Organic / inorganic bioactive materials Part I: Synthesis, structure and in vitro assessment of collagen/silicocarnotite biocoatings

Vladimir Hristov EMAIL logo , Lachezar Radev , Bisserka Samuneva and Georgi Apostolov
From the journal Open Chemistry

Abstract

The silicocarnotite, as an inorganic part of the coatings, has been synthesized using a polystep sol-gel method. The chemical composition of the prepared silicocarnotite sol is described as 58.12 CaO, 29.42 P2O5, 12.45 SiO2 (wt%), where Ca/P+Si = 1,67. The acid soluble type I collagen, as an organic part of the obtained coatings, was mixed with silicocarnotite powder in a weight ratio of 25:75 and 75:25 weight ratio without cross-linkage. The acidity of the obtained mixture was readjust with 25% NH4OH to pH = 9.0. The mixture was then dried at 37°C for 12 h.

The growth of B-type carbonate containing hydroxyapatite (B-type CO3HA) in which CO3 2+→PO4 3− on the surface of collagen/silicocarnotite coatings soaked in 1.5 simulated body fluid (1.5 SBF) was observed. The nucleation of B-type CO3HA was estimated on the obtained coatings after 3 days immersion in 1.5 SBF. The negatively charged carboxylate groups from the collagen surface may be responsible for the HA deposition. This was confirmed by the “red shift” of carboxylate groups of collagen molecules in the FTIR spectra. After soaking in 1.5 SBF, the morphology of prepared coatings and HA formation was observed by SEM.

[1] B.D. Ratnher, et al., Ceramics, Glasses and glassceramics (Academic Press, San Diego, 1996) 73 Search in Google Scholar

[2] L. Hench, J. Am. Ceram. Soc. 74[7], 1487 (1991) http://dx.doi.org/10.1111/j.1151-2916.1991.tb07132.x10.1111/j.1151-2916.1991.tb07132.xSearch in Google Scholar

[3] S. Levenberg, R. Langer, Advances in tissue engineering current topics in development biology (Academic Press, San Diego, 2004) 113 10.1016/S0070-2153(04)61005-2Search in Google Scholar

[4] A. Lawson, J. Czermuszka, Proc. Instn. Mech. Eng. part H, 413 (1998) 10.1243/0954411981534187Search in Google Scholar

[5] Y. Doi, et al., J. Biomed. Mater. Res. 31, 43 (1996) http://dx.doi.org/10.1002/(SICI)1097-4636(199605)31:1<43::AID-JBM6>3.0.CO;2-Q10.1002/(SICI)1097-4636(199605)31:1<43::AID-JBM6>3.0.CO;2-QSearch in Google Scholar

[6] T. Ushiki, Arch. Histol. Cytol. 65, 109 (2002) http://dx.doi.org/10.1679/aohc.65.10910.1679/aohc.65.109Search in Google Scholar

[7] C. Du, et al., J. Biomed. Mater. Res. 50, 518 (2000) http://dx.doi.org/10.1002/(SICI)1097-4636(20000615)50:4<518::AID-JBM7>3.0.CO;2-W10.1002/(SICI)1097-4636(20000615)50:4<518::AID-JBM7>3.0.CO;2-WSearch in Google Scholar

[8] I. Tcacencu, M. Wendel, J. Mater. Sci.: Mater. Med. 19, 2015 (2008) http://dx.doi.org/10.1007/s10856-007-3284-210.1007/s10856-007-3284-2Search in Google Scholar

[9] J. Chakraborty, M.K. Sinha, D. Basuw, J. Am. Ceram. Soc. 90[4], 1258 (2007) http://dx.doi.org/10.1111/j.1551-2916.2007.01596.x10.1111/j.1551-2916.2007.01596.xSearch in Google Scholar

[10] S. Itoh, et al., J. Biomed. Mater. Res. 54, 445 (2001) http://dx.doi.org/10.1002/1097-4636(20010305)54:3<445::AID-JBM190>3.0.CO;2-910.1002/1097-4636(20010305)54:3<445::AID-JBM190>3.0.CO;2-9Search in Google Scholar

[11] K.S. Tenhuisen, et al., J. Biomed. Mater. Res. 29, 803 (1995) http://dx.doi.org/10.1002/jbm.82029070410.1002/jbm.820290704Search in Google Scholar

[12] H.W. Sung, et al., J. Biomed. Mater. Res. 46, 20 (1999) http://dx.doi.org/10.1002/(SICI)1097-4636(19990915)46:4<520::AID-JBM10>3.0.CO;2-910.1002/(SICI)1097-4636(19990915)46:4<520::AID-JBM10>3.0.CO;2-9Search in Google Scholar

[13] N. Sasaki, et al., Biomaterals 10, 129 (1989) http://dx.doi.org/10.1016/0142-9612(89)90046-X10.1016/0142-9612(89)90046-XSearch in Google Scholar

[14] T. Gao, et al., J. Biomed. Mater. Res. 32, 505 (1996) http://dx.doi.org/10.1002/(SICI)1097-4636(199612)32:4<505::AID-JBM2>3.0.CO;2-V10.1002/(SICI)1097-4636(199612)32:4<505::AID-JBM2>3.0.CO;2-VSearch in Google Scholar

[15] D.A. Wahl, et al., J. Mater. Sci.: Mater. Med. 18, 201 (2007) http://dx.doi.org/10.1007/s10856-006-0682-910.1007/s10856-006-0682-9Search in Google Scholar

[16] J. Qian, R. Bhatnagar, J. Biomed. Mater. Res. 31, 545 (1996) http://dx.doi.org/10.1002/(SICI)1097-4636(199608)31:4<545::AID-JBM15>3.0.CO;2-F10.1002/(SICI)1097-4636(199608)31:4<545::AID-JBM15>3.0.CO;2-FSearch in Google Scholar

[17] A. Letic-Gavrilovic, A. Piatelli, K. Abe, J. Mater. Sci.: Mater. Med. 14, 95 (2003) http://dx.doi.org/10.1023/A:102209920853510.1023/A:1022099208535Search in Google Scholar

[18] M. Chapman, R. Bucholz, C. Cornell, J. Bone Joint Surg. Am. 79A, 495 (1997) 10.2106/00004623-199704000-00004Search in Google Scholar

[19] V. Amaro Martins, et al., Artif. Organs 22, 215 (1998) http://dx.doi.org/10.1046/j.1525-1594.1998.06004.x10.1046/j.1525-1594.1998.06004.xSearch in Google Scholar

[20] D. Bakos, M. Soldan, I. Harnandes-Fuentes, Biomaterials 20, 191 (1999) http://dx.doi.org/10.1016/S0142-9612(98)00163-X10.1016/S0142-9612(98)00163-XSearch in Google Scholar

[21] J.A. Schroeder, M. Brown, J. Biomed. Mater. Res.: Appl. Biomater. 48, 309 (1999) http://dx.doi.org/10.1002/(SICI)1097-4636(1999)48:3<309::AID-JBM15>3.0.CO;2-Z10.1002/(SICI)1097-4636(1999)48:3<309::AID-JBM15>3.0.CO;2-ZSearch in Google Scholar

[22] T. Kokubo, H. Kuchitani, S. Sakka, J. Biomed. Mater. Res. 24, 721 (1990) http://dx.doi.org/10.1002/jbm.82024060710.1002/jbm.820240607Search in Google Scholar

[23] Y. Ebisawa, et al., J. Mater. Sci.: Mater. Med. 1, 239 (1993) http://dx.doi.org/10.1007/BF0070108310.1007/BF00701083Search in Google Scholar

[24] M. Filguerias, G. Torre, L. Hench, J. Biomed. Mater. Res. 27, 445 (1993) http://dx.doi.org/10.1002/jbm.82027040510.1002/jbm.820270405Search in Google Scholar

[25] H. Kim, et al., Bull. Chem. Soc. Japan 69, 2387 (1996) http://dx.doi.org/10.1246/bcsj.69.238710.1246/bcsj.69.2387Search in Google Scholar

[26] K-Y. Lee, et al., Biomed. Mater. 1, R31 (2006) http://dx.doi.org/10.1088/1748-6041/1/2/R0110.1088/1748-6041/1/2/R01Search in Google Scholar

[27] Y-J. Lee, et al., J. Korean Ceram. Soc. 40, 1096 (2003) Search in Google Scholar

[28] A.J. Ruys, J. Aust. Ceram. Soc. 29, 71 (1993) Search in Google Scholar

[29] S.R. Kim, et al., Key Eng. Mater. 218–220, 85 (2002) http://dx.doi.org/10.4028/www.scientific.net/KEM.218-220.8510.4028/www.scientific.net/KEM.218-220.85Search in Google Scholar

[30] D. Arcos, J. Rodrigues-Carvajal, M. Valett-Regi, Chem. Mater. 16, 2300 (2004) http://dx.doi.org/10.1021/cm035337p10.1021/cm035337pSearch in Google Scholar

[31] F. Balas, J. Perez-Pariente, M. Valett-Regi, J. Biomed. Mater. Res. 66A, 364 (2003) http://dx.doi.org/10.1002/jbm.a.1057910.1002/jbm.a.10579Search in Google Scholar

[32] I.R. Gibson, S.M. Best, W. Bonfield, J. Biomed. Mater. Res. 44, 422 (1999) http://dx.doi.org/10.1002/(SICI)1097-4636(19990315)44:4<422::AID-JBM8>3.0.CO;2-#Search in Google Scholar

[33] Th. Leventouri, C.E. Bunaciu, V. Perdikatsis, Biomaterials 24, 4205 (2003) http://dx.doi.org/10.1016/S0142-9612(03)00333-810.1016/S0142-9612(03)00333-8Search in Google Scholar

[34] I.R. Gibson, S. Best, W. Bonfield, J. Am. Ceram. Soc. 85[11], 2771 (2002) 10.1111/j.1151-2916.2002.tb00527.xSearch in Google Scholar

[35] N. Patel, et al., J. Mater. Sci.: Mater. Med. 13, 1199 (2002) http://dx.doi.org/10.1023/A:102111471007610.1023/A:1021114710076Search in Google Scholar

[36] J. Huang, et al., J. Mater. Sci.: Mater. Med. 16, 1137 (2005) http://dx.doi.org/10.1007/s10856-005-4720-910.1007/s10856-005-4720-9Search in Google Scholar

[37] J. Vandiver, et al., J. Biomed. Mater. Res. 78A, 352 (2006) http://dx.doi.org/10.1002/jbm.a.3073710.1002/jbm.a.30737Search in Google Scholar

[38] X.L. Tang, X.F. Hiao, R.F. Liu, Mater. Lett. 59, 3841 (2005) http://dx.doi.org/10.1016/j.matlet.2005.06.06010.1016/j.matlet.2005.06.060Search in Google Scholar

[39] E.S. Thian, et al., Biomaterials 27, 2692 (2006) http://dx.doi.org/10.1016/j.biomaterials.2005.12.01910.1016/j.biomaterials.2005.12.019Search in Google Scholar

[40] C.M. Botelho, et al., J. Mater. Sci: Mater. Med. 13, 1123 (2002) http://dx.doi.org/10.1023/A:102117760189910.1023/A:1021177601899Search in Google Scholar

[41] Y-J. Lee, et al., J. Korean. Ceram. Soc. 40, 1096 (2003) Search in Google Scholar

[42] J. Reid, et al., Biomaterials 26, 2887 (2005) http://dx.doi.org/10.1016/j.biomaterials.2004.09.00510.1016/j.biomaterials.2004.09.005Search in Google Scholar

[43] L. Guo, M. Huang, X. Zhang, J. Mater. Sci.: Mater. Med. 14, 817 (2003) http://dx.doi.org/10.1023/A:102504872433010.1023/A:1025048724330Search in Google Scholar

[44] A. Oyane, et al., Biomaterials 20, 79 (1999) http://dx.doi.org/10.1016/S0142-9612(98)00146-X10.1016/S0142-9612(98)00146-XSearch in Google Scholar

[45] I.R. Gibson, J. Mater. Sci.: Mater. Med. 12, 799 (2000) http://dx.doi.org/10.1023/A:100890561318210.1023/A:1008905613182Search in Google Scholar

[46] M.H. Santos, L. Hemeine, H. Mansur, Mater. Sci. Eng. C 28, 563 (2008) http://dx.doi.org/10.1016/j.msec.2007.07.00210.1016/j.msec.2007.07.002Search in Google Scholar

[47] K. Payne, A. Vies, Biopolymers 27, 1749 (1988) http://dx.doi.org/10.1002/bip.36027110510.1002/bip.360271105Search in Google Scholar

[48] S. Krimm, J. Bandekar, Adv. Protein Chem. 38, 181 (1986) http://dx.doi.org/10.1016/S0065-3233(08)60528-810.1016/S0065-3233(08)60528-8Search in Google Scholar

[49] E. Sachlos, et al., Acta Biomaterialia 4, 1322 (2008) http://dx.doi.org/10.1016/j.actbio.2008.03.01610.1016/j.actbio.2008.03.016Search in Google Scholar

[50] M. Chang, C. Ko, W. Douglas, Biomaterials 24, 2853 (2003) http://dx.doi.org/10.1016/S0142-9612(03)00115-710.1016/S0142-9612(03)00115-7Search in Google Scholar

[51] E. Landi, et al., J. Eur. Ceram. Soc. 23, 2931 (2003) http://dx.doi.org/10.1016/S0955-2219(03)00304-210.1016/S0955-2219(03)00304-2Search in Google Scholar

[52] J.P. Lafon, E. Champion, D. Bernache-Assolant, J. Eur. Ceram. Soc. 28, 139 (2008) http://dx.doi.org/10.1016/j.jeurceramsoc.2007.06.00910.1016/j.jeurceramsoc.2007.06.009Search in Google Scholar

[53] V. Jokanovic, et al., J. Mater. Sci.: Mater. Med. 17, 539 (2006) http://dx.doi.org/10.1007/s10856-006-8937-z10.1007/s10856-006-8937-zSearch in Google Scholar PubMed

[54] I. Hofmann, et al., J. Am. Ceram. Soc. 90[3], 821 (2007) http://dx.doi.org/10.1111/j.1551-2916.2007.01500.x10.1111/j.1551-2916.2007.01500.xSearch in Google Scholar

[55] I. Rehman, W. Bonfield, J. Mater. Sci.: Mater. Med. 8, 1 (1997) http://dx.doi.org/10.1023/A:101857021354610.1023/A:1018570213546Search in Google Scholar

[56] M. Chang, J. Tanaka, Biomaterials 23, 4811 (2002) http://dx.doi.org/10.1016/S0142-9612(02)00232-610.1016/S0142-9612(02)00232-6Search in Google Scholar

[57] M. Kikuchi, et al., Biomaterals 25, 63 (2004) http://dx.doi.org/10.1016/S0142-9612(03)00472-110.1016/S0142-9612(03)00472-1Search in Google Scholar

[58] H. Kai, et al., Surface&Coatings Technology 201, 1902 (2006) Search in Google Scholar

[59] W. Zhang, et al., J. Am. Ceram. Soc. 86[6], 1062 (2003) Search in Google Scholar

[60] A. Boskey, T. Wright, R. Blank, J. Biomed. Mater. Res. 14, 330 (1999) 10.1359/jbmr.1999.14.3.330Search in Google Scholar

[61] M. Chang, W.H. Douglas, J. Tanaka, J. Mater. Sci.: Mater. Med. 17, 387 (2006) http://dx.doi.org/10.1007/s10856-006-8243-910.1007/s10856-006-8243-9Search in Google Scholar

[62] M. Santos, H. Mansur, Mater. Res. 10[4], 431 (2007) 10.1590/S1516-14392007000400018Search in Google Scholar

[63] N. Hijon, et al., Chem. Mater. 16, 1451 (2004) http://dx.doi.org/10.1021/cm031164s10.1021/cm031164sSearch in Google Scholar

[64] K. Liu, et al., Biochim. Biophys. Acta 4, 73 (1996) Search in Google Scholar

[65] C. Rodrigues, et al., Biomaterials 24, 4897 (2003) http://dx.doi.org/10.1016/S0142-9612(03)00410-110.1016/S0142-9612(03)00410-1Search in Google Scholar

[66] J. Barralen, S. Best, W. Bonfield, J. Biomed. Mater. Res. 41, 79 (1998) http://dx.doi.org/10.1002/(SICI)1097-4636(199807)41:1<79::AID-JBM10>3.0.CO;2-C10.1002/(SICI)1097-4636(199807)41:1<79::AID-JBM10>3.0.CO;2-CSearch in Google Scholar

[67] M. Valett-Regi, D. Arcos, J. Mater. Chem. 15, 1509 (2005) http://dx.doi.org/10.1039/b414143a10.1039/B414143ASearch in Google Scholar

[68] N. Mostafa, H. Hassan, F. Mohamed, J. Alloys Compd. (in press) Search in Google Scholar

[69] M. Pilard, et al., Acta Biomaterialia (in press) Search in Google Scholar

[70] M. Santos, et al., Biomed. Mater. 2, 135 (2007) http://dx.doi.org/10.1088/1748-6041/2/2/01210.1088/1748-6041/2/2/012Search in Google Scholar

[71] B-H. Yoon, et al., Biomaterials 26, 2957 (2005) http://dx.doi.org/10.1016/j.biomaterials.2004.07.06210.1016/j.biomaterials.2004.07.062Search in Google Scholar PubMed

[72] D. Lickorish, et al., J. Biomed. Mater. Res. 68A, 19 (2003) http://dx.doi.org/10.1002/jbm.a.2003110.1002/jbm.a.20031Search in Google Scholar PubMed

Published Online: 2009-10-6
Published in Print: 2009-12-1

© 2009 Versita Warsaw

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Downloaded on 27.1.2023 from https://www.degruyter.com/document/doi/10.2478/s11532-009-0067-2/html
Scroll Up Arrow