Infrared (IR) radiation was discovered 217 years ago. However, the first IR photodetectors (IRPDs) were only invented in the late 20th century. Detecting and sensing IR radiation is extremely important in various applications. IR radiation can generally be divided into different categories, namely near-wavelength region from 0.8 to 3 μm, mid-wavelength IR (MWIR) region from 3 to 5 μm, and long wavelength IR (LWIR) region from 8 to 12 μm. Note that there are different conventions for naming these bands. For example, 1.55 μm is considered short-wavelength IR, or SWIR, within the Department of Defense community, but is considered near-IR (NIR) within the astronomy community. The MWIR and LWIR regions are most important for free-space communications and astronomy, since the high transparency of the atmosphere at these wavelengths allows transmission without significant losses. The same regions are also widely used for night vision and missile tracking for military applications. IR detection also enables many non-contact, non-destructive inspection methods that are widely utilized in industry, such as automotive and defect detection in electronic circuits. IR detection has similarly found many medical applications. Most such IR radiations directly come from a thermal source, and hence they carry information on the identity of the source itself. For example, the temperature of the emitting object can be determined from the IR radiation received, allowing for non-contact, high-sensitivity temperature measurements. Moreover, the wavelength spectrum of the detected IR radiation can also provide a great deal of information on the composition of the source or intermediate absorbing medium. The bonding energies of many materials, especially organic compounds, have resonant frequencies in the IR region. Detecting these resonances (i.e. IR spectroscopy) is a very powerful tool for analyzing chemical bonds in molecules and is used in astronomy to analyze stars and exoplanets.
The first semiconductor photodetectors were fabricated using lead sulfide (PbS) in Germany ,  for military application such as night vision as early as 1933. In 1941, Cashman  successfully improved the technology using thallous sulfide  and successful produced PbS detectors for the first time in the US at Northwestern University in 1944 . After World War II, the IRPDs were widely used in military and astronomy applications such as simple radiometric instruments, passive night vision technology capable of allowing vision under ambient starlight conditions, and anti-air missile seekers . Even up to now low-cost versatile PbS and PbSe polycrystalline thin films remain the photoconductive detectors of choice for many applications in the 1–3 μm and 3–5 μm spectral range.
The first extrinsic (photon energies smaller than the bandgap) photoconductive detectors were reported in the early 1950s ,  after the discovery of the transistor, which stimulated a considerable improvement in growth and material purification techniques. Extrinsic photoconductive response from copper, mercury, zinc, and gold impurity levels doped in germanium gave rise to devices operating in the 8–14 μm (LWIR spectral window) and the 14–30 μm very long wavelength IR (VLWIR) region. They must be operated at very low temperatures to achieve performance similar to that of intrinsic detectors, and they sacrifice quantum efficiency to avoid needing thick detectors. Although Si has several advantages over Ge (namely, a lower dielectric constant giving shorter dielectric relaxation time and lower capacitance, higher dopant solubility and larger photoionization cross-section for higher quantum efficiency, and lower refractive index for lower reflectance), the performance is much lower compared to highly developed Ge detectors. After being dormant for about 10 years, extrinsic Si was reconsidered after the invention of charge-coupled devices (CCDs) by Boyle and Smith . In 1973, Shepherd and Yang  proposed the metal silicide/silicon Schottky-barrier detectors. For the first time it became possible to have much more sophisticated readout schemes – both detection and readout could be implemented on a silicon chip.
At the same time in the early 1950s, rapid advances were being made in narrow bandgap semiconductors that would later prove useful in extending wavelength capabilities and improving sensitivities of devices. The beginning of the 1960s saw the introduction of narrow gap III−V semiconductor alloys (InAs1−x Sbx), IV−VI (Pb1−x SnxTe), and II−VI (Hg1−x CdxTe) material systems. These materials have provided an unprecedented degree of freedom in IR detector design. The bandgap energy tunability results in IR detector applications that span all IR bands. The fundamental properties of narrow-gap semiconductors (high optical absorption coefficient, high electron mobility, and low thermal generation rate), together with the capability for bandgap engineering, make these alloy systems almost ideal for a wide range of IR detectors. The difficulties in growing mercury cadmium telluride (HgCdTe) material, significantly due to the high vapor pressure of Hg, encouraged the development of alternative detector technologies over the past 40 years. One of these was PbSnTe, which was vigorously pursued in parallel with HgCdTe in the late 1960s and early 1970s , . PbSnTe was comparatively easy to grow and good-quality LWIR photodiodes and lasers were readily demonstrated. However, in the late 1970s two factors led to the abandonment of PbSnTe detector work: high dielectric constant and large temperature coefficient of expansion (TCE) mismatch with Si. The scanning-based IR imaging systems of the 1970s required relatively fast response times so that the scanned image was not smeared in the scan direction. A large dielectric constant hinders making low-capacitance devices, which are needed for fast operation. The second drawback, large TCE, can lead to failure of the indium bonds in hybrid structure (between silicon readout and the detector array) after repeated thermal cycling from room temperature to the cryogenic temperature of operation. Eighty years since the development of the first semiconductor IRPD, the development of IRPDs has been matured and well studied. At the end of the last millennium there were two dominant IR systems, InSb- and HgCdTe-based detectors, which were well developed and available in commercial systems. While these two systems saw improvements over the last 12 years, their change has not nearly been as marked as that of the engineered quantum-based detectors [i.e. quantum well infrared photodetectors (QWIPs), quantum dot-based infrared photodetectors (QDIPs), quantum dot in well infrared photodetectors (DWELL-IPs), and strained-layer superlattices (SLS)-based photodetectors]. However, the mature IRPD technology is costly, difficult to fabricate, and requires low temperature operation. In the last two decades, a lot of new nanostructures and technologies have emerged to reduce the cost of IRPDs and improve the IRPD performance especially for high temperature operation.
In this paper, we review the progress made in all of these systems over the last decade. We will also review the new material systems, such as two-dimensional (2D) materials, carbon nanotubes, and metal oxides. In the second section, we review IRPD devices based on the mature material namely II–VI, III–V, and silicon and compare them with emerging new materials such as graphene, transition metal dichalcogenides (TMDCs), and carbon nanotubes. In the third section, we will review the current progress of nanostructures such as graphene, 2D materials, quantum well (QW), quantum dot (QD), DWELL, SLS and colloid quantum dot (CQD) which dramatically improve the electronic properties of IRPDs. Newly emerging nanostructures such as nanowires and nanotube are also discussed. In the fourth section, we will focus on nanostructures used to enhance the coupling of light with the IRPD. These include nanostructured antireflection (AR) coatings, optical antennas, plasmonic and metamaterials. In the last section, we will briefly list the pros and cons of all the discussed material systems and future prospect of the structures and materials covered here.
2 IRPD based on different bulk material systems
For an IRPD to work, a light-sensitive material capable of absorbing electromagnetic radiation is needed. It converts the absorbed light into a signal that can be collected by a readout device. In order for the absorption process to happen, a semiconductor is used generally. While semiconductor-free methods (such as direct rectification of the electromagnetic radiation, called “rectenna”) have been demonstrated, they have far smaller quantum efficiency compared with the semiconductor-based IRPDs.
For different IR regimes or wavelengths, different semiconductor materials with different effective bandgaps are needed for IR detection. In this section, we review IRPDs based on the mature developed material, namely II–VI, III–V, silicon-based semiconductor, and emerging new materials such as graphene, TMDCs and carbon nanotubes. In the past decade, 2D materials have attracted much attention due to their extraordinary electronic and optical properties, and have a large potential in optoelectronic applications such as photodetection. We will compare the recent progress in IR photodetection based on graphene and graphene-like 2D materials with the commercially mature IRPD materials. Additionally, we will look at the key potentials and the difficulties involved in commercialization and integration of such emerging material into focal plane arrays (FPAs). Figure 1 shows the detectivity of various available detectors with different materials when operated at the indicated temperature.
2.1 II–VI-based IRPD
The II–VI material system, such as HgCdTe, is one of the most important semiconductor alloy systems and the most commonly used material for IR detectors in the spectral range between 1 and 25 μm. The HgCdTe ternary alloy is an ideal IR material system due to these key features: composition-dependent tailorable energy bandgap, high optical absorption coefficient, high quantum efficiency and favorable inherent recombination mechanisms leading to long carrier lifetimes and high operating temperatures. The attributes of HgCdTe translate to flexibility and the capability to produce SWIR, MWIR, and LWIR detectors. HgCdTe IRPD can be divided into two base structures, front illuminated and back illuminated. Rogalski has reviewed the HgCdTe IRPD structures in detail . Despite its unparalleled device performance, such as high detectivity, high quantum efficiency (>70%), and fast response time (several ns), HgCdTe IR detector technology has a number of major limitations, including health hazard, high cost, limited array size, low operating temperature and material fragility. Consequently, other competing IR technologies have been regularly proposed to replace HgCdTe to overcome the limitations of HgCdTe-based IR detectors. These include lead salt alloys, InSb, QW IR detectors, QD IR detectors and type II superlattice (T2SL)-based detectors. Although significant effort has been devoted to developing these alternative IR technologies , , , , , , , , , , , , , , at this stage, HgCdTe IR detectors still dominate high performance IR systems. However, HgCdTe IR technology has its own challenges, including: (1) p-type doping control; (2) lower cost and larger array format size for FPAs; (3) higher operating temperatures; (4) multi-band detection; and (5) advanced plasma dry etching control.
2.2 III–V alloy-based IRPD
The first III–V material used for MWIR detection was InSb, which had the smallest energy gap of any III–V binary alloys known at the time. The energy gap of InSb is poorly matched to the 3–5 μm band at higher operating temperatures, and better performance can be obtained from HgCdTe. InAs is a similar compound to InSb, but has a larger energy gap, so that the threshold wavelength is 3–4 μm. However, MWIR HgCdTe photodiodes have significant higher performance in the 30–120 K temperature range. The InSb devices are dominated by generation-recombination currents in the 60–120 K temperature range because of defect centers in the energy gap.
InGaAs ternary alloy was made available after improvements were made in growing techniques. The energy gap of the In1−x As ternary system spans from 0.35 eV for InAs to 1.43 eV for GaAs. In0.53Ga0.47As alloy (Eg=0.73 eV) lattice matched to the InP substrate has been shown to be a suitable detector material for NIR (1.0–1.7 μm) spectral range compared to HgCdTe and InSb. Having lower dark current and noise than indirect-bandgap germanium, InGaAs is addressing both entrenched applications including lightwave communication systems, low light-level night vision, and new applications such as remote sensing: eye-safe range finding and process control , , , , , , , , . InGaAs photodiodes have shown high device per absorption layer. The photodetector responsivity can be maximized at the desired wavelength of the end-user to enhance the signal-to-noise ratio.
Another material in III–V family which stands out compared to other materials for IRPD is InAsSb. InAsSb ternary alloy is more stable in comparison with HgCdTe and has a fairly weak dependence between the band edge and composition. The stability of this material is conditioned by the stronger chemical bonds available in the lower atomic number III–V family and the larger covalent bonding contribution compared to ionic bonding in HgCdTe. Some other physical properties of InAsSb material are better compared to those of HgCdTe. For instance, its dielectric constant is low and the room temperature self-diffusion coefficient is low. However, the InAsSb ternary alloy does not have a sufficiently small gap at 77 K for operation in the 8–14 μm wavelength range, but work began on SLSs , which will be discussed in Section 3.1.2.
2.3 Silicon/germanium-based IRPD
Silicon, being an indirect bandgap semiconductor with a centro-symmetric crystalline structure, is not directly suited for optoelectronics. Si/Ge IRPDs are usually divided into two types: intrinsic detectors and extrinsic detectors. Silicon intrinsic detectors are usually designed and fabricated as PIN photodiodes or Schottky-barrier detectors .
For intrinsic IRPDs, Si has lower costs and lower leakage current advantage – both stem from the near-perfect processing of this material. Si-based IRPDs are compatible with silicon circuits; however, silicon is not the ideal material for IRPDs due to its bandgap mismatch to many important wavelengths including the telecommunication bands. Si has a lower dielectric constant than Ge, and the related device technology of Si has been extensively developed, including contacting methods, surface passivation, and mature metal oxide semiconductor and CCD technologies. Moreover, Si detectors are characterized by superior hardness for high-energy particles, such as nuclear radiation and space environments. The well-established technology also helps in the manufacturing of uniform detector arrays and the formation of low-noise contacts. Impressive progress in the development of hybrid p-i-n Si-complementary metal oxide semiconductor (CMOS) arrays for the large visible and NIR imaging market has been presented by Raytheon Vision Systems , , . For the longer wavelengths, the most popular Schottky-barrier detector is the PtSi detector, which can be used for detection in the 3–5 μm spectral range. Radiation is transmitted through the p-type silicon and is absorbed in the metal PtSi, producing hot holes which are then emitted over the potential barrier into the silicon, leaving the silicide charged negatively .
For even longer wavelength, extrinsic IRPDs can be used as they can reach up to approximately 300 μm. The spectral range of the extrinsic photodetector is determined by the doping impurity and by the material into which it is introduced. Detectors based on silicon and germanium have found the widest application compared with extrinsic photodetectors on other materials. Increasing interest in extrinsic detectors has been observed due to the creation of multi-element FPAs for application in space and ground-based IR astronomy and on defense space vehicles. Successes in the technology of photodetectors, creation of deep-cooled, low-noise semiconductor preamplifiers and multiplexers, as well as unique designs of photodetector devices and equipment for deep cooling, have ensured the achievement of a record-breaking detectivity close to the radiation limit even under exceedingly low backgrounds in space , . A detailed review of a bulk Si/Ge IR detector can be found in , which shows the mature application of Si/Ge IR detectors.
Table 1 shows some of the best existing IRPD imaging arrays based on the aforementioned material systems.
3 Nanostructures to enhance the electronic properties of the IRPD
Based on the considerations of the previous section, we can further improve the photodetector performance (detectivity bandwidth product) by two methods. First method is based on engineering the electronic properties of the absorbing material for improved figures of merits such as detectivity and quantum efficiency. The second method is based on increasing the coupling of light to the electronic states of the absorbing material. Interestingly, both methods can be implemented by utilizing different micro- and nanofabrication techniques. In the following we will discuss the nanostructures used to enhance the electronic properties of the IRPD, while in Section 4 we will cover the nanostructures used to enhance the optical coupling of the IRPD to free-space photons.
We will first discuss QW and semiconductor superlattice (SL) structures, which are amongst the oldest and most mature nanotechnologies used to enhance the efficiency of the IRPD. SL and QW structures have continued to dominate the field due to the possibility of creating new classes of materials and heterojunctions with unique electronic and optical properties with high uniformity of epitaxial growth over large areas.
3.1 QW-based IRPD
3.1.1 Intersubband QWIP
Figure 2 shows the low-temperature energy bandgap diagram of different semiconductors with diamond and zinc-blende structure versus their lattice constant matching. Thin layers of semiconductors with close lattice constants – within each of the gray zones – can be grown on top of each other, using strain compensation. Such thin QWs and barriers can be designed as shown in Figure 3 to produce localized quantum states within each conduction or valence band, with a specific energy difference to resonate with the targeted IR radiation. Such “intersubband” photodetectors are called QWIPs.
Among the different types of QWIPs, GaAs/AlGaAs QW detectors are the most mature due to the almost perfect natural lattice match between GaAs and AlGaAs , , , , , , , , , , , , . GaAs/AlGaAs QW devices have many advantages, including their ability to be used with standard GaAs-based manufacturing techniques and processing technologies, highly uniform and well-controlled molecular beam epitaxy growth on six-inch GaAs wafers, high yield and thus low cost, more thermal stability, and extrinsic radiation hardness. However, the optical cross-section absorption is limited by the dopant concentrations, leading to a low quantum efficiency and relatively poor performance at temperatures >40 K due to short intersubband lifetimes (dominated by fast phonon relaxation). While some complex quantum structures have been explored , the emerging ideas to address this performance limitation are based on optical antenna and plasmonic structures, which will be discussed in Section 4.
3.1.2 Interband superlattice IRPD
A rapidly maturing III–V IRPD structure is InAs/InxGa1−x Sb (InAs/InGaSb) strained-layer T2SL detectors , , , . The optical absorption of T2SL occurs in interband transition, which makes it an intrinsic device with high quantum efficiency. T2SLs can produce a bandgap that is smaller than constituting semiconductors, due to the staggered (type II) energy band lineup of these layers. However, this band lineup causes low overlap integral between the electron and hole wavefunctions, and hence a low IR absorption. In recent years, T2SL has been further improved by a current blocking layer which has larger energy bandgap than the surrounding SL layers , . An example of this new band diagram can be seen in Figure 4.
Most of the blocking barrier consists of aluminum incorporated into either the InAs or GaSb layer to form the band structure period of the SL either like a W or an M shape. However, the precise position of the barrier in the middle of the well is needed to increase the number of energy states available at the desired energy level , . Razeghi’s group , , ,  showed a blocking barrier T2SL with detectivity as high as 1.05×1012 cm Hz1/2/W at 150 K in the MWIR regime and then a 320×256 pixel FPA was constructed using this design, with imaging possible up to 170 K.
3.2 QD-based IRPD
The desires for higher operating temperatures, higher efficiency, and a lower cost IRPD has given birth to even lower quantum dimensionality than QWs. QDs as show in Figure 5, have zero dimensionality, have been incorporated into different material systems to enhance the efficiency and higher operating temperatures. Here we reviewed the two popular types of QDIPs based on III–V material (InGaAs/GaAs and InAs/InP) , ,  and silicon-based material (Ge/Si) , , .
3.2.1 QDIP based on III–V material
In 1998, the first QDIP based on intersub-level transitions was demonstrated along with the first QD laser . QDIPs are similar to QWIPs but with extra advantages due to the three-dimensional (3D) confinement in the QDs compared to the 2D confinement in QW. There are three major advantages of QDIPs compared to QWIPs: (1) QDIPs are intrinsically sensitive to IR irradiation at normal incidence due to the breaking of the polarization selection rule , (2) QDIPs have lower dark current than QWIPs because of weaker thermionic emission from the QDs with 3D quantum confinement of carriers , and (3) the discrete energy levels in QDs have no dispersion, which reduces the phonon scattering and can lead to longer carrier lifetime (>100 ps), and so higher operating temperatures , . The detection mechanism in QDIPs is also based on intersubband transitions between the quantized energy levels of the dots and continuum states , . However, QDIPs have lower absorption quantum efficiency due to the small fill factor area of QDs and large inhomogeneous broadening of the self-assembled QDs , . This inhomogeneous broadening also makes fine tuning to specific wavelengths difficult, and leads to issues with strain and dislocations with increasing number of absorption layers, diminishing the absorption coefficient.
In the last few decades, Lin et al.  improved the performance of QDIP responsivity, detectivity, as well as demonstrating higher operating temperatures and lower dark currents by using sandwiched QD layers with Al0.3Ga0.7As current blocking barriers. The background-limited infrared photodetector (BLIP) of the improved QDIP was demonstrated to be as high as 250 K . Lin et al.  showed that the QDIP can be further improved in regard to the responsivity and lower dark current by direct doping the QDs. Later on QDIPs with QW active regions, known as DWELL structures, were proposed to improve the detection wavelength tunability with InGaAs strain relief layers , . Surprisingly, DWELL IRPDs turned out to have advantages such as enhancement of absorption, low dark current, and high responsivity , , . DWELL IRPDs have been extensively explored by Krishna’s research group, and some of the main achievements are presented in their review articles . They have demonstrated some impressive results including: (1) multiwavelength operation in the MWIR, LWIR, and VLWIR, (2) fine tuning operating wavelength, (3) tunable bias, and (4) higher operating temperatures, especially for the VLWIR response. A 320×256 LWIR FPA was developed and images were obtained at 78 K ; however, this FPA has low responsivity and quantum efficiency.
3.2.2 QDIP based on Ge/Si heterostructures
Germanium QDs can be grown on Ge/Si and Ge/SiGe/Si multilayer heterostructures using the effect of the self-assembly of semiconductor nanostructures during the heteroepitaxial growth of materials with a large lattice mismatch . Similar to other materials, Ge QDIP improves the performance of the heterostructures in multiple ways, such as by allowing absorption of normally incident electromagnetic radiation, high (up to 1000) photoelectric gain, and lower dark currents in Ge/Si QDIP . High temperature operation QDIP at mid-IR (MIR) has also been achieved, even up to room temperature . However, the quantum efficiency and photocurrent of Ge/Si QDIP are far lower than those of the bulk material. Despite the low quantum efficiency, Ge/Si QDIP is still one of the most popular QDIPs because of its lower cost. This is due to well-established silicon technology for fabricating MIR devices with low defect content and a high spatial homogeneity of photovoltaic characteristics. Ge/Si QDIPs also have better thermal expansion coefficients, which can easily be matched to a silicon readout circuit so that the array size is not limited by the cooling-induced mechanical stresses of the entire structure.
3.3 Nanowires and nanopillar for IRPD
Semiconductor nanowires (NWs) exhibit unique photonic and electrical properties such as high sensitivity and AR due to their unique anisotropic geometry, and high surface-to-volume ratio. NW architectures can be bandgap engineered using compound semiconductor materials and current advanced fabrication technologies. Moreover, NWs of almost all the existing semiconductor materials can now be realized by either top-down or bottom-up approaches. Although a lot of work has been devoted to investigating NW IRPDs in the past few years , , , , , , , most of the reported NW IRPDs are limited in the visible and ultraviolet spectral regions , , , and little work is conducted in the IR region , . III–V semiconductor NWs with narrow bandgaps are considered as promising candidates for constructing IRPDs. To date, IRPDs based on InAs, InP, InGaAs, InPAs, and InGaSb nanowires have been reported , , , . The fabrication of NW IRPDs can be categorized into three types, namely, photoconductor, phototransistor (where photosensitivity is greatly enhanced by an additional gate bias), and heterostructure NW devices including homo-/heterojunction and Schottky photodiodes.
3.3.1 Photoconductor NW IRPD
NW photoconductors are NW-based photodetectors where the material is sandwiched between two electrodes . NW photodetectors based on III–V compound semiconductors are one of the most studied due to their excellent transport properties, easy fabrication, and wide tunability wavelength by alloy bandgap engineering. Also, their low capacitance leads to high operating speeds. For example, an intersecting array of InP NWs can have a fast photoconductive response (14 ps FWHM at 780 nm) . In recent years, InGaAs and InAs have been studied intensely. InGaAs has potential bandgap tunability from the NIR to MIR, as well as high electron mobility and small leakage current. Single-crystal In0.65Ga0.35As nanowires are reported to have a large responsivity of 6.5×103 A/W over a broad range from 1100 to 2000 nm . The photoresponsivity of 5.3×103 A/W was reported in Schottky-Ohmic contacted InAs NW photodetectors as shown in Figure 6 at the wavelength around 1.5 μm . II–VI material NWs, such as CdS, CdSe, ZnSe, CdTe and ZnTe, are typically used for visible light detection. CdS NWs and nanobelts are among the most studied photoconductors in group II–VI for visible and ultraviolet light detection . In the visible-NIR range (400–800 nm), CdTe nanoribbons with p-type conductivity present significant photoresponse to irradiation with a high responsivity of 7.8×102 A/W .
3.3.2 Phototransistor NW IRPD
A phototransistor is a bipolar or unipolar transistor in which light is converted to carriers and the current can be amplified through transistor action, leading to much greater photosensitivity. However, most of the NW phototransistors today have surface recombination loss, as carriers recombine before they can be collected. This problem can be solved by a core/shell design. A good example is an InAs NW phototransistor with a self-assembly photogating layer containing randomly distributed lattice defects as a trapping layer to capture photoexcited electrons . This core/shell-like n-InAs NW phototransistor has a very large photoconductive gain of 105 and a fast response time of 12 ms at the wavelength of 1.2 μm . Single GaAsSb NWs have also shown a decent responsivity of 2.37 A/W with a low operating bias voltage of 0.15 V achieved at the wavelength of 1.3 μm . These GaAsSb NWs were grown in a self-assembly fashion using a horizontal flow metalorganic vapour phase epitaxy reactor at 100 mbar.
3.3.3 Heterostructure NW IRPD
A lot of promising heterostructured NW architectures as shown in Figure 7 adopted methods from thin-film compound semiconductor photodetector technologies such as homogeneous, inhomogeneous, Schottky junction photodiodes, and avalanche photodetector. The p-n/p-i-n junction is normally used for homo/heterojunction NW photodiodes which operate under reverse bias. A single NW of InAs/InAsP axial heterojunctions is reported to have very low dark current, strong polarization dependence, and high photoconductivity when operated at 77 K . Another example of NW heterostructures is core-shell NW junctions which attract a lot of interest due to high efficient photosensing and high light absorption enhancement . For IR detection, GaAs systems are the most widely investigated. Examples include GaAs/AlGaAs core-shell , , , ,  and GaAs/InGaP/GaAs core-multishell NWs . Among them, an NIR photodetector based on a core-shell GaAs/AlGaAs NW exhibited a peak photoresponsivity of 0.57 A/W at room temperature, comparable to large-area planar commercial GaAs photodetectors, and a high detectivity of 7.2×1010 cm Hz1/2 W−1 at λ=855 nm .
Another example of heterostructure NWs is Schottky photodiode structures [usually the construction is an metal semiconductor metal (MSM) photodetector], which exhibit fast response speed . Arguably, the most promising NW photodetectors are the ones based on avalanche multiplication. NW avalanche photodiodes (APDs) with diverse configurations have been demonstrated. These include the “crossed” n-CdS/p-Si NW heterojunction , axial p-i-n single Si NW homojunction , InAsP QD in the axial InP p-n junction , radial GaAs nanoneedle junction , and radial GaAs p-n junction . GaAs-based APD GaAs nanoneedles exhibit an excellent multiplication factor as large as 29 at −2 V and 263 at −8 V .
3.3.4 Si/Ge NW IRPD
Si/Ge NW IRPDs naturally have indirect bandgap which limits it from the high optical absorption application. However, by reducing their dimension, one can increase the quantum confinement and change the band structure. Also, impurity doping can lead to better performance photodetectors. A detailed review of Si/Ge NWs and their applications has been published recently by Ray et al. . However, most of the works on Si/Ge NWs are focused at visible wavelength and very limited applications on NIR and MIR. The most notable work on Si NW in the NIR region with a high responsivity of 2.5×104 A/W in NIR wavelength (900 nm) at a zero bias condition has been reported recently . The Si NWs with 80–100 nm diameter were fabricated by metal (Ag)-assisted electroless chemical etching techniques. Further enhancement of the Au NP-decorated Si NW has also been reported by Jee et al. . The Au NP-decorated Si NWs achieved 63 times enhancement at the wavelength of 1000 nm, but the reported responsivity is around 0.1 A/W.
3.4 New emerging nanomaterials for detection
Graphene was the first 2D material which attracted the attention of many scientists due to its appealing features for nanophotonic applications originating from its zero-bandgap nature . With linear dispersion near the Dirac point  and various forms of light-matter interaction , graphene offers a high optical responsivity in a broad spectral range. However, graphene has low absorption as an IRPD, which is due to its short carrier lifetime  and its zero-bandgap nature. This gives rise to interest in another family of 2D materials – the single-layer TMDCs , such as molybdenum disulfide (MoS2) and tungsten diselenide (WSe2). Unlike graphene, the TMDC family has indirect-to-direct bandgap transitions that occur when the material thickness decreases from multilayer to monolayer. Moreover, TMDCs can easily be incorporated into a wide range of heterostructures with atomic-level control to achieve a higher performance IRPD.
3.4.1 Graphene-based photodetector
Graphene is a promising material for photodetectors compared to conventional semiconductors due to ultrahigh mobility, making it suitable for high-speed communications , , , . Single-atomic-layer graphene is stable, low cost, easy to fabricate, and has high internal quantum efficiency  when used in the NIR and MIR regions for optoelectronic applications. However, single-layer graphene is an inherently weak light absorber, which originates from its short interaction length , , , and the narrow effective area of lateral graphene p-n junctions also limits the efficiency of photocarrier extraction , , . In other words, the applications of grapheme-based photodetectors are limited by the lower external quantum efficiency and photoresponsivity in comparison to traditional photodetectors .
Various approaches have been proposed to enhance the sensitivity, including the introduction of a bandgap or an electron trap layer, such as building graphene QD-like structures  or cutting graphene into nanoribbons . However, these bandgap opening methods degraded the electronic performances of graphene, especially the high mobility, thus leading to a decrease in the photoresponse speed . Unfortunately, the overall quantum efficiency of graphene is quite low compared to conventional materials such as III–V semiconductors, due to the nature of zero bandgap structures. Figure 8A summarized the responsivity versus the response time for detectors based on difference 2D material, and comparison with commercial silicon and InGaAs photodiodes. Figure 8B also showed the wavelength dependency of different 2D material use in photodetector.
3.4.2 TMDC-based photodetector
Recently, another family of 2D materials with far better optical properties has emerged. Single-layer TMDCs , such as MoS2 and WSe2, have been intensely researched. The direct bandgap of monolayer TMDCs leads to efficient light emission covering the energy range from below 1 eV to well above 2.5 eV  and beyond, making them promising for a wide range of optoelectronic devices. Bandgap tunability with the layer thickness is another important property of this material. The bandgaps of trilayer, bilayer, and monolayer MoS2, determined by photoluminescence, change from 1.35 to 1.65 and 1.8 eV , respectively. The bandgap of other typical TMDCs, such as WSe2, MoSe2 , WS2 , and GaTe , also increases with decreasing layer thickness, due to the quantum confinement of carriers in the direction normal to the 2D plane. 2D TMDC photodetectors exhibit decent responsivity from the IR to the near UV range. The first reported monolayer MoS2 photodetector  exhibited a responsivity of 7.5 mA/W in the visible range. Choi et al.  demonstrated a responsivity of ~100 mA/W by using a multilayer MoS2 photodetector. However, the speed of photoresponse is relatively slow (ranging from microseconds to seconds) owing to the trapping of photocarriers. It is also noticeable that most of the high-sensitivity TMDC-based photodetectors reported above are for visible and NIR application. However, the recently re-discovered few-layer black phosphorus (bP) is an interesting material for photodetection for IR and far infrared (FIR), especially due to its intermediate bandgap between graphene (i.e. zero bandgap) and TMDCs. The study by Youngblood et al.  shows an intrinsic responsivity of up to 135 mA/W and 657 mA/W in 11.5-nm- and 100-nm-thick devices, respectively, at room temperature and at a frequency of 3 GHz. The few-layer bP is embedded within an on-chip waveguide structure with a few-layer graphene top gate, allowing for optimal interaction with light and tunability of the carrier density. The bP-based device presented in  stands out from the rest by showing comparable performance to both a commercial silicon photodiode and a graphene-based detector. Despite the large amount of funding and research invested on 2D materials, there is currently very limited set of 2D material covering the IR region of the spectrum . This might represent an important future research area, considering the strong need for conformal and thin IR detectors.
3.4.3 2D material-based heterostructure IRPD
As discussed in the previous section, conventional graphene and TMDC-based phototransistors have relatively poor responsivity (~10−2 A/W) owing to their weak optical absorption. Recently this limitation has been addressed by 2D material synthesized with other semiconductor material, nanostructured or different 2D materials. For example, MoS2 nanocrystal on silicon on insulator structure , , MoS2/bp heterojunctions , graphene/MoTe2/graphene heterostructures , graphene/MoS2 heterojunctions, and WSe2/MoS2 heterojunction photodetectors  show significant improvement in responsivity to the visible and NIR regions. A recent review paper on different dimensional material heterostructures  summarizes the works on different dimensional material for increasing the responsibility of the 2D material in the IRPD. One of the most notable works is QD on the graphene photodetector, where the QD optical absorption leads to a large photoexcited charge carrier in the graphene channel, and added with the high mobility of graphene, the QD/graphene heterojunction photodetector achieves a massive responsivity exceeding 107 A/W in the NIR region . However, most of the mixed-dimensional heterojunction photodetectors discussed above have a relatively slow response (101–10−6 s) due to their enhanced capacitance and charge traps. Nonetheless, there are a growing number of active research studies on faster IRPD devices with lower responsivity based on 2D heterojunctions. For example, single walled carbon nanotubes/MoS2 p-n heterojunction photodetectors show responsivity in the visible and NIR with a response time of 15 μs . Similarly, field-effect transistors based on the heterojunction between a monolayer of WS2 and PbS CQDs demonstrated a photoresponsivity of ~14 A/W, while exhibiting a fast photoresponse time of ~153 μs. Most of such 2D heterojunction-based devices have the potential to become low-cost and high-performance IRPDs, while significant future research is needed to the commercialization stage.
In the past decade, CQD as shown in Figure 9 has emerged as one of the most appealing potential nanomaterials for IRPDs. CQDs show quantum confinement and are commonly made of II–VI, III–V, and IV–VI semiconductors by means of inexpensive and scalable wet-chemical synthetic procedures , . Photodetection by CQD is based on the conductivity of CQD solid films. The first generation of CQD light detectors focused on photoconduction , where photogeneration of an electron-hole pair is followed by capture of one type of carrier (can be the electrons or holes), while the other remains substantially free to travel. Most of the CQD photoconductors reported until now are for the NIR to MIR regime, and based on the lead chalcogenide nanocrystals , . The speed of these CQD photoconductor devices depends on the carrier lifetime. Very large photoconductive gain, in the range of 103–106, can be achieved . Photodetectors based on CQDs exploit tuning of the band edge to suitably chosen spectral cutoff energy, enabling dark current minimization for a given desired spectral response. The dark current is amplified via the same gain mechanism as photocurrent. However, it could be minimized by using photo-field-effect transistors . The transistor introduces a threshold, so that turn-on occurs only after a certain photocarrier density (hence light level) is exceeded. PbSe CQD field effect phototransistors based on metallic (Au/Ag) nanowire transparent electrodes with a high responsivity of 2×104 A/W and a high specific detectivity of 7×1012 Jones at low operation voltage (~1 V) in the NIR have been reported .
The speed of CQD detectors has been historically an issue. The extended lifetimes of trapped photocarriers, which are the source of slow response, can be controlled via the CQD surface chemistry and surface passivation . Extracting photocarriers by using the built-in field in a photodiode provides a ready path to achieving efficient photocurrent generation; when the excited-state lifetime is tipically ~100 ns, a built-in or applied potential on the order of 1 V can achieve a drift-based extraction time comparable with the excited lifetime when the lower of the electron or hole mobility exceeds 2×10−3 cm2/V s in the MIR regime . Similarly, in the MIR regime, the CQD photodiode based on monodispersed HgSe CQD photodetectors that are illuminated with radiation resonant with intraband electronic absorption between 3 and 5 μm is reported. The HgSe CQD photodetector achieved the lowest dark current of 80 μA, but with a relatively small detectivity of 8.5×108 Jones at 80 K .
The maturity of the CQD in imaging has been much faster compared to other nanostructures. PbS CQD-based FPAs and camera prototype devices have been demonstrated, with a wide range of array and pixel sizes. The imaging arrays display a spectral response from 400 to 2000 nm, a high dynamic range of ~60 dB, a fast rise/fall time of about 2 μs, and a very respectable detectivity ~1012 Jones , . These FPAs display multispectral sensitivity with detectivity comparable to InGaAs devices that currently dominate the commercial market. However, they offer a very attractive low-cost route, since they can be spin-coated on top of silicon readout integrated circuit (ROIC) chips. This approach could in principle produce a high-yield and low-cost alternative to the current indium bump-bonding of the sensor chip to the ROIC chip.
4 Nanostructures to enhance the optical coupling of IRPD
As mentioned in Section 3, the performance of the IRPD can be increased by maximizing the radiation flux coupling to the photonsensing medium. Traditionally, there are a lot of methods to enhance the flux entering the structure using refractive concentrator, reflective concentrator, and AR coating. Over the past few decades, with the advances in nanofabrication, a lot of nanostructures such as subwavelength structures (SWSs), photonic crystals (PCs), metamaterial, plasmonic structure, and optical antenna have been implemented to help improve the optical coupling to IRPDs. In this review, we will discuss the nanostructure-based approaches for enhanced optical coupling to the IRPD.
4.1 Nanostructure-based AR coating and light trapping effect
As discussed in Section 3, new IRPD materials such as graphene, 2D material, and NW have a very thin layer which leads to low absorption. A possible way to increase the absorption probability, while at the same time keeping the detector optical thickness constant, is to ensure a longer path of light through the detector and to maximize the incident light on the structure. The idea is to maximize the incident light and trap the light that has already entered the active region and keep it as long as possible. The beam could be returned into the detector from its surface, immediately before leaving the structure. The incident optical flux into an optical element can be maximized by decreasing reflection from the incident surface.
4.1.1 SWS for AR
Most of the semiconductor materials used for IRPDs have a large refractive index (typically 3–4). Therefore, AR structures are important for IRPDs, since the loss due to reflection from the surface is around 25–40%, and even higher at increased incident angles. The simplest AR coating can be made by depositing one or several optically thin films on the surface utilizing interference effects to cancel the back-reflection . However, this approach has significant limitations due to the change of reflectivity with the incident angle. This is a rather fundamental limitation in thin-film interferometric filters, since the wavenumber (k-vector) parallel to the films is preserved throughout all layers. Another related issue is the narrow spectral response band of this approach, which renders such AR coating layers ineffective in modern “multi-color” and “multi-band” IRPDs. Antireflective condition can be generated by forming SWSs in front of the detector . Such structures are also denoted as high spatial frequency structures or subwavelength surface textures . SWSs generally have a two-fold function in light management in photodetectors: since they effectively represent gradient-index structures, they produce a broadband impedance matching that leads to a broadband AR performance. SWSs can also be designed to function as efficient mode couplers that couple the incident mode to many modes inside the high-index detector volume, and with a diverse polarization. This property can be used to couple to material with specific polarization, such as QWIP. The optical behavior of SWSs can be satisfactorily approximated in a majority of situations by using the effective medium theory .
SWS structures can be formed randomly across the surface or as periodic arrays. Random SWS structures give broadband antireflective properties, but repeatability is an issue. On the other hand, periodic SWSs can be designed based on required wavelengths, but usually the fabrication is more complex and costly. Random SWSs can be formed by self-assembled nanospheres to perform nanosphere lithography by reactive-ion etching and obtain patterns of nanocavities on interface material . For example, a cone-shaped Si nanostructure can reduce the reflectance (a planar SI) from 30% to 3% by using inductively coupled plasma – reactive ion etching at the NIR wavelength (800–1000 nm) . This irregular structure is also referred to as random surface corrugations. Similarly for the periodic SWS, periodic structure lithography (holographic lithography, e-beam lithography) is performed followed by chemical or physical etching. SWSs offer important advantages over interference AR coatings. Examples of period SWSs include moth eye-like structures, 2D pyramidal, and also nanopillars. Figure 10 shows that SWSs can effectively enable fabrication of any desired effective refractive index profile . These SWS nanostructures can efficiently reduce the reflection of the surface leading to higher absorption in a wide range of wavelengths including the NIR and MIR regions .
4.1.2 Resonant cavity structure
One the most commonly used light-trapping structures in IRPDs is the resonant cavity structure (Figure 11). The absorption within the detector can be significantly increased by placing the active area into a resonant cavity between resonator mirrors (usually consisting of a highly reflective mirror and a distributed Bragg mirror). If the product of the effective absorption coefficient and the active area thickness is small enough, the cavity will maintain a single allowed optical mode, while the other modes will be suppressed . The resonant cavity enhanced (RCE) photodetector is usually known as RCEPD.
The amplification of the radiation at the resonant wavelength in an RCE device and rejection of others results in an increased spectral selectivity of resonant detectors. However, the RC structure also decreases the speed of the detector  which becomes limited by carrier transit time. Another disadvantage is an increase of the allowed operating temperature because of the shift of the BLIP limit . RCE structures were used to improve performance in almost all IRPD systems such as p-i-n diodes , QW , T2SL , QD , quantum dot in quantum well , and light emitting diodes .
4.1.3 PC structure
Research on PC structures with a periodic refractive index modulation has opened up several ways to control light. Most existing devices are realized as 2D PC structures, as they are compatible with standard semiconductor processing. PC behaves as a high reflection coefficient mirror for all wavelengths within the photonic bandgap (PBG), and the waves with such wavelengths are evanescent within it. An important property of PC is defect modes, i.e. the allowed energy modes within their PBG which appear when the symmetry of the PC is broken , .
The use of a PC cavity to improve characteristics of IRPDs was described in . The photodetector is enclosed within a PBG structure with a PBG either equivalent to the electronic bandgap of the utilized semiconductor material or larger than it. A defect may be introduced in the PC on the incident side of the photodetector, and its transmission peak adjusted to a desired wavelength. Such an approach improves the performance of the detector in two ways at the same time. As other methods of photodetector enhancement through optical path increase, it increases the probability of absorption of useful radiation in the active region and thus improves quantum efficiency and the responsivity. At the same time, reabsorption (photon recycling) increases the radiative lifetime and thus shifts the BLIP detectivity limit. The photoresponse of the PCS-QWIP (Figure 12) shows a wider response peak but additionally displays several pronounced resonance peaks .
4.2 Nanostructures for enhanced light-matter interaction
A field of research that is currently exponentially growing is light-matter interaction structures such as plasmonic and nanoantenna . Dielectric or metallic nanostructures can enhance the absorption cross-sections of the photosensitive material, typically by electromagnetic fields localized within subwavelength areas. Unlike cavities discussed in the previous section, plasmonic and metallic nanoantennas as shown in Figure 13 provide extreme field concentration and strong light-matter interaction across a broad spectral band. They have been intensively investigated due to the large enhancement on the absorption of thin layer IRPDs such as QWIP, graphene, and other 2D material.
4.2.1 Plasmonic enhancement in IRPD
Surface plasmon-mediated light-trapping schemes for photodetectors ,  may be divided into two distinct groups; namely, (1) localized surface plasmon consists of plasmonic nanoparticles or nanovoids, and (2) surface plasmon polariton consists of different diffractive structures . The former includes field localization and generation of hotspots , plasmon-based singular optics , and metamaterial-based transformation . The latter includes structures such as gratings  for field coupling into guided modes and subwavelength plasmonic crystals that may be periodic  or quasi periodic .
Among subwavelength PCs described within the context of IR photodetection, an important position belongs to 2D arrays of nanoapertures in opaque metal film. Such structures first drew attention for their ability to transmit light in spite of the dimensions of nanoapertures being much smaller than the operating wavelength. This effect is commonly known as the extraordinary optical transmission (EOT) . EOT is a result of the excitation of surface plasmon polaritons at the metal surface. It forces the electromagnetic waves incident to the surface to pass through the apertures. The transmission couples all incident electromagnetic energy on the surface to the mode impinging through the aperture. Thus, large field localizations appear in the apertures. This behavior effectively corresponds to impedance matching between propagating waves and the perforated metal film.
Interesting structures of these types similar to Figure 14 have been developed, to enhance the weak optical absorption of graphene. Compared to traditional structures including cavities ,  and waveguides , , these metal plasmonic structures ,  can enhance the light-matter interaction over a broad spectral band. A planar microcavity based on graphene sandwiched between two highly reflecting mirrors achieved a 26-fold enhancement in the absorption of graphene with a responsivity of 21 mA/W . These are also used for other 2D materials , . The third approach is to enhance the local electrical field, which is guided into the region of the graphene photoactive area using plasmonic metal structures, hence increasing the light absorption , . This field enhancement is proven to dramatically improve the performance of graphene-based photodetectors. The graphene photodetectors can couple with metal nanostructures at different resonance frequencies, and the photocurrent and external quantum efficiency could be enhanced by 1500% .
4.2.2 Optical antenna
Nanoantenna or optical antenna  is a structure that couples the propagating light waves and the evanescent (near) fields. The large change of the photon momentum is the unique property of such devices. Depending on the nanoantenna type and its design, the mode confinement in the evanescent field can be deeply subwavelength. The simplest and the most basic nanoantenna is a nanosphere. This structure actually behaves like a dipole and its scattering properties can be calculated using the Mie theory . Much larger field localizations are obtained using two identical nanospheres (known as dimer) or in an array (nanoparticle chain) . Many other shapes can be used as nanoantennas such as nanorods, two-wire  bowtie  diablo-type nanoantenna , the Yagi-Uda, group of director nanorods , spiral nanoantennas , and those with fractal geometries . Many other shapes can be used.
In 2010, our group reported an ultra-thin QWIP integrated with a nanohole-array optical antenna (Figure 15) . The optical antenna captures far-field light and enhances its concentration at the active region of QWIP. The polarization selection rule in intersubband QWs prevents absorption of normal-incident light. The nanohole-array antenna can efficiently convert the polarization of normal-incident light to a perpendicular polarization by exciting the surface plasmons on the surface of the perforated metal. The peaks of responsivity and detectivity both occur at 8 μm, reaching 7 A/W and 7.4×1010 cm Hz1/2/W, respectively. Such a high responsivity and detectivity is due to a high quantum efficiency (QE) of 40%, which is an order of magnitude larger than the QE of a plain QWIP structure with a similar thickness of ~λe QE.
Several similar structures were reported since then, including a plasmonic optical antenna coupled with a LWIR QDIP . The antenna consists of a pair of half-wavelength dipole antennas with a 20 nm gap in between. E-field enhancement of more than 30 times is obtained in the gap, corresponding to over 900 times light intensity enhancement. This LWIR QDIP shows strong incident-angle-dependent photocurrent enhancement with a clear antenna-induced detection pattern (i.e. directivity).
In the last decade, high-gain and high-directivity IRPDs have been intensely studied. Optical antennas coupled with metal-oxide-metal (MOM) diodes have been used to demonstrate beam steering in the MIR (10 μm) . The devices show narrow beam widths of ~35° FWHM in power, and reception angles of ±50°. Two dipole antennas coupled to coplanar strip waveguides, inspired by similar systems in microwave electronics , are coupled to a rectifying MOM diode. Due to the interference between the two antennas, the diode can be placed off-center and “see” off-normal angles. Recently, a double-metal nanoantenna as microcavity has been fabricated on a QWIP detector to confine light in 3D . Strong subwavelength light confinement of this microcavity antenna leads to three times reduction in dark current due to the reduced detection area. The structure achieved a peak responsivity of 0.074 A/W photoconductive gain g=0.25 at a wavelength of 9 μm at all incident angles.
Recently, our group proposed a novel metallo-dielectric hybrid antenna, with a metallic cavity antenna coupled to a photonic jet produced by a dielectric microsphere. This structure as shown in Figure 16 has a high QE of about 50% and a high directivity of about 20 dB. The quantum efficiency and the directivity are significantly better than the bowtie optical antenna with ~1% QE and poor directivity gain (a few dBs) . When integrated with QWIP, the detectivity of the hybrid antennas is more than 30 times higher than the limit of conventional QWIP detectors at all temperatures due to the strong directivity gain. However, the optical antennas cannot increase the detectivity of the interband detector beyond the limit of conventional devices, because of their comparable radiative and non-radiative lifetime. Another similar optical antenna integrates a split-ring bull’s eye antenna on a germanium detector to focus light from a relatively large area into a subwavelength germanium slab. The measured photocurrent is improved by seven times, with a responsivity of 3.93 mA/W at 1310 nm .
4.2.3 Metamaterial structures
Subwavelength dielectric and metallic structures made in 1D, 2D, and 3D arrays have created a novel class of structures known as electromagnetic metamaterials , . They could be defined as artificial structures whose effective electromagnetic properties cover regions beyond what is found in nature. It is possible to obtain effective relative dielectric permittivity, relative magnetic permeability, and refractive index in a vastly expanded range by tailoring their geometry and material properties (example as shown in Figure 17).
For example, negative index metamaterials are combined with dielectrics to produce a broad range of new device properties , , , , . Metamaterial-containing multilayers exhibit many peculiar properties, with both theoretical and practical interests. For example, it is possible to fabricate resonant cavities with subwavelength dimensions . Such structures might be used to reduce the volume of the absorber, and hence the dark current/noise, while maintaining a high QE. Another application that is related to IRPDs is a multilayer metamaterial based on the so-called double fishnet structure with enhanced IR absorption and a relatively large directivity . Compared with the aforementioned photonic jet approach, this method is all planar, and uses standard micro/nano-fabrication methods. A persisting problem with such metamaterials is their large absorption losses – specifically in their negative refractive index range, as well as relatively narrow bandwidths due to their resonant nature.
5 Advance application of IRPD
In the past, the main application for IRPDs was for surveillance and warning for military or Department of Defense. Currently, the applications of IRPDs are widely extended to different industries such as automotive, medical, semiconductor, food, and also astronomy. In the past, night vision and surveillance systems were the main application of IRPDs . However, IR cameras have been adopted in various industries such as automation, automotive, civil engineering, and food production in the modern society due to their non-contact precision temperature measurement and non-destructive monitoring. IR cameras have been used for food quality control , semiconductor chip and device control , paved road condition control, and various other monitoring activities (http://www.flir.com/home/). As for medical application, various medical tools such as blood vein monitor , brain trauma detection , diabetic neuropathy , thermography, and cancer cell detection  are invented using IR technology due to the non-contact and non-destructive monitoring (http://medcitynews.com/2013/02/5-innovative-uses-for-infrared-technology-from-early-bedsore-detection-to-preventing-surgical-errors-video/). However, a lot of the medical tools are in the testing phase and many more will be available in the industry within the next decade. One of the most interesting applications for the IRPD camera is astronomy. A review of Figure 18 shows that a lot of molecules can be detected using their unique IR signature. Molecules such as H2, O2, CO2, and water are essential for life . Based on the IR detection from the light from exoplanets, we can potentially determine whether they are habitable or not. This is one of the most important missions in astronomy. However, up to now most highly sensitive IRPD cameras required cryogenic cooling, which makes the camera bulky and increases the maintenance cost. The key emerging factors for future IRPD technologies are, namely, (1) the possibility of making large imaging FPAs, since most applications require arrays of detectors, (2) room-temperature or TE-cooled imaging systems, since most of the current sensitivity IRPD cameras require cryogenic cooling, (3) the ability to integrate with silicon microcircuit technologies to make more compact and low-cost systems, and (4) possibility of mass production, so that the cost of the IRPD devices or cameras can be lowered.
6 Conclusion and future prospect
In conclusion, we have reviewed novel nanotechnology approaches for IRPDs, and compared them with the traditional solutions. The rapid progress of the IR photodetection in the recent history is partly due to the advances in micro-nano fabrication and technology. We anticipate that IRPDs will see increasing use in a number of fields, ranging from the military target detection to environmental sensing. Imaging technology has become one of the most important directions in IRPDs. Bulk detectors such as AlGaAs, HgCdTe, and SiGe have been widely commercialized due to ease of large-scale fabrication, flexibility in the absorption wavelengths covering almost all IR bands, and high responsivity at cryogenic temperatures. However, low dark current and high performance IRPDs at high temperatures is highly needed in many emerging application areas. Advances in nanofabrication enable QWIP and QDIP detectors to perform in the longer wavelength bands, and with a higher operating temperature than their bulk counterparts.
Moving forward, progress in the field of IRPDs may come from dramatically different sources. In recent years, graphene and other 2D materials have been intensely researched for higher operating temperature and lower cost IRPD production. However, these new materials suffer from a low absorption coefficient, a high sensitivity to the ambient, and a large area fabrication limitation.
One immediate direction for the 2D material might be to follow the CQD technology development path, which has settled on producing optically thick CQD layers capped with sealing layers. In the long run, however, these low-dimensional materials have the potential to surpass the performance of bulk semiconductors, since they allow intimate integration of new SWSs such as plasmonic structures and metamaterial. As such, they hold the potential to achieve higher detectivity in the IR bands and at elevated temperatures. Table 2 summarized the advantages and disadvantages of different type of IRPDs discussed in this review paper, as well as the current status for the applicability to large area FPA fabrication.
Kutzscher EW. Review on detectors of infrared radiation. Electro-Opt Syst Design 1973;5:5. Google Scholar
Rollin BV, Simmons EL. Long wavelength infrared photoconductivity of silicon at low temperatures. Proc Phys Soc 1952;B65:995–6. Google Scholar
Shepherd F, Yang A. Silicon Schottky retinas for infrared imaging. IEDM Tech Dig 1973;1973:310–3. Google Scholar
Melngailis J, Harman TC. Single-crystal lead-tin chalcogenides. In: Willardson RK, Beer AC, eds. Semiconductors and semimetals. New York, Academic Press, 1970. Google Scholar
Harman TC, Melngailis J. Narrow gap semiconductors. In: Wolfe R, ed. Applied solid state science. New York, Academic Press, 1974. Google Scholar
Rogalski A. History of infrared detectors. Optoelectron Rev 2012;20:279–308. Google Scholar
Cellek OO, Ozer S, Besikci C. High responsivity InP-InGaAs quantum well infrared photodetectors: characteristics and focal plane array performance. IEEE J Quantum Electron 2005;41:980–5. CrossrefGoogle Scholar
Gunapala S, Ting D, Bandara S, et al. A large-scale quantum dot IR focal plane array. SPIE Newsroom, 2008. DOI: 10.1117/2.1200803.1043. Google Scholar
Lim H, Tsao S, Zhang W, Razeghi M. High-performance InAs quantum-dot infrared photodetectors grown on InP substrate operating at room temperature. Appl Phys Lett 2007;90:131112. CrossrefGoogle Scholar
Haddadi A, Chen G, Chevallier R, Hoang AM, Razeghi M. InAs/InAs1−x Sbx type-II superlattices for high performance long wavelength infrared detection. Appl Phys Lett 2014;105:121104. CrossrefGoogle Scholar
Olsen GH, Joshi AM, Mason SM, et al. Room-temperature InGaAs detector arrays for 2.5 μm. Proc SPIE 1989;1157: 276–82. Google Scholar
Olsen GH. InGaAs fills the near-IR detector-array vacuum. Laser Focus World 1991;27:A21–30. Google Scholar
Joshi AM, Ban VS, Mason S, Lange MJ, Kosonocky WF. 512 and 1024 element linear InGaAs detector arrays for near-infrared (1–3 μm) environmental sensing. Proc SPIE 1992;1735:287–95. CrossrefGoogle Scholar
Kozlowski LJ, Vural K, Arias JM, Tennant WE, DeWames RE. Performance of HgCdTe, InGaAs and quantum well GaAs/AlGaAs staring infrared focal plane arrays. Proc SPIE 1997;3182:2–13. CrossrefGoogle Scholar
Kilcoyne S, Malone N, Harris M, Vampola J, Lindsay D. Silicon p-i-n focal plane arrays at Raytheon. Proc SPIE 2008;7082:70820J. Google Scholar
Shepherd FD. Schottky diode based infrared sensors. Proc SPIE 1984;443:42–9. Google Scholar
McCreight CR, McKelvey ME, Goebel JH, Anderson GM, Lee JH. Detector arrays for low-background space infrared astronomy. Laser Focus/Electro-Optics 1986;22:128–33. Google Scholar
Esaki L. A bird’s-eye view on the evolution of semiconductor superlattices and quantum wells. IEEE J Quant Electron 1986;QE22:1611–24. Google Scholar
Gunapala SD, Bandara SV. Recent development in quantum-well infrared photodetectors. Thin films, Vol. 21, New York, Academic Press, 1995. Google Scholar
Gunapala SD, Bandara SV, Liu JK, et al. Long-wavelength 640×486 GaAs/AlGaAs quantum well infrared photodetector snap-shot camera. IEEE Trans Electron Dev 1988;45:1890–5. Google Scholar
Gunapala SD, Bandara SV. Quantum well infrared photodetectors. Francombe MH, ed. Handbook of thin devices, Vol. 2, San Diego, Academic Press, 2000. Google Scholar
Manasreh MO, ed. Semiconductor quantum wells and superlattices for long-wavelength infrared detectors. Norwood, MA, Artech House, 1993. Google Scholar
Mailhiot C, Smith DL. Long-wavelength infrared detectors based on strained InAs/Ga1−x InxSb type-II superlattices. J Vac Sci Technol 1989;A7:445–9. Google Scholar
Fuchs F, Burkle L, Hamid R, et al. Optoelectronic properties of photodiodes for the mid- and far-infrared based on the InAs/GaSb/AlSb materials family. Proc SPIE 2001;4288:171–82. CrossrefGoogle Scholar
Nguyen BM, Razeghi M, Nathan V, Brown GJ. Type-II “M” structure photodiodes: an alternative material design for mid-wave to long wavelength infrared regimes. Proc SPIE 2007;6479:64790S. CrossrefGoogle Scholar
Nguyen BM, Hoffman D, Delaunay PY, Razeghi M. Dark current suppression in type II InAsGaSb superlattice long wavelength infrared photodiodes with M-structure barrier. Appl Phys Lett 2007;91:163511. CrossrefGoogle Scholar
Chakrabarti S, Stiff-Roberts A, Su X, Bhattacharya P, Ariyawansa G, Perera A. High-performance mid-infrared quantum dot infrared photodetectors. J Phys D Appl Phys 2005;38:2135. CrossrefGoogle Scholar
Gunapala SD, Bandara SV, Hill CJ, et al. Demonstration of 640×512 pixel long-wavelength infrared (LWIR) quantum dot infrared photodetector (QDIP) imaging focal plane array. Infrared Phys Techn 2007;50:149–55. CrossrefGoogle Scholar
Konle J, Presting H, Kibbel H, Thonke K, Saucer R. Enhanced performance of silicon based photodetectors using silicon/germanium nanostructures. Solid-State Electron 2001;45:1921–5. CrossrefGoogle Scholar
Elfving A, Larsson M, Holtz PO, Hansson GV, Ni WX. Efficient near infrared Si/Ge quantum dot photo-detector based on a heterojunction bipolar transistor. In: Gregorkiewicz T, Elliman RG, Fauchet PM, Hutchby JA, eds. Optoelectronics of group-IV-based materials. Warrendale, PA, Materials Research Society, 2003. Google Scholar
Kim S, Mohseni H, Erdtmann M, Michel E, Jelen C, Razeghi M. Growth and characterization of InGaAs/InGaP quantum dots for mid infrared photo conductive detector. Appl Phys Lett 1998;73:963–5. CrossrefGoogle Scholar
Jiang J, Tsao S, O’Sullivan T, et al. High detectivity InGaAs/InGaP quantum-dot infrared photodetectors grown by low pressure metal organic chemical vapor deposition. Appl Phys Lett 2004;84:2166–8. CrossrefGoogle Scholar
Lin S, Tsai Y, Lee S. Photovoltaic quantum-dot infrared detectors. Appl Phys Lett 2001;78:2784–6. Google Scholar
Kim ET, Chen Z, Madhukar A. Tailoring detection bands of InAs quantum-dot infrared photodetectors using Inx-Ga1-xAs strain-relieving quantum wells. Appl Phys Lett 2001;79:3341–3. CrossrefGoogle Scholar
Raghavan S, Rotella P, Stintz A, et al. High-responsivity, normal-incidence long-wave infrared (λ ~ 7.2 μm) InAs/In0.15Ga0.85As dots-in-a-well detector. Appl Phys Lett 2002;81:1369–71. CrossrefGoogle Scholar
Singha RK, Manna S, Das S, Dhar A, Ray SK. Room temperature infrared photoresponse of self-assembled Ge/Si  quantum dots grown by molecular beam epitaxy. Appl Phys Lett 2010;96:233113. CrossrefGoogle Scholar
Liu XQ, Liu X, Wang JL, Liao CN, Xiao XH. Scalable integration of indium zinc oxide/photosensitive-nanowire composite thin-film transistors for transparent multicolor photodetectors array. Adv Mater 2014;26:2919–24. CrossrefPubMedGoogle Scholar
Bube RH. Photoconductivity of solids. New York, Wiley, 1960. Google Scholar
Logeeswaran VJ, Sarkar A, Islam MS, et al. A 14-ps full width at half maximum high-speed photoconductor fabricated with intersecting InP nanowires on an amorphous surface. Appl Phys Mater Sci Process 2008;91:1–5. CrossrefGoogle Scholar
Guo N, Hu W, Liao L, et al. Anomalous and highly efficient InAs nanowire phototransistors based on majority carrier transport at room temperature. Adv Mater 2014;6:8203–9. Google Scholar
Gu Y, Kwak ES, Lensch JL, Allen JE, Odom TW, Lauhon LJ. Near-field scanning photocurrent microscopy of a nanowire photodetector. Appl Phys Lett 2005:87;043111. Google Scholar
Chuang LC, Sedgwick FG, Chen R, et al. GaAs-based nanoneedle light emitting diode and avalanche photodiode monolithically integrated on a silicon substrate. Nano Lett 2011;11:385–90. CrossrefPubMedGoogle Scholar
Persano A, Nabet B, Taurino A, Prete P, Lovergine N, Cola A. Polarization anisotropy of individual core/shell GaAs/AlGaAs nanowires by photocurrent spectroscopy. Appl Phys Lett 2011;98:153106. CrossrefGoogle Scholar
Ray SK, Katiyar AK, Raychaudhuri AK. One-dimensional Si/Ge nanowires and their heterostructures for multifunctional applications – a review. Nanotechnology 2017;28:092001. CrossrefPubMedGoogle Scholar
Das K, Mukherjee S, Manna S, Ray SK, Raychaudhuri AK. Single Si nanowire (diameter ≤100 nm) based polarization sensitive near-infrared photodetector with ultra-high responsivity Nanoscale 2014;6:11232–9. CrossrefGoogle Scholar
Jee SW, Zhou K, Kim DW, Lee JH. A silicon nanowire photodetector using Au plasmonic nanoantennas. Nano Convergence 2014;1:1–7. Google Scholar
Freitag M, Low T, Xia FN, Avouris P. Photoconductivity of biased graphene. Nat Photon 2013;7:53–9. Google Scholar
Wang QH, Kalantar-Zadeh K, Kis A, Coleman JN, Strano MS. Electronics and optoelectronics of two-dimensional transition metal dichalcogenides. Nat Nanotechnol 2012;7:699–712. CrossrefPubMedGoogle Scholar
Koppens F, Mueller T, Avouris P, Ferrari A, Vitiello M, Polini M. Photodetectors based on graphene, other two-dimensional materials and hybrid systems. Nat Nanotechnol 2014;9:780. CrossrefPubMedGoogle Scholar
Saleh BE, Teich MC. Fundamental of photonic. New Jersey, Wiley, 2007. Google Scholar
Yan K, Wu D, Peng H, et al. Modulation-doped growth of mosaic graphene with single-crystalline p-n junctions for efficient photocurrent generation. Nat Commun 2012;3:1280. CrossrefPubMedGoogle Scholar
Ryzhii V, Ryzhii M, Ryabova N, Mitin V, Otsuji T. Graphene nanoribbon phototransistor: proposal and analysis. Jpn J Appl Phys 2009;48:04C144. Google Scholar
Huo N, Yang S, Wei Z, Li SS, Xia JB, Li J. Photoresponsive and gas sensing field-effect transistors based on multilayer WS2 nanoflakes. Sci Rep 2014;4:5209. Google Scholar
Liu F, Shimotani H, Shang H, et al. High-sensitivity photodetectors based on multilayer GaTe flakes. ACS Nano 2013;8:752–60. Google Scholar
Youngblood N, Chen C, Koester SJ, Li M. Waveguide-integrated black phosphorus photodetector with high responsivity and low dark current. Nat Photonics 2015;9:247–52. Google Scholar
Mukherjee S, Biswas S, Das S, Ray SK. Nanotechnology solution-processed, hybrid 2D/3D MoS2/Si heterostructures with superior junction characteristics. Nanotechnology 2017;28:135203. PubMedCrossrefGoogle Scholar
Zhang K, Fang X, Wang Y, et al. Ultrasensitive near-infrared photodetectors based on a graphene-MoTe2-graphene vertical van der Waals heterostructure. ACS Appl Mater Interfaces 2017;9:5392–8. CrossrefGoogle Scholar
Jariwala D, Marks TJ, Hersam MC. Mixed-dimensional van der Waals heterostructures. Nat Mater 2016;16:171–81. Google Scholar
Konstantatos G, Levina L, Fischer A, Sargent EH. Engineering the temporal response of photoconductive photodetectors via selective introduction of surface trap states. Nano Lett 2008;8:1446–50. PubMedCrossrefGoogle Scholar
Adinolfi V, Kramer IJ, Labelle AJ, Sutherland BR, Hoogland S, Sargent EH. Photojunction field-effect transistor based on a colloidal quantum dot absorber channel layer. ACS Nano 2015;9:356–62. CrossrefPubMedGoogle Scholar
Clifford JP, Konstantatos G, Johnston KW, Hoogland S, Levina L, Sargent EH. Fast, sensitive and spectrally tuneable colloidal-quantum-dot photodetectors. Nat Nanotechnol 2009;4:40–4. CrossrefPubMedGoogle Scholar
Klem EJD, Gregory C, Temple D, Lewis J. Colloidal quantum dot Vis-SWIR imaging: demonstration of a focal plane array and camera prototype (Presentation Recording). Proc SPIE 2015;9555:955505. CrossrefGoogle Scholar
Macleod HA. Thin-film optical filters. Bristol, Institute of Physics Publishing, 2001. Google Scholar
Landau LD, Lifshitz EM. Electrodynamics of continuous media. Oxford: Pergamon Press, 1984. Google Scholar
Tan CL, Jang SJ, Lee YT. Localized surface plasmon resonance with broadband ultralow reflectivity from metal nanoparticles on glass and silicon subwavelength structures. Opt Express 2012;20:17448–55. CrossrefPubMedGoogle Scholar
Zhu J, Yu Z, Burkhard GF, et al. Optical absorption enhancement in amorphous silicon nanowire and nanocone array. Nano Lett 2008;9:279–82. Google Scholar
Douglas SH, Bruce MD. Design, fabrication, and measured performance of anti-reflecting surface textures in infrared transmitting materials. Proc SPIE 5786, Window and Dome Technologies and Materials IX, 2005:349. Google Scholar
Katiyar AK, Mukherjee S, Zeeshan M, Ray SK, Raychaudhuri AK. Enhancement of efficiency of a solar cell fabricated on black Si made by inductively coupled plasma-reactive ion etching process: a case study of a n-CdS/p-Si heterojunction cell. ACS Appl Mater Interfaces 2015;7:23445–53. CrossrefGoogle Scholar
Ünlü MS, Onat BM, Leblebici Y. Transient simulation of heterojunction photodiodes-part II: analysis of resonant cavity enhanced photodetectors. Lightwave Technol J 1995;13:406–15. CrossrefGoogle Scholar
Gkkavas M, Dosunmu O, Ünlü MS, et al. High-speed high-efficiency large-area resonant cavity enhanced p-i-n for multimode fiber communications. IEEE Photon Technol Lett 2001;13:1349–51. CrossrefGoogle Scholar
Steveler E, Verdun M, Portier B, et al. Optical index measurement of InAs/GaSb type-II superlattice for mid-infrared photodetection at cryogenic temperatures. Appl Phys Lett 2014;105:141103. CrossrefGoogle Scholar
Wang CC, Lin SD. Resonant cavity-enhanced quantum-dot infrared photodetectors with sub-wavelength grating mirror. J Appl Phys 2013;113:21. Google Scholar
Jakšić Z, Djurić Z. Cavity enhancement of Auger-suppressed detectors: a way to background-limited room-temperature operation in 3–14 μm range. IEEE J Sel Top Quant Electr 2004;10:771–6. CrossrefGoogle Scholar
Katsidis CC, Siapkas DI. General transfer-matrix method for optical multilayer systems with coherent, partially coherent, and incoherent interference. Appl Opt 2002;41:3978–87. PubMedCrossrefGoogle Scholar
Derkacs D, Lim S, Matheu P, Mar W, Yu E. Improved performance of amorphous silicon solar cells via scattering from surface plasmon polaritons in nearby metallic nanoparticles. Appl Phys Lett 2006;89:093103. CrossrefGoogle Scholar
Quinten M. Optical properties of nanoparticle systems: Mie and beyond. Weinheim, Wiley-VCH, 2011. Google Scholar
Schuck PJ, Fromm DP, Sundaramurthy A, Kino GS, Moerner WE. Improving the mismatch between light and nanoscale objects with gold bowtie nanoantennas. Phys Rev Lett 2005;94:017402. PubMedCrossrefGoogle Scholar
Ren FF, Ang KW, Ye J, Yu M, Lo GQ, Kwong DL. Split bull’s eye shaped aluminum antenna for plasmon-enhanced nanometer scale germanium photodetector. Nano Lett 2011;11:1289–93. PubMedCrossrefGoogle Scholar
Cai W, Shalaev V. Optical metamaterials: fundamentals and applications. Dordrecht, Springer, 2009. Google Scholar
Ramakrishna SA, Grzegorczyk TM. Physics and applications of negative refractive index materials. Bellingham, WA, SPIE Press and Boca Raton, FL, CRC Press, Taylor & Francis Group, 2009. Google Scholar
Tang J, Xiao Z, Xu K. Broadband ultrathin absorber and sensing application based on hybrid materials in infrared region. Plasmonics 2016;49:1–8. Google Scholar
Xu F, Fujimura K. Pedestrian detection and tracking with night vision. Proc IEEE Intelligent Vehicles Symposium 2002, Paris, France, 2002. Google Scholar
Deng ZS, Liu J. Enhancement of thermal diagnostics on tumors underneath the skin by induced evaporation. Proc. 27th Annual Conference of IEEE Engineering in Medicine and Biology, Shanghai, China, 2005. Google Scholar
Ghafarpour A, Zare I, Ghayoumi ZH, Haddadnia J. A review of the dedicated studies to breast cancer diagnosis by thermal imaging in the fields of medical and artificial intelligence sciences. Biomed Res 2016;27:543–52. Google Scholar
Turco RP. Earth under siege: from air pollution to global change, 2nd ed. New York, Oxford University Press, 2002. Google Scholar
About the article
Published Online: 2017-10-25
Published in Print: 2018-01-01
Citation Information: Nanophotonics, Volume 7, Issue 1, Pages 169–197, ISSN (Online) 2192-8614, DOI: https://doi.org/10.1515/nanoph-2017-0061.
©2017 Hooman Mohseni et al., published by De Gruyter, Berlin/Boston. This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License. BY-NC-ND 3.0