Abstract
In this work we present our experimental results on synthesis, structure evolution and in vitro bioactivity assessment of new gelatin/silicocarnotite hybrid materials. The hybrids were obtained by diluting gelatin (G) and silicocarnotite (S) ceramic powder with G:S ratios of 75:25 and 25:75 wt.% in hot (40°C) water. The hybrids were characterized using XRD, FTIR, SEM/EDS and XPS. FTIR depicts that the “red shift” of amide I and COO− could be attributed to the fact that the gelatin prefers to chelate Ca2+ from S. The growth of calcium phosphates on the surface of the hybrids synthesized and then immersed in 1.5 SBF for 3 days was studied by using of FTIR, XRD and SEM/EDS. According to FTIR results, after an immersion of 3 days, A and B-type CO3HA can be observed on the surface. XRD results indicate the presence of hydroxyapatite with well defined crystallinity. SEM/EDS of the precipitated layers show the presence of CO3HA and amorphous calcium phosphate on the surface of samples with different G/S content when immersed in 1.5 SBF. XPS of the G/S hybrid with 25:75 wt.% proved the presence of Ca-deficient hydroxyapatite after an in vitro test for 3 days.
[1] M. Chang, R. DeLong, Dental Materials 25, 261 (2009) http://dx.doi.org/10.1016/j.dental.2008.07.00510.1016/j.dental.2008.07.005Search in Google Scholar
[2] L. Gineste et al., J. Biomed. Mater. Res. 48, 224 (1999) http://dx.doi.org/10.1002/(SICI)1097-4636(1999)48:3<224::AID-JBM5>3.0.CO;2-A10.1002/(SICI)1097-4636(1999)48:3<224::AID-JBM5>3.0.CO;2-ASearch in Google Scholar
[3] A. Clasen, I. Ruyter, Adv. Dent. Res. 11, 523 (1997) http://dx.doi.org/10.1177/0895937497011004210110.1177/08959374970110042101Search in Google Scholar
[4] Q. Liu, J. de Wijn, C.A. van Blitterswujk, J. Biomed. Mater. Res. 40, 257 (1998) http://dx.doi.org/10.1002/(SICI)1097-4636(199805)40:2<257::AID-JBM10>3.0.CO;2-J10.1002/(SICI)1097-4636(199805)40:2<257::AID-JBM10>3.0.CO;2-JSearch in Google Scholar
[5] A. Wang et al., Appl. Surf. Sci. 253, 3311 (2007) http://dx.doi.org/10.1016/j.apsusc.2006.07.02510.1016/j.apsusc.2006.07.025Search in Google Scholar
[6] W. Zhang, S. Liao, F. Cui, Chem. Mater. 8, 3221 (2003) http://dx.doi.org/10.1021/cm030080g10.1021/cm030080gSearch in Google Scholar
[7] J. Song, V. Malathong, C. Bretozzi, J. Am. Chem. Soc. 127, 3366 (2005) http://dx.doi.org/10.1021/ja043776z10.1021/ja043776zSearch in Google Scholar
[8] J. Song, E. Saiz, C. Bertozzi, J. Am. Chem. Soc. 125, 1236 (2003) http://dx.doi.org/10.1021/ja028559h10.1021/ja028559hSearch in Google Scholar
[9] G. Wei, F. Ma, Biomaterials 25, 4749 (2004) http://dx.doi.org/10.1016/j.biomaterials.2003.12.00510.1016/j.biomaterials.2003.12.005Search in Google Scholar
[10] M. Chang, C. Ko, W. Douglas, Biomaterials 24, 2853 (2003) http://dx.doi.org/10.1016/S0142-9612(03)00115-710.1016/S0142-9612(03)00115-7Search in Google Scholar
[11] K. Furucai, Y. Oaki, H. Imai, Chem. Mater. 18, 229 (2006) http://dx.doi.org/10.1021/cm052213z10.1021/cm052213zSearch in Google Scholar
[12] S. Teng et al., Compos. Sci. Technol. 66, 1532 (2006) http://dx.doi.org/10.1016/j.compscitech.2005.11.02110.1016/j.compscitech.2005.11.021Search in Google Scholar
[13] M. Chang, C. Ko, W. Douglas, Biomaterials 24, 3087 (2003) http://dx.doi.org/10.1016/S0142-9612(03)00150-910.1016/S0142-9612(03)00150-9Search in Google Scholar
[14] M. Chen et al., Appl. Sufr. Sci. 254, 2730 (2008) http://dx.doi.org/10.1016/j.apsusc.2007.10.01110.1016/j.apsusc.2007.10.011Search in Google Scholar
[15] M. Chang, C. Ko, W. Douglas, J. Mater. Sci. 40, 2723 (2005) http://dx.doi.org/10.1007/s10853-005-2116-310.1007/s10853-005-2116-3Search in Google Scholar
[16] W. Liu et al., J. Mater. Sci. 41, 1851 (2006) http://dx.doi.org/10.1007/s10853-005-3184-010.1007/s10853-005-3184-0Search in Google Scholar
[17] M. Chang, T. Ikoma, J. Tanaka, J. Mater. Sci. 39, 5547 (2004) http://dx.doi.org/10.1023/B:JMSC.0000039284.70028.fa10.1023/B:JMSC.0000039284.70028.faSearch in Google Scholar
[18] M. Chang, W. Douglas, J. Mater. Sci.: Mater. Med. 18, 2045 (2007) http://dx.doi.org/10.1007/s10856-007-3152-010.1007/s10856-007-3152-0Search in Google Scholar PubMed
[19] J. Sundaram, T. Durance, R. Wang, Acta Biomaterialia 4, 932 (2008) http://dx.doi.org/10.1016/j.actbio.2008.01.01910.1016/j.actbio.2008.01.019Search in Google Scholar PubMed
[20] C. Shu et al., Ceramics International 33, 193 (2007) http://dx.doi.org/10.1016/j.ceramint.2005.09.00110.1016/j.ceramint.2005.09.001Search in Google Scholar
[21] H-W. Kim, H-E. Kim, V. Salih, Biomaterials 26, 5221 (2005) http://dx.doi.org/10.1016/j.biomaterials.2005.01.04710.1016/j.biomaterials.2005.01.047Search in Google Scholar
[22] X. Liu et al., Biomaterials 30, 2252 (2009) http://dx.doi.org/10.1016/j.biomaterials.2008.12.06810.1016/j.biomaterials.2008.12.068Search in Google Scholar
[23] M. Chang, J. Mater. Sci.: Mater. Med. 19, 2837 (2008) http://dx.doi.org/10.1007/s10856-008-3414-510.1007/s10856-008-3414-5Search in Google Scholar
[24] E. Rosseeva et al., Chem. Mater. 20, 6003 (2008) http://dx.doi.org/10.1021/cm800574810.1021/cm8005748Search in Google Scholar
[25] A. Cios, B. Mycek, Ceram. Int. 27, 767 (2001) http://dx.doi.org/10.1016/S0272-8842(01)00028-110.1016/S0272-8842(01)00028-1Search in Google Scholar
[26] M. Iiokazu, M. Esaki, J. Mater. Sci.: Mater. Med. 10, 249 (1999) http://dx.doi.org/10.1023/A:100896631407510.1023/A:1008966314075Search in Google Scholar
[27] T. Nordstrom et al., J. Biotechnol. 69, 125 (1999) http://dx.doi.org/10.1016/S0168-1656(99)00038-310.1016/S0168-1656(99)00038-3Search in Google Scholar
[28] S.-M. Lien, C-H. Chien, T-J. Huang, Materials Science and Engineering C 29, 315 (2008) http://dx.doi.org/10.1016/j.msec.2008.07.01710.1016/j.msec.2008.07.017Search in Google Scholar
[29] S. Panzavolta et al., Acta Biomaterialia 5, 636 (2009) http://dx.doi.org/10.1016/j.actbio.2008.08.01710.1016/j.actbio.2008.08.017Search in Google Scholar PubMed
[30] K-Y. Chen et al., Biomaterials 30, 1682 (2009) http://dx.doi.org/10.1016/j.biomaterials.2008.12.02410.1016/j.biomaterials.2008.12.024Search in Google Scholar PubMed
[31] A. Ruys, J. Aust. Ceram. Soc. 29, 71 (1993) Search in Google Scholar
[32] Y-J. Lee et al., J. Korean. Ceram. Soc. 40, 1096 (2003) Search in Google Scholar
[33] S-R. Kim et al., Key Eng. Mater. 218–220, 85 (2002) http://dx.doi.org/10.4028/www.scientific.net/KEM.218-220.8510.4028/www.scientific.net/KEM.218-220.85Search in Google Scholar
[34] F. Balas, J. Perez-Pariente, M. Vallet-Regi, J. Biomed. Mater. Res. 66A, 364 (2003) http://dx.doi.org/10.1002/jbm.a.1057910.1002/jbm.a.10579Search in Google Scholar PubMed
[35] J. Reid et al., Biomaterials 26, 2005 (2005) http://dx.doi.org/10.1016/j.biomaterials.2004.09.00510.1016/j.biomaterials.2004.09.005Search in Google Scholar PubMed
[36] L. Radev et al., Cent. Eur. J. Chem. 7, 317 (2009) http://dx.doi.org/10.2478/s11532-009-0022-210.2478/s11532-009-0022-2Search in Google Scholar
[37] L. Radev et al., Cent. Eur. J. Chem. 7, 322 (2009) http://dx.doi.org/10.2478/s11532-009-0014-210.2478/s11532-009-0014-2Search in Google Scholar
[38] V. Hristov et al., Cent. Eur. J. Chem. (in press) Search in Google Scholar
[39] L. Radev et al., Cent. Eur. J. Chem. (in press) Search in Google Scholar
[40] R. Reis et al., J. Mater. Sci.: Mater. Med. 8, 897 (1997) http://dx.doi.org/10.1023/A:101851410766910.1023/A:1018514107669Search in Google Scholar
[41] M. Ferraz et al., J. Mater. Sci.: Mater. Med. 12, 629 (2001) http://dx.doi.org/10.1023/A:101124582804610.1023/A:1011245828046Search in Google Scholar
[42] B. Samuneva et al., J. Sol-Gel Sci. Techol. 26, 273 (2003) http://dx.doi.org/10.1023/A:102076760329910.1023/A:1020767603299Search in Google Scholar
[43] Y. Ivanova et al., Cent. Eur. J. Chem. 7, 42 (2009) http://dx.doi.org/10.2478/s11532-008-0098-010.2478/s11532-008-0098-0Search in Google Scholar
[44] Y. Ivanova et al., Thin Solid Films 515, 271 (2006) http://dx.doi.org/10.1016/j.tsf.2005.12.08010.1016/j.tsf.2005.12.080Search in Google Scholar
[45] B. Samuneva et al., J. Non-Cryst. Solids 354, 733 (2008) http://dx.doi.org/10.1016/j.jnoncrysol.2007.07.09410.1016/j.jnoncrysol.2007.07.094Search in Google Scholar
[46] G. Falini, M. Gazzano, A. Ripamonti, J. Mater. Chem. 10, 535 (2000) http://dx.doi.org/10.1039/a906271h10.1039/a906271hSearch in Google Scholar
[47] W. Zhang et al., J. Am. Ceram. Soc. 86[6], 1052 (2003) http://dx.doi.org/10.1111/j.1151-2916.2003.tb03422.x10.1111/j.1151-2916.2003.tb03422.xSearch in Google Scholar
[48] K. Pal, A. Banthia, D. Majumdar, AAPS Pharm. Sci. Tech. 8[1], E1 (2007) 10.1208/pt080121Search in Google Scholar
[49] M. Santos, L. Hemeine, H. Mansur, Mater. Sci. Eng. C 28, 563 (2008) http://dx.doi.org/10.1016/j.msec.2007.07.00210.1016/j.msec.2007.07.002Search in Google Scholar
[50] K. Payne, A. Vies, Biopolymers 27, 1749 (1988) http://dx.doi.org/10.1002/bip.36027110510.1002/bip.360271105Search in Google Scholar
[51] S. Krimm, J. Bandekar, Adv. Protein Chem. 38, 181 (1986) http://dx.doi.org/10.1016/S0065-3233(08)60528-810.1016/S0065-3233(08)60528-8Search in Google Scholar
[52] J. Vandiver et al., J. Biomed. Mater. Res. 78A, 352 (2006) http://dx.doi.org/10.1002/jbm.a.3073710.1002/jbm.a.30737Search in Google Scholar PubMed
[53] I. Rehman, W. Bonfield, J. Mater. Sci.: Mater. Med. 8, 1 (1997) http://dx.doi.org/10.1023/A:101857021354610.1023/A:1018570213546Search in Google Scholar
[54] A. Martines, I. Izquierdo-Barba, M. Vallet-Regi, Chem. Mater. 12, 3080 (2000) http://dx.doi.org/10.1021/cm001107o10.1021/cm001107oSearch in Google Scholar
[55] I. Gibson, S. Best, W. Bonfield, J. Biomed. Mater. Res. 44, 422 (1998) http://dx.doi.org/10.1002/(SICI)1097-4636(19990315)44:4<422::AID-JBM8>3.0.CO;2-#Search in Google Scholar
[56] J. Roman, S. Padila, M. Vallet-Regi, Chem. Mater. 15, 798 (2003) http://dx.doi.org/10.1021/cm021325c10.1021/cm021325cSearch in Google Scholar
[57] X. Yang et al., Mater. Sci. Eng. C 29, (2009) Search in Google Scholar
[58] B. Gaihre et al., Mater. Sci. Eng. C 28, 1297 (2008) http://dx.doi.org/10.1016/j.msec.2008.01.00110.1016/j.msec.2008.01.001Search in Google Scholar
[59] Z. Yang et al., J. Mater. Chem. 15, 1807 (2005) http://dx.doi.org/10.1039/b418015c10.1039/b418015cSearch in Google Scholar
[60] K. Mohamed, A. Mostafa, Mater. Sci. Eng. C 28, 1087 (2008) http://dx.doi.org/10.1016/j.msec.2007.04.04010.1016/j.msec.2007.04.040Search in Google Scholar
[61] M. Chang, W. Douglas, J. Tanaka, J. Mater. Sci.: Mater. Med. 17, 387 (2006) http://dx.doi.org/10.1007/s10856-006-8243-910.1007/s10856-006-8243-9Search in Google Scholar PubMed
[62] Y. Yusufogly, M. Akinc, J. Am. Ceram. Soc. 91[10], 3147 (2008) http://dx.doi.org/10.1111/j.1551-2916.2008.02540.x10.1111/j.1551-2916.2008.02540.xSearch in Google Scholar
[63] Y. Suetsugu, I. Shimoya, J. Tanaka, J. Am. Ceram. Soc. 81[3], 746 (1998) 10.1111/j.1151-2916.1998.tb02403.xSearch in Google Scholar
[64] G.A. Stanciu et al., J. Biomed. Pharm. Eng. 1[1], 34 (2007) Search in Google Scholar
[65] N. Hijon et al., Chem. Mater. 1451 (2004) 10.1021/cm031164sSearch in Google Scholar
[66] I. de Lima, A.M. Costa, I.N. Bastos, Mater. Res. 9, 1 (2006) 10.1590/S1516-14392006000400010Search in Google Scholar
[67] F. Boccafoschi et al., Biomaterials 26, 7410 (2005) http://dx.doi.org/10.1016/j.biomaterials.2005.05.05210.1016/j.biomaterials.2005.05.052Search in Google Scholar PubMed
[68] M. Vallet-Regi, D. Arcos, J. Mater. Chem. 15, 1509 (2005) http://dx.doi.org/10.1039/b414143a10.1039/B414143ASearch in Google Scholar
[69] C. Durucan, P. Brown, J. Mater. Sci.: Mater. Med. 11, 365 (2000) http://dx.doi.org/10.1023/A:100893402444010.1023/A:1008934024440Search in Google Scholar
© 2009 Versita Warsaw
This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.