Seizing of Gas Turbine Vane Fixing Bolts Made of X22CrMoV12–1

Seizing of Gas Turbine Vane Fixing Bolts Made of X22CrMoV12–1
  • S. Riesenbeck and A. Neidel
From the journal Practical Metallography

Abstract

It is known from field experience that gas turbine vane fixing bolts, made from high-alloy chromium steel, got stuck in their mating bores and often caused problems upon disassembly. Many of them had to be drilled out rather than removed normally. Several metallurgical in­vestigations determined excessive surface oxidation to be the physical cause for the seizing of the bolts. It was recom­mended to change the bolt material from high-alloy steel to a nickel base superalloy with significantly higher oxidation resistance than steel in order to prevent surface scaling and seizure.

Kurzbeschreibung

Aus der Praxis ist bekannt, dass sich Gasturbinenschaufel-Fixierbolzen aus hochlegiertem Chromstahl in ihren Bohrungen festsetzen und dann bei der Demontage häufig Probleme verursachen. Oftmals muss man sie herausbohren, weil sie sich auf normalem Weg nicht mehr entfernen lassen. In mehreren metallurgischen Untersuchungen wurde übermäßige Oberflächenoxidation als physikalische Ursache für das Festfressen der Bolzen nachgewiesen. Es wurde empfohlen, als Material für die Bolzen eine Nickelbasis-Superlegierung statt hochlegiertem Stahl zu verwenden, da diese eine erheblich höhere Oxidationsbeständigkeit als Stahl aufweist, um Verkrustungen und Festfressen zu vermeiden.


Übersetzung: E. Engert


References / Literatur

[1] Internal report P347/2008/0508, June 6, 2008.10.1055/s-2008-1072641Search in Google Scholar

[2] VDI-Richtlinie 3822, VDI-Verlag2011.Search in Google Scholar

[3] Rossmann, A.: Die Sicherheit von Turbo-Flugtriebwerken, Band 5, p. 19.1.4–1 to 19.1.4–15. Eigenverlag2005.Search in Google Scholar

[4] ibid., p. 19.2.2–1 to 19.2.2–14.Search in Google Scholar

[5] ibid., Band 4, p. 15.3–5.Search in Google Scholar

[6] Internal report GT BLN QM/2011/0550, July 8, 2011.Search in Google Scholar

[7] Neidel, A. (ed.): Handbuch Metallschäden, 2. Aufl., S. 698700. Carl Hanser Verlag München Wien2012.Search in Google Scholar

[8] ibid., p. 726727.Search in Google Scholar

[9] http://en.wikipedia.org/wiki/nimonic, accessed March 30, 2013 at 04 : 32 p.m.Search in Google Scholar

[10] Donachie, M.J.; Donachie, S.J.: Superalloys. A Technical Guide. 2nd edition2002. ASM International, Materials Park, Ohio, USA.10.31399/asm.tb.stg2.9781627082679Search in Google Scholar

[11] Sims, C.T.; Hagel, W.C.: The Superalloys. John Wiley & Sons, New York1972.Search in Google Scholar

[12] Betteridge, W.; Heslop, J.: The Nimonic Alloys and Other Nickel-Base High-Temperature Alloys. 2nd Edition 1974. Edward Arnold (Publishers) Limited 1974.Search in Google Scholar

[13] DIN 17742.Search in Google Scholar

[14] DIN 17750–52.Search in Google Scholar

Published Online: 2014-08-05
Published in Print: 2014-08-14

© 2014, Carl Hanser Verlag, München

Downloaded on 8.2.2023 from https://www.degruyter.com/document/doi/10.3139/147.110249/html
Scroll Up Arrow