Jump to ContentJump to Main Navigation
Show Summary Details
More options …

High Temperature Materials and Processes

Editor-in-Chief: Fukuyama, Hiroyuki

Editorial Board: Waseda, Yoshio / Fecht, Hans-Jörg / Reddy, Ramana G. / Manna, Indranil / Nakajima, Hideo / Nakamura, Takashi / Okabe, Toru / Ostrovski, Oleg / Pericleous, Koulis / Seetharaman, Seshadri / Straumal, Boris / Suzuki, Shigeru / Tanaka, Toshihiro / Terzieff, Peter / Uda, Satoshi / Urban, Knut / Baron, Michel / Besterci, Michael / Byakova, Alexandra V. / Gao, Wei / Glaeser, Andreas / Gzesik, Z. / Hosson, Jeff / Masanori, Iwase / Jacob, Kallarackel Thomas / Kipouros, Georges / Kuznezov, Fedor


IMPACT FACTOR 2018: 0.427
5-year IMPACT FACTOR: 0.471

CiteScore 2018: 0.58

SCImago Journal Rank (SJR) 2018: 0.231
Source Normalized Impact per Paper (SNIP) 2018: 0.377

Open Access
Online
ISSN
2191-0324
See all formats and pricing
More options …
Volume 31, Issue 6

Issues

High Cycle Fatigue and Cyclic Plastic Deformation Behaviour of High Temperature Oxidation Resistant Titanium Aluminide Coated IMI 834 Alloy at 873 K

Ashok Kumar Ray / Prabir Kumar Roy
Published Online: 2012-12-13 | DOI: https://doi.org/10.1515/htmp-2011-0144

Abstract

High cycle and force-controlled (HCF) as well as low cycle fatigue (LCF) behaviour of titanium alloy IMI 834 was comparatively studied in bare condition and with titanium aluminide (Al2Ti) coating, at 873 K in air, for compressor disc of aero engines. HCF testing of bare and Al2Ti coated IMI 834 alloy at 873 K in air revealed that the coated materials has higher lifetime than the bare alloy. However, for low cycle, high stress lifetimes, the unprotected bare alloy is stronger, possibly due to early crack formation and growth in coated layer. In the case of LCF tests at higher values of total strain amplitudes Al2Ti coated IMI 834 alloy has longer fatigue life (Nf) as compared to the bare IMI 834 alloy which appears to be due to load shifting to the coat, but at lower values of total strain amplitude, Al2Ti coating on IMI 834 alloy seems to have no effect on Nf . Higher values of cyclic strength coefficient (K′) and cyclic hardening exponent (n′) for coated IMI 834 alloy indicate that coating offers resistance to cyclic plastic deformation at 873 K in air, and hence is beneficial. The coating adheres well to the substrate and is also fairly resistant to high temperature corrosion in sea water atmosphere at 873 K.

Keywords: Titanium aluminide coating; titanium alloy IMI 834; adhesion; fatigue; deformation and fracture; corrosion

About the article

Materials Science and Technology Division, National Metallurgical Laboratory (CSIR), PO-Burmamines, Jamshedpur-831007, India


Received: 2012-02-09

Accepted: 2012-02-10

Published Online: 2012-12-13

Published in Print: 2012-12-14


Citation Information: , Volume 31, Issue 6, Pages 691–699, ISSN (Online) 2191-0324, ISSN (Print) 0334-6455, DOI: https://doi.org/10.1515/htmp-2011-0144.

Export Citation

©[2012] by Walter de Gruyter Berlin Boston.Get Permission

Comments (0)

Please log in or register to comment.
Log in