (Fe-Al-Ta)

Entwicklung eines zweistufigen Ätzverfahrens zur Kornanalyse von intermetallischen Eisenaluminiden (Fe-Al-Ta)
E. Schaberger-Zimmermann, R. D. Pütz, E. Subašić and D. Zander
From the journal Practical Metallography

Abstract

The present work will introduce a novel two-step etching procedure for grain analysis of intermetallic iron aluminides. A grain boundary etching technique from the literature will be complemented by subsequent grain-contrast etching to visualize different grains in polarized light. The use of an XY-table for the acquisition of MosaiX images also enables grain analysis over the entire cross-section of the sample.

Kurzfassung

In der vorliegenden Arbeit wird ein neues zweistufiges Ätzverfahren zur Kornanalyse von intermetallischen Eisenaluminiden vorgestellt. Aufbauend auf einer Korngrenzenätzung aus der Literatur, wird eine nachgeschaltete Kornflächenätzung durchgeführt, um die verschiedenen Körner unter polarisiertem Licht zu visualisieren. Die Verwendung eines XY-Tisches zur Aufnahme von MosaiX-Bildern erlaubt zudem die Kornanalyse über den vollständigen Probenquerschnitt.

Acknowledgements

The authors would like to collectively thank the Federal Ministry for Economic Affairs and Energy (BMWi, Bundesministerium für Wirtschaft und Energie) for funding [03ET7077B] & [03ET7077A].

Danksagung

Die Autoren bedanken sich gemeinsam für die finanzielle Förderung beim Bundesministerium für Wirtschaft und Energie (BMWi) [03ET7077B] & [03ET7077A].

References / Literatur

[1] Hanus, P.; Bartsch, E.; Palm, M.; Krein, R.; Bauer-Partenheimer, K.; Janschek, P.: Intermetallics 18 (2010), 1379–1384 DOI: /10.1016/j.intermet.2009.12.03510.1016/j.intermet.2009.12.035Search in Google Scholar

[2] Morris, D.G.; Muñoz-Morris, M.A.: Adv. Eng. Mater. 13 (2011), 43–47 DOI: /10.1002/adem.20100021010.1002/adem.201000210Search in Google Scholar

[3] Zamanzade, M.; Barnoush, A.; Motz, C.: Crystals 6 (2016), 10 DOI: /10.3390/cryst601001010.3390/cryst6010010Search in Google Scholar

[4] Stoloff, N.S.: Mater. Sci. Eng. A 258 (1998), 1–14 DOI: /10.1016/S0921-5093(98)00909-510.1016/S0921-5093(98)00909-5Search in Google Scholar

[5] Palm, M.; Stein, F.; Dehm G.: Annu. Rev. Mater. Res. 49 (2019), 297–326 DOI: /10.1146/annurev-matsci-070218-12591110.1146/annurev-matsci-070218-125911Search in Google Scholar

[6] Kutz, T.N.; Zander, D.: Corrosion 73 (2017), 648–654 DOI: /10.5006/220810.5006/2208Search in Google Scholar

[7] Zander, D.; Pütz, R.D.: Intermetallics 126 (2020), 106924 DOI: /10.1016/j.intermet.2020.10692410.1016/j.intermet.2020.106924Search in Google Scholar

[8] Hotaˇr , A.; Palm, M.: Intermetallics 18 (2010), 1390–1395 DOI: /10.1016/j.intermet.2010.02.01410.1016/j.intermet.2010.02.014Search in Google Scholar

[9] Prokopčáková, P.; Švec, M.; Palm, M.: Int. J. Mater. Res. 107 (2016), 396–405 DOI: /10.3139/146.11135710.3139/146.111357Search in Google Scholar

[10] Wang, X.; Szpunar, J.A.: J. Alloys Compd. 752 (2018), 40–52 DOI: /10.1016/j.jallcom.2018.04.17310.1016/j.jallcom.2018.04.173Search in Google Scholar

[11] Yurek, G.J.; Eisen, D.; Garratt-Reed, A.: Metall. Mater. Trans. A 13 (1982), 473–485 DOI: /10.1007/BF0264335510.1007/BF02643355Search in Google Scholar

[12] Pint, B.A.; Leibowitz, J.; Devan, J.H.: Oxid. Met. 51 (1999), 181–197 DOI: /10.1023/A:101886240480010.1023/A:1018862404800Search in Google Scholar

[13] Pint, B.A.; Walker, L.R.; Wright, I.G.: Mater. at High Temp. 21 (2004), 175–185 DOI: /10.1179/mht.2004.02110.1179/mht.2004.021Search in Google Scholar

[14] Kant, R.; Prakash, U.; Agarwala, V.; Satya Prasad, V.V.: Bull. Mater. Sci. 39 (2016), 1827–1834 DOI: /10.1007/s12034-016-1326-410.1007/s12034-016-1326-4Search in Google Scholar

[15] Łyszkowski, R.; Bystrzycki, J.: Arch. Metall. Mater. 52 (2007), 347–350Search in Google Scholar

Received: 2020-12-09
Accepted: 2020-12-17
Published Online: 2021-03-31

© 2021 Walter de Gruyter GmbH, Berlin/Boston