Jump to ContentJump to Main Navigation
Show Summary Details
More options …

High Temperature Materials and Processes

Editor-in-Chief: Fukuyama, Hiroyuki

Editorial Board: Waseda, Yoshio / Fecht, Hans-Jörg / Reddy, Ramana G. / Manna, Indranil / Nakajima, Hideo / Nakamura, Takashi / Okabe, Toru / Ostrovski, Oleg / Pericleous, Koulis / Seetharaman, Seshadri / Straumal, Boris / Suzuki, Shigeru / Tanaka, Toshihiro / Terzieff, Peter / Uda, Satoshi / Urban, Knut / Baron, Michel / Besterci, Michael / Byakova, Alexandra V. / Gao, Wei / Glaeser, Andreas / Gzesik, Z. / Hosson, Jeff / Masanori, Iwase / Jacob, Kallarackel Thomas / Kipouros, Georges / Kuznezov, Fedor


IMPACT FACTOR 2018: 0.427
5-year IMPACT FACTOR: 0.471

CiteScore 2018: 0.58

SCImago Journal Rank (SJR) 2018: 0.231
Source Normalized Impact per Paper (SNIP) 2018: 0.377

Open Access
Online
ISSN
2191-0324
See all formats and pricing
More options …
Ahead of print

Issues

Influence of Processing Route and Section Size on Elevated Temperature Tensile Properties of 9Cr-1Mo Ferritic Steel

Binod Kumar Choudhary
Published Online: 2012-01-11 | DOI: https://doi.org/10.1515/htmp.2012.125

Abstract

Tensile tests were performed on specimens obtained from 20 mm plate in normalised and tempered condition and quenched and tempered thick section tubeplate forging to assess the influence of processing route and section size on room and elevated temperatures (300–873 K) tensile properties of 9Cr-1Mo ferritic steel. Yield and ultimate tensile strength values of plate and tubeplate forging exhibited a gradual decrease up to intermediate temperatures followed by a rapid decrease at high temperatures. Ductility values displayed a gradual decrease to a minimum at intermediate temperatures followed by an increase at high temperatures. The fracture mode remained transgranular. At intermediate temperatures, 9Cr-1Mo steel in both the product forms exhibited similar serrated flow, an important manifestation of dynamic strain ageing. At all temperatures, thick section tubeplate forging exhibited lower strength and higher ductility values compared to normalised and tempered steel. The inferior strength values were attributed to coarse microstructure of the forging.

Keywords.: Ferritic steel; tubeplate forging; tensile properties; coarse lath martensite; serrated yielding

About the article

Received: 2011-12-08

Accepted: 2011-12-09

Published Online: 2012-01-11

Published in Print: 2012-01-01


Citation Information: High Temp. Mater. Proc., Pages -–-, ISSN (Online) 2191-0324, ISSN (Print) 0334-6455, DOI: https://doi.org/10.1515/htmp.2012.125.

Export Citation

Comments (0)

Please log in or register to comment.
Log in