Metallurgical Failure Investigation of Cracked Hook Nuts Used for Upending Gas Turbine Rotors on Site

Metallkundliche Schadensuntersuchung gebrochener Hakenmuttern, die dem Aufrichten von Gasturbinenläufern vor Ort dienen
A. Neidel and B. Fischer
From the journal Practical Metallography

Abstract

Two types of non-metallic inclusion stringers were found in so-called upending hook nuts, in the vicinity of an indication on the bore wall's surface, first, manganese sulfides that can be expected in this material, and second, endogeneous oxidic inclusions from the steelmaking process. The latter ones, too, can be expected to an extend in the structural steel that was used to make the hook nuts from. However, they are present in an excessive amount and were causative for the decohesions that produced the reported MT indications. The forging process which was employed to produce the semifinished product used to machine the hook nuts from was unable to fragment and disperse the non-metallic inclusions sufficiently as is usually the case.

Kurzfassung

Zwei Typen nichtmetallischer Einschlusszeilen wurden in den Muttern der Aufrichthaken in der Nähe einer Auffälligkeit auf der Oberfläche der Bohrungswand entdeckt: einerseits Mangansulfide, die in diesem Werkstoff zu erwarten sind, und andererseits vom Stahlherstellungsprozess herrührende endogene oxidische Einschlüsse. Letztere können bis zu einem gewissen Umfang ebenfalls in dem zur Herstellung der Hakenmuttern verwendeten Baustahl erwartet werden. Allerdings sind sie in erheblichen Ausmaß vorhanden und verursachten die Werkstofftrennungen, die zu den erwähnten MT-Prüfanzeigen führten. Der Schmiedevorgang, der zur Herstellung des Halbzeugs diente, aus dem die Hakenmuttern gearbeitet werden, führte nicht, wie es normalerweise der Fall ist, zur ausreichenden Fragmentierung und Dispersion der nichtmetallischen Einschlüsse.

References / Literatur

[1] SeumeJ.; LechnerC. (Ed.): Stationäre Gasturbinen, Springer-Verlag, Berlin, Heidelberg, Deutschland, 2003Search in Google Scholar

[2] DGTLV 804821001, Siemens AG, internal purchasing specificationSearch in Google Scholar

[3] EN 10025–1: February 2005Search in Google Scholar

[4] EN 10025–2: April 2005Search in Google Scholar

[5] Atlas zur Wärmebehandlung der Stähle, Bd. 2, Verlag Stahleisen, Düsseldorf1972Search in Google Scholar

[6] HasseS.: Gießerei-Lexikon.18. edition.Schiele & Schön, Berlin2001Search in Google Scholar

[7] LangeG. (Hrsg.): Systematische Beurteilung technischer Schadensfälle. 3. Auflage, DGM, 1992Search in Google Scholar

[8] GroschJ.: Schadenskunde im Maschinenbau. 4. Auflage, Expert Verlag, 2004.Search in Google Scholar

[9] ASM Handbook, Volume 11: Failure Analysis and Prevention. 6. Auflage, ASM International, 1998Search in Google Scholar

Published Online: 2013-11-08
Published in Print: 2013-11-15

© 2013, Carl Hanser Verlag, München

Downloaded on 3.12.2022 from frontend.live.degruyter.dgbricks.com/document/doi/10.3139/147.110237/html
Scroll Up Arrow