Abstract

X-ray powder diffraction was performed on β-Ag2Te at room temperature, on ion conducting α-Ag2Te at 523 K, 723 K and 923 K respectively and on γ-Ag2Te at 1123 K.

Rietveld profile refinement of β-Ag2Te confirmed the space group P21/c and the positional parameters of the model of Frueh (Z. Kristallogr. 112 (1959) 44–52).

For the α-modification in space group Fm[unk]m, best results were obtained for a model with a statistical distribution of Ag ions: about 60% of the available Ag ions were placed into 32f(xxx) positions around the tetrahedral 8c(¼ ¼ ¼) sites and the remainder on the 48i(xx½) positions. The probability density function (PDF) calculated with these formal structure parameters suggests next neighbour jumps of Ag ions via the 48i sites.

The first structure refinement of γ-Ag2Te showed it to crystalize in space group Im[unk]m and to be iso-structural to α-AgI. Third order anharmonic coefficients of the temperature factor of the Ag ions could be refined from our X-ray powder data. Corresponding PDF maps show Ag-densities bridging next nearest as well as second next nearest neighbours.

Abstract

Es wurden Mischkristalle der Zusammensetzung Zn0.5Cd0.5Sb durch Zonenschmelzen hergestellt. Die so erhaltenen und durch In-Dotierung n-leitenden Proben erwiesen sich in den elektrischen Eigenschaften als wesentlich stabiler als polykristallines Material, was auf eine Beteili­gung von Korngrenzen bei den n-p-Umwandlungserscheinungen dieser Mischkristalle hindeutet. Nun möglich gewordene Messungen der elektrischen Transportgrößen (elektrische Leitfähigkeit, Hall-Effekt, Thermokraft, transversaler Nernst-Ettingshausen-Effekt) in Abhängigkeit von der Temperatur ergaben, daß bei Zimmertemperatur n-leitende Proben bei tiefen Temperaturen p-Leitung zeigen. Die Ergebnisse werden diskutiert.