Effect of Sr Addition on the Microstructure of a Rapidly Solidified Al-12 wt.% Si Alloy

Auswirkung eines Sr-Zusatzes auf das Gefüge einer rasch erstarrten Al-12 Gew.-% Si-Legierung
  • Yan Wang , Zhonghua Zhang , Shaohua Zheng , Weimin Wang and Xiufang Bian
From the journal Practical Metallography

Abstract

The effect of Sr addition on the microstructure of a melt-spun Al-12% Si alloy has been investigated using X-ray diffraction and transmission electron microscopy. The Sr addition has no effect on the phase constitution but has a marked effect on the microstructure of the melt-spun alloy. The distribution, morphology and orientation of Si in the melt-spun alloy with the Sr addition are different from those in the alloy without Sr. Under rapid solidification conditions, cooling rates play a dominant role in the microstructure formation of the Al-12% Si alloy.

Kurzfassung

Untersucht wurde die Auswirkung eines Sr-Zusatzes auf das Gefüge einer Al-12 Gew.-% Si Schmelzspinnlegierung mittels Röntgenbeugung und Transmissionselektronenmikroskopie. Der Sr-Zusatz hatte keine Auswirkung auf die Phasenzusammensetzung, zeigt jedoch erhebliche Auswirkungen auf das Gefüge der Schmelzspinnlegierung. Verteilung, Morphologie und Orientierung von Si in der Schmelzspinnlegierung mit Sr-Zusatz unterscheiden sich von denen in Legierungen ohne Sr. Unter den Bedingungen der raschen Erstarrung spielen Kühlraten eine beherrschende Rolle in der Gefügebildung einer Al-12% Si-Legierung.

Literatur/References

[1] Kim, T.S.; Lee, B.T.; Lee, C.R.; Chun, B.S.: Mater. Sci. Eng. A304–306 (2001) 617.Search in Google Scholar

[2] Joenoes, A.T.; Gruzleski, J.E.: Cast Metals4 (1991) 62.Search in Google Scholar

[3] Fatahalla, N.; Hafiz, M.; Abdulkhalek, M.: J. Mater. Sci.34 (1999) 3555.Search in Google Scholar

[4] Ourdjini, A.; Elliott, R.: Mater. Sci. Technol.11 (1995) 1241.Search in Google Scholar

[5] Liu, Q.Y.: Scripta Mater. 38 (1998) 1083.10.1016/S1359-6462(98)00011-6Search in Google Scholar

[6] Khan, S.; Elliott, R.: J. Mater. Sci.29 (1994) 736.Search in Google Scholar

[7] Lu, S.Z.; Hellawell, A.: J. Cryst. Growth73 (1985) 316.Search in Google Scholar

[8] Shamsuzzoha, M.; Hogan, L.M.: J. Cryst. Growth72 (1985) 735.Search in Google Scholar

[9] Nogita, K.; Dahle, A.K.: Mater. Trans.42 (2001) 393.Search in Google Scholar

[10] Lu, S.Z.; Hellawell, A.: Metall. Trans. A18 (1987) 1721.Search in Google Scholar

[11] Pacz, A.: U.S. patent 1387900, 1920.Search in Google Scholar

[12] Haque, M.M.: J. Mater. Proc. Technol.55 (1995) 193.Search in Google Scholar

[13] Zhang, Z.H.; Bian, X.F.; Liu, X.F.: Z. Metallkd.92 (2001) 1323.Search in Google Scholar

[14] Zhang, Z.H.; Bian, X.F.: Z. Metallkd.92 (2001)1319.Search in Google Scholar

[15] Jones, H.: J. Mater. Sci.19 (1984) 1043.Search in Google Scholar

[16] Birol, Y.: J. Mater. Sci.31 (1996) 2139.Search in Google Scholar

[17] Wagner, R.S.: Acta Metall. 8 (1960) 57.10.1016/0001-6160(60)90145-0Search in Google Scholar

[18] Hamilton, D.R.; Seidensticker, R.G.: J. Appl. Phys.31 (1960) 1165.Search in Google Scholar

[19] Steen, H.A.H.; Hellawell, A.: Acta Metall. 20 (1972) 363.10.1016/0001-6160(72)90030-2Search in Google Scholar

[20] Matyja, H.; Giessen, B.C.; Grant, N.J.: J. Inst. Metals96 (1968) 30.Search in Google Scholar

[21] Van Der Hoeven, J.A.; Van Mourik, P.; Mittemeijer, E.J.: J. Mater. Sci. Lett.2 (1983) 158.Search in Google Scholar

[22] Antonione, C.; Battezzati, L.; Marino, F.: J. Mater. Sci. Lett.5 (1986) 586.Search in Google Scholar

[23] Todeschini, P.; Champier, G.; Samuel, F.H.: J. Mater. Sci.27 (1992) 3539.Search in Google Scholar

Received: 2003-2-25
Accepted: 2004-5-28
Published Online: 2013-06-11
Published in Print: 2005-08-01

© 2005, Carl Hanser Verlag, München

Downloaded on 28.3.2024 from https://www.degruyter.com/document/doi/10.3139/147.100273/html
Scroll to top button