The Influence of Cold Working and Recrystallization on the Homogenization of As-cast Cu-50 wt.% Ni Alloy

Die Einfluüsse von Kaltverformung und Rekristallisation auf die Homogenisierung einer Cu-50 Gew.-% Ni-Gußlegierung
Rejane Aparecida Nogueira and Angelo Fernando Padilha

Abstract

The effects of cold working and recrystallization on the homogenization of a Cu-50 wt.% Ni alloy have been investigated by electron probe microanalysis and other complementary techniques. The occurrence of homogenization has been explained by the synergism of 3 factors: deformation alters interdendritic spacing and diffusion distances, crystalline defects enhance diffusion and microstructure sweeping by grain boundaries during recrystallization assists solute redistribution by grain boundary diffusion.

Abstract

Die Einflüsse von Kaltverformung und Rekristallisation auf die Homogenisierung einer Cu-50 Gew.-% Ni-Gußlegierung wurden mit Hilfe von Elektronenstrahlmikroanalyse und anderen komplementären Methoden untersucht. Das Auftreten der Homogenisierung wurde durch das Zusammenwirken von drei Faktoren erklärt. Durch die Verformung ändern sich der interdendritische Abstand und die Diffusionswege, Gitterbaufehler beschleunigen die Diffusion, und das Durchlaufen des Gefüges von Korngrenzen während der Rekristallisation vereinfacht die Umverteilung des Mischkristalls mittels Korngrenzendiffusion.


Rejane Aparecida Nogueira Instituto de Pesquisas Energéticas e Nucleares Comissão Nacional de Energia Nuclear, C.P. 11049 − Pinheiros − CEP 05422-970 São Paulo, Brasil
Angelo Fernando Padilha Escola Politécnica da Universidade de São Paulo, Departamento de Engenharia Metalúrgica e de Materiais C.P. 8174 − CEP 05508-900 São Paulo, Brasil

Literature

1 Weinberg, F.; Buhr, R.K.: J. Iron Steel Inst. 207 (1969) 1114 – 21.Search in Google Scholar

2 Cole, G.S.: Metall. Trans. 2 (1971) 357 – 70.10.1007/BF02663323Search in Google Scholar

3 Martin, J.W.; Doherty, R.D.: Stability of Microstructure in Metallic Systems, Cambridge University Press, Cambridge (1976) 30 – 34.Search in Google Scholar

4 Falleiros, I.G.S.: Metallography 5 (1972) 125 – 37.10.1016/0026-0800(72)90050-XSearch in Google Scholar

5 Granger, D.A.; Bower, T.F.: J. Inst. Metals 98 (1970) 353 – 63.Search in Google Scholar

6 Feest, E.A; Doherty, R.D.: Metall. Trans. 4 (1973) 125 – 36.10.1007/BF02649611Search in Google Scholar

7 Fletcher, A.J.; King, S.; Rickinson, B.; Atkinson, H.: Mater. Sc. Techn. 9 (1993) 555 – 61.10.1179/mst.1993.9.7.555Search in Google Scholar

8 Butrymowicz, D.B.; Manning, J.R.; Read, M.E.: Diffusion Rate Data and Mass Transport Phenomena for Copper system. In: National Bureau of Standards. Diffusion in metals data center, Washington, USA, DC 20234 (1977) 194 – 233.Search in Google Scholar

9 Kurz, W.; Fisher, D.J.: Fundamentals of Solidification, 3rd edition, Trans. Tech. Publication, Aedermannsdorf, Switzerland (1989) 289 – 292.Search in Google Scholar

10 Politis, C.; Johnson, W.L.: J. Appl. Phys. 60 (1986) 1147 – 51.10.1063/1.337359Search in Google Scholar

11 Fecht, H.J.; Hellstern, E.; Fu, Z.; Johnson, W.L.: Metall. Trans. A 21A (1990) 2333 – 7.10.1007/BF02646980Search in Google Scholar

12 Gottstein, G.; Steffen, H.; Hemminger, W.; Hoschek, G.; Broxterman, K.; Grewe, H.G.; Lang, E.: Scripta metall. 9 (1975) 791 – 6.10.1016/0036-9748(75)90242-2Search in Google Scholar

13 Guilemany, J.M.; Fernández, J.; Peregrin, F.; Guixá, O.: Recrystallization 92. Proc. Int. Conf., Trans. Tech. Publication, Aedermannsdorf, Switzerland (1993) 655 – 60.Search in Google Scholar

Received: 1996-04-03
Published Online: 2021-11-30

© 1997 Carl Hanser Verlag, München