Abstract
The results of investigation of the isothermal oxidation wear mechanism of Ti-46Al-7Nb-0.7Cr-0.1Si-0.2Ni intermetallic alloy with AlCrN coating are presented. Tests in 9%O2 + 0.2%HCl + 0.08%SO2 + N2 atmosphere were performed at a temperature of 700°C. The structure of the specimen and chemical composition of the oxidation products were analysed using scanning electron microscopy and energy dispersive X-ray analysis. In addition, mass changes were investigated.
References
[1] F.Appel, J.D.H.Paul, M.Oehring: Gamma Titanium Aluminide Alloys, Science and Technology, Wiley-VCH Verlag GmbH & Co. KGaA (2011). 10.1002/9783527636204Search in Google Scholar
[2] E.ALoria: Intermetallics8 (2000) 1339–1345. 10.1016/S0966-9795(00)00073-XSearch in Google Scholar
[3] W.Szkliniarz: Metallic materials with the participation of intermetallic phases (in Polish); Z.Bojar and W.Przetakiewicz (Eds.), Technical Military Academy, Warsaw (2006) 66–88.Search in Google Scholar
[4] F.Appel, M.Oehring, R.Wagner: Intermetallics8 (2000) 1283–1312. 10.1016/S0966-9795(00)00036-4Search in Google Scholar
[5] S.Król, M.Prażmowski: Material Engineering3 (2006) 456–459 (in Polish).Search in Google Scholar
[6] M.Yoshihara, Y.W.Kim: Intermetallics13 (2005) 952–958. 10.1016/j.intermet.2004.12.007Search in Google Scholar
[7] J.Małecka: Corros. Sci.63 (2012) 287–292. 10.1016/j.corsci.2012.06.009Search in Google Scholar
[8] J.Małecka: Journal of Achievements in Materials and Manufacturing Engineering, Vol. 50, 1 (2012) 40–46.Search in Google Scholar
[9] J.Małecka, W.Grzesik: Journal of Achievements in Materials and Manufacturing Engineering, Vol. 43, 1 (2010) 252–259.Search in Google Scholar
[10] S.Mrowec, T.Werber: Gaseous corrosion, Publishing house “Silesia”, Katowice, (1965) (in Polish). 10.1016/S0010-938X(65)80028-2Search in Google Scholar
[11] J.Małecka, W.Grzesik, A.Hernas: Corros. Sci.52 (2010) 263–272. 10.1016/j.corsci.2009.09.015Search in Google Scholar
© 2013, Carl Hanser Verlag, München