Bend Straightening of a Carbonitrided Gear Shaft – Consequences on Residual Stresses and Retained Austenite near the Surface*

Biegerichten einer carbonitrierten Getriebewelle – Auswirkungen auf randnahe Eigenspannungen und Restaustenitgehalte
C. Schott, W. Zinn, B. Scholtes and T. Niendorf

Abstract

Carbonitriding of shafts in drive technology is strongly connected with distortion. Bend straightening is an important process step in order to eliminate distortion without removing the hardened surface layer. As shown in several investigations, even for simple part geometries, bending induced stresses and plastic deformations have a strong impact not only on the residual stress state but also on the microstructure after straightening. As gear shafts become increasingly filigree and complex in their geometry, the components state after straightening is only understood in rare cases. Due to indispensable, function based notches as well as changes in the cross section, these effects will occur especially in areas of small cross sections or notches in conjunction with high bending stresses. It is the objective of this work, to characterize these critical areas with respect to the distribution of residual stresses and retained austenite along the circumference as well as in the in-depth direction. Therefore, the measured distributions of residual stresses, integral width values and retained austenite near the surface will be presented and discussed. For this purpose a carbonitrided gear shaft taken out of a large production volume was investigated before and after a commonly used straightening operation.

Kurzfassung

In der Antriebstechnik stellt das Biegerichten nach der Einsatzhärtung von Wellen einen wichtigen Prozessschritt dar, um den oftmals unvermeidlichen Verzug zu beseitigen und gleichzeitig die harte Randschicht des Bauteils zu erhalten. Wie bereits in einigen Untersuchungen dargestellt wurde, beeinflussen die beim Richten vorliegenden Spannungen und die daraus resultierenden plastischen Deformationen sowohl den Eigenspannungszustand als auch die Mikrostruktur schon bei geometrisch simplen Bauteilen. Für die zunehmend filigranen und in ihrer Geometrie komplexen Wellen ist der Zustand nach dem Richten jedoch nur in seltenen Fällen bekannt und nachvollziehbar. Bei einer Welle, die konstruktiv notwendige Querschnittsänderungen oder auch Kerben aufweist, werden die genannten Effekte dort auftreten, wo Bereiche mit geringem Querschnitt und solche mit hohen Lastspannungen durch den Richtprozess zusammenfallen. Ziel dieser Arbeit ist es, diese kritischen Bereiche im Hinblick auf die Verteilung von Eigenspannungen und Restaustenit, sowohl entlang des Umfangs als auch in Tiefenrichtung, detailliert zu charakterisieren, um ein besseres Verständnis für den Zustand gerichteter Wellen zu gewinnen. Dazu werden die ermittelten randnahen Eigenspannungsverläufe und die Verteilungen der Integralbreiten sowie der Restaustenitgehalte am Beispiel einer in großer Stückzahl hergestellten Getriebewelle vor und nach einem praxisüblichen Richtprozess vorgestellt und diskutiert.


*

Lecture at the HK 2016, 72nd HeatTreatmentCongress, 26–28 October 2016 in Cologne, Germany

3 (Kontakt/Corresponding author)

References

1. Grosch, J.: Fatigue resistance of carburized and nitrided steels. In: Thermochemical Surface Engineering of Steels, Mittemeijer, E.J. M.; Somers, M.A. (Eds.), Woodhead Publ., Cambridge, UK, 2014, pp. 209240. – ISBN 978-0-85709-592-3 Search in Google Scholar

2. Lübben, Th.; Zoch, H.-W.: Einführung in die Grundlagen des Distortion Engineering. HTM J. Heat Treatm. Mat.67 (2012) 5, pp. 275290, 10.3139/105.110161 Search in Google Scholar

3. Zoch, H.-W.; Lübben, Th. (Eds.): Proceedings 5th Int. Conf. on Distortion Engineering, 23–25.09.15, Bremen, Germany, 2015. – ISBN 978-3-88722-749-4 Search in Google Scholar

4. Heeß, K; et al.: Maß- und Formänderungen infolge Wärmebehandlung von Stählen: Grundlagen – Ursachen – Praxisbeispiele. 2nd ed., expert, Renningen, Germany, 2013 Search in Google Scholar

5. Paul, M.; Vogel, W.: Richten einsatzgehärteter Bauteile. HTM Haerterei-Techn. Mitt.45 (1990) 2, pp. 9097 Search in Google Scholar

6. Scholtes, B.; Ellermann, A.; Baunack, D.; Kraus, A.; Zinn, W.: Werkstofftechnische Grundlagen des Biegerichtens. HTM J. Heat Treatm. Mat.70 (2015) 1, pp. 418, 10.3139/105.110246 Search in Google Scholar

7. Schott, C.; Ellermann, A.; Zinn, W.; Scholtes, B: Consequences of Bend Straightening Processes on Residual Stresses and Strength of Quenched and Tempered Steels. HTM J. Heat Treatm. Mat.71 (2016) 2, pp. 7582, 10.3139/105.110283 Search in Google Scholar

8. Bartels, R. J.: Einfluss des Restaustenits auf das Verformungsverhalten gehärteter Stähle. VDI Fortschritts-Berichte, Reihe 5, No. 162, VDI, Duesseldorf, Germany, 1989 Search in Google Scholar

9. Tomala, V.; Hirsch, T.; Hoffmann, F.; Mayr, P.: Versagensverhalten durchgreifend wärmebehandelter und gerichteter bauteilähnlicher Proben. HTM Haerterei-Techn. Mitt.54 (1999) 6, pp. 392399 Search in Google Scholar

10. Randelius, M.; Aslund, J.; Hosseini, S.: Straightening of case hardened bars before and after tempering. VBCentrum, VBC-R-2008-001, Swerea KIMAB, Stockholm, Sweden, 2008 Search in Google Scholar

11. Haglund, S.; Kristoffersen, H.: Simulation of Residual Stresses after Straightening of Induction Hardened Components. HTM J. Heat Treatm. Mat.69 (2014) 3, pp. 165172, 10.3139/105.110223 Search in Google Scholar

12. Fahlkrans, J.; Melander, A.; Gardstam, J.; Haglund, S.: Straightening of induction hardened shafts – influence on fatigue strength and residual stress. HTM J. Heat Treatm. Mat.67 (2012) 3, pp. 179187, 10.3139/105.110149 Search in Google Scholar

13. Aslund, J.; Hosseini, S.; Haglund, S.: Influence of straightening on fatigue properties – a study of bending fatigue and residual stresses of case hardened SS2511 steel. VBCentrum, VBC-R-2009-004, Swerea KIMAB, Stockholm, Sweden, 2009 Search in Google Scholar

14. Clausen, B.; Hoffmann, F.; Zoch, H.-W.: Beeinflussung der Randschicht durch die Einsatzhärtung. HTM J. Heat Treatm. Mat.63 (2008) 6, pp. 326336, 10.3139/105.100473 Search in Google Scholar

15. Macherauch, E.; Müller, P. Z.: Das sin2ψ-Verfahren der röntgenographischen Spannungsmessung. Z. Angew. Physik13 (1961), pp. 305312 Search in Google Scholar

Published Online: 2017-06-20
Published in Print: 2017-05-16

© 2017, Carl Hanser Verlag, München