Residual stress states as a result of bending and straightening processes of steels in different heat treatment conditions

  • Arne Ellermann and Berthold Scholtes

Abstract

Steels with different content of cementite (Armco iron, Ck45 and C80) as well as four different heat treatment conditions of 42CrMoS4 are examined under both uniaxial and four-point bending loading with load reversal regarding the residual stress distribution due to straightening processes. It was found that increasing cementite content and a fine lamellar microstructure increase the developing residual stresses. While uniaxial loading causes only micro stresses, bending loading causes additional macro residual stresses. Due to this, at reversed load residual stresses decrease faster under bending loading than under uniaxial loading. Furthermore, residual stresses originating from bending loading decrease in the outer planes faster than in the inner ones when load is reversed. In general it turned out that every straightening process causes inevitable and characteristic residual stresses.


* Dipl.-Ing. Arne Ellermann, Moenchebergstr. 3, D-34125 Kassel, Germany. Tel.: +49561 8043701, Fax: +49561 8043662, E-mail:

Dedicated to Prof. Dr.-Ing. Christina Berger on the occasion of her 65th birthday


References

[1] K.Heeß: Maß- und Formänderungen infolge Wärmebehandlung von Stählen, 3rd edition, expert Verlag, Renningen (1997).Search in Google Scholar

[2] M.Dijkman, G.Goch: Distortion compensation strategies in the production process of bearing rings, Mat.-wiss. u. Werkstofftechn.40 (2009) 443447.Search in Google Scholar

[3] J.Volkmuth, F.Hengerer: Einfluß des Ausgangsmaterials auf den Verzug bei der Wärmebehandlung von Massenteilen, HTM Härterei-Techn. Mitt.44 (1989) 8994.Search in Google Scholar

[4] C.M.BergströmL.-E.Larsson, T.Tewin: Reduzierung des Verzugs beim Einsatzhärten, HTM43 (1988) 3640.Search in Google Scholar

[5] M.Paul, W.Vogel: Richten einsatzgehärteter Bauteile, HTM Härterei-Techn. Mitt.45 (1990) 9097.Search in Google Scholar

[6] M.Kornmeier, B.Scholtes: Zur Ermittlung verformungsbedingter Makro- und Mikroeigenspannungen durch mechanische und röntgenographische Eigenspannungsanalysen, Mat.-wiss. und Werkstofftechnik29 (1998) 635642.Search in Google Scholar

[7] M.Belassel, J.L.Lebrun, S.Denis, E.Gautier, J.P.Bettembourg: Effect of Thermal and Mechanical Loading on the Generation of Macro and Micro Stresses in Eutectoid Steel, Proceedings of the Fourth International Conference on Residual Stresses, Baltimore, Soc. for Exp. Mechanics, Bethel (1994) 341401.Search in Google Scholar

[8] T.Hanabusa, H.Fujiwara, M.Nishida: Residual Stress Development in Steels after Tensile deformation, in: G. Beck, S. Denis, A. Simon (Eds.), Proceedings of ICRS2, 1988, Nancy, France, Elsevier Applied Science, London New York (1989) 555560.Search in Google Scholar

[9] G.Zöltzer: Einfluß von Mikro- und Makroeigenspannungen auf das Deformationsverhalten bauteilähnlicher Proben, Dr.-Ing. thesis, University of Kassel (1999).Search in Google Scholar

[10] B.Eigenmann, E.Macherauch: Röntgenographische Untersuchung von Eigenspannungszuständen in Werkstoffen, Teil II, Mat.-wiss. u. Werkstofftechn.26 (1995) 199216.10.1002/mawe.19950260410Search in Google Scholar

[11] B.Scholtes: Eigenspannungen in mechanisch randschichtverformten Werkstoffzuständen, DGM Informationsgesellschaft mbH, Oberursel (1991).Search in Google Scholar

[12] B.Scholtes: Die Auswirkungen des Bauschingereffekts auf das Verformungsverhalten technisch wichtiger Vielkristalle, Dr.-Ing. thesis, University of Karlsruhe (1980).Search in Google Scholar

[13] J.Bauschinger: ßber die Veränderung der Elasticitätsgrenze und der Festigkeit des Eisens und Stahls durch Strecken, Recken und Quetschen, durch Erwärmen und Abkühlen und durch oftmal wiederholte Beanspruchung, Mittheilungen aus dem mechanisch-technischem Laboratorium der K. Technischen Hochschule in München (1886) Heft 13.Search in Google Scholar

[14] E.Macherauch, H.Wohlfahrt, U.Wolfstieg: Zur zweckmäßigen Definition von Eigenspannungen, HTM Härterei-Techn. Mitt.28 (1973) 201211.Search in Google Scholar

[15] B.Eigenmann, E.Macherauch: Röntgenographische Untersuchung von Spannungszuständen in Werkstoffen, Teil I, Mat.-wiss. u. Werkstofftechn.26 (1995) 148160.10.1002/mawe.19950260310Search in Google Scholar

[16] L.Che, M.Gotoh, S.Tagako, Y.Hirose: X-Ray Elastic Constant Determination and Residual Stress Estimation of Spherical Carbide in JIS SK3, Proceedings of the Sixteenth International Offshore and Polar Engineering Conference, San Francisco, USA (2006).Search in Google Scholar

[17] K.van Acker, J.Root, P.Van Houtte, E.Aernoudt: Acta mater.44 (1996) 40394049.10.1016/S1359-6454(96)00051-1Search in Google Scholar

[18] H.Fischmeister, B.Karlsson: Z. Metallkunde68 (1977) 311327.Search in Google Scholar

[19] G.Zöltzer, B.Scholtes: Analysis of Residual Stresses in Plastically Deformed Plain Carbon Steels, Proceedings of the Sixth International Conference on Residual Stresses ICRS-6 Oxford, UK, IOM Communications, London (2000) 171178.Search in Google Scholar

Received: 2011-3-28
Accepted: 2011-10-21
Published Online: 2013-06-11
Published in Print: 2012-01-01

© 2012, Carl Hanser Verlag, München

Downloaded on 19.3.2024 from https://www.degruyter.com/document/doi/10.3139/146.110624/pdf
Scroll to top button