Formation and Transformation of Intermetallic Particles in a Strip-cast Al-0.8Fe-0.6Si Alloy

Entstehung und Umwandlung von intermetallischen Partikeln in einer stranggegossenen Al-0.8Fe-0.6Si Legierung
Yücel Birol

Abstract

The majority of the particles at the surface of a strip-cast Al- 0.8Fe-0.6Si alloy were identified as β-AlFeSi. There were a relatively small number of α-AlFeSi and Si particles while no evidence for binary Al–Fe phases was available. The center of the strip revealed a similar distribution of intermetallic particles with β-AlFeSi still being the dominant constituent. While Si dissolved rapidly into the aluminium matrix, the interdendritic network, mostly of β stringers, was gradually replaced by a uniform dispersion of α-AlFe- Si particles during heat treatments. The phases identified in deformed and undeformed samples after 8 hour heat treatments in the temperature range 540 to 600 °C were identical. The transformation of β-AlFeSi was accelerated, however, in those samples which have received a cold-rolling pass before the heat treatment. Finally, only the hexagonal α has prevailed in all samples after extended holding at 600 °C.

Abstract

Die Partikel auf der Oberfläche kontinuierlich stranggegossener Bander aus Al-0.8Fe-0.6Si wurden mit Hilfe von Röntgenbeugung und energiedispersiver Röntgenanalyse identifiziert. Es wurde festgestellt, daß die meisten Partikel β-AlFeSi Verbindungen sind. Außerdem wurden noch α-Al- FeSi und Si-Partikel gefunden. Eine binäre Al–Fe Phase konnte nicht ermittelt werden. Auch in der Mitte der Band- oberfläche konnte eine ähnliche Phasenverteilung festgestellt werden. Während der Wärmebehandlung löst sich das Silicium sehr schnell in der Matrix. Das aus β-AlFeSi bestehende Gefüge zwischen den Dendriten wandelt mit der Zeit zu α-AlFeSi um. Nach 8-stündiger Glühung zwischen 540 und 600 °C sind die entstandenen Phasen, unabhängig von den vorangegangenen Verformungen, identisch. Bei den kaltverformten Proben erfolgt die β-AlFeSi Umwandlung sehr schnell. Bei allen bei 600 °C über längere Zeit geglühten Proben bleibt allein die hexagonale α-AlFeSi Phase.


Y. Birol Marmara Research Center P.O. Box 21 41470 Gebze Kocaeli, Turkey

Literature

1 Miki, I.; Kosuge, H.; Nagahama, K.:J. Japan. Inst. Light Met. 25 (1975) 1–9.Search in Google Scholar

2 Kosuge, H.; Mizukami, I.: ibid. 25 (1975) 48–58.Search in Google Scholar

3 Asami, A.; Tanaka, T; Hideno, A.: ibid. 28 (1975) 321–327.Search in Google Scholar

4 Westengen, H.: Z. Metallkd. 73 (1982) 360–368.Search in Google Scholar

5 Young, R.M.K.; Clyne, T.W.: Scripta metall. 15 (1981) 1211–1216.Search in Google Scholar

6 Dons, A.L.: Z. Metallkd. 76 (1985) 609 – 612.Search in Google Scholar

7 Griger, A.; Stefaniey, V.; Lendvai, A.; Turmezey, T.: Aluminium 65 (1989) 1049–1056.Search in Google Scholar

8 Hollingsworth, E.H.; Frank, G.R.; Willett, R.E.: Trans.AIME 224 (1962) 188–189.Search in Google Scholar

9 Skjerpe, P.: Metall. Trans. A 18A (1987) 189–200.Search in Google Scholar

10 Dons, A.L.: Z. Metallkd. 75 (1984) 170–174.Search in Google Scholar

11 Dons, A.L.: ibid. 77 (1986) 126–130.Search in Google Scholar

12 Siemensen, C.J.; Vellasamy, R.: ibid. 68 (1977) 428–431.Search in Google Scholar

13 Birol,Y.; Sertçelik, F.: unpublished results (1997).Search in Google Scholar

14 Matjya, H.; Giessen, B.C.; Grant, N.J.: J. Inst. Metals 96 (1968) 30.Search in Google Scholar

15 Munson, D.: ibid. 95 (1967) 217 – 219.Search in Google Scholar

16 Sun, C.Y.; Mondolfo, L.F.: ibid. 95 (1967) 384.Search in Google Scholar

17 Birol, Y.: Aluminium 74 (1998) 318 – 321.Search in Google Scholar

Received: 1998-03-30
Published Online: 2021-12-20

© 1998 Carl Hanser Verlag, Munchen