TiO2/SiO2 multilayer as an antireflective and protective coating deposited by microwave assisted magnetron sputtering

  • M. Mazur EMAIL logo , D. Wojcieszak , J. Domaradzki , D. Kaczmarek , S. Song and F. Placido
From the journal Opto-Electronics Review

Abstract

In this paper designing, preparation and characterization of multifunctional coatings based on TiO2/SiO2 has been described. TiO2 was used as a high index material, whereas SiO2 was used as a low index material. Multilayers were deposited on microscope slide substrates by microwave assisted reactive magnetron sputtering process. Multilayer design was optimized for residual reflection of about 3% in visible spectrum (450–800 nm). As a top layer, TiO2 with a fixed thickness of 10 nm as a protective film was deposited. Based on transmittance and reflectance spectra, refractive indexes of TiO2 and SiO2 single layers were calculated. Ultra high vacuum atomic force microscope was used to characterize the surface properties of TiO2/SiO2 multilayer. Surface morphology revealed densely packed structure with grains of about 30 nm in size. Prepared samples were also investigated by nanoindentation to evaluate their protective performance against external hazards. Therefore, the hardness of the thin films was measured and it was equal to 9.34 GPa. Additionally, contact angle of prepared coatings has been measured to assess the wetting properties of the multilayer surface.

[1] M. Giotia, S. Logothetidis, C. Charitidis, Y. Panayiotatos, and I. Varsano, “On the properties and functionality of ultra-thin diamond related protective coatings used in optical systems”, Sensor Actuat. A-Phys 99, 35–40 (2002). http://dx.doi.org/10.1016/S0924-4247(01)00887-110.1016/S0924-4247(01)00887-1Search in Google Scholar

[2] M. Asghar, M. Shoaib, F. Placido, and S. Naseem, “Wide bandpass optical filters with TiO2 and Ta2O5”, Cent. Eur. J. Phys. 6, 853–863 (2008). http://dx.doi.org/10.2478/s11534-008-0104-310.2478/s11534-008-0104-3Search in Google Scholar

[3] J. Han, Y. Dou, M. Wei, D. G. Evans, and X. Duan, “Antireflection/antifogging coatings based on nanoporous films derived from layered double hydroxide”, Chem. Eng. J. 169, 371–378 (2011). http://dx.doi.org/10.1016/j.cej.2011.02.07010.1016/j.cej.2011.02.070Search in Google Scholar

[4] S.Y. Lien, D.S. Wuu, W.C. Yeh, and J.C. Liu, “Tri-layer antireflection coatings (SiO2/SiO2-TiO2/TiO2) for silicon solar cells using a sol-gel technique”, Sol. Energ. Mat. Sol. C90, 2710–2719 (2006). http://dx.doi.org/10.1016/j.solmat.2006.04.00110.1016/j.solmat.2006.04.001Search in Google Scholar

[5] N.Y. Kim, Y.B. Son, J.H. Oh, C.K. Hwangbo, and M.C. Park, “TiN layer as an antireflection and antistatic coating for display”, Surf. Coat. Tech. 128–129, 156–160 (2000). http://dx.doi.org/10.1016/S0257-8972(00)00574-010.1016/S0257-8972(00)00574-0Search in Google Scholar

[6] C. Martinet, V. Paillard, A. Gagnaire, and J. Joseph, “Deposition of SiO2 and TiO2 thin films by plasma enhanced chemical vapour deposition for antireflection coating”, J. Non-Cryst. Solids 216, 77–82 (1997). http://dx.doi.org/10.1016/S0022-3093(97)00175-010.1016/S0022-3093(97)00175-0Search in Google Scholar

[7] M.H. Asghar, F. Placido, and S. Naseem, “Reactively evaporated multilayer antireflection coatings for Ge optical window”, J. Phys. D — Appl. Phys. 40, 2065–2070 (2007). http://dx.doi.org/10.1088/0022-3727/40/7/03110.1088/0022-3727/40/7/031Search in Google Scholar

[8] M.H. Asghar, F. Placido, and S. Naseem, “Characterization of reactively evaporated TiO2 thin films as high and medium index layers for optical applications”, Eur. Phys. J. Appl. Phys. 35, 177–184 (2006). http://dx.doi.org/10.1051/epjap:200608710.1051/epjap:2006087Search in Google Scholar

[9] A. Rothschild, F. Edelman, Y. Komem, and F. Cosandey, “Sensing behaviour of TiO2 thin films exposed to air at low temperatures”, Sensor. Actuat. B-Chem. 67, 282–289 (2000). http://dx.doi.org/10.1016/S0925-4005(00)00523-210.1016/S0925-4005(00)00523-2Search in Google Scholar

[10] S. Boyadzhiev, V. Georgieval, and M. Rassovska, “Characterization of reactive sputtered TiO2 thin films for gas sensor applications”, J. Phys. Conf. Ser. 253, 012040 (2010). http://dx.doi.org/10.1088/1742-6596/253/1/01204010.1088/1742-6596/253/1/012040Search in Google Scholar

[11] M. Kaito, Y. Oshima, and K. Uraba, “Preparation and electrochromism of RF-sputtered TiO2 films”, Jpn. J. App. Phys. 36, 4423 (1997). http://dx.doi.org/10.1143/JJAP.36.442310.1143/JJAP.36.4423Search in Google Scholar

[12] M. Qi, K. Itoh, M. Murabayash, and C.R. Lavers, “Characterization and application of a channel-planar composite waveguide”, Opt. Lett. 25, 1427–1429 (2000). http://dx.doi.org/10.1364/OL.25.00142710.1364/OL.25.001427Search in Google Scholar PubMed

[13] L.J. Meng and F. Placido, “Annealing effect on ITO thin films prepared by microwave-enhanced dc reactive magnetron sputtering for telecommunication applications”, Surf. Coat. Tech. 166, 44–50 (2003). http://dx.doi.org/10.1016/S0257-8972(02)00767-310.1016/S0257-8972(02)00767-3Search in Google Scholar

[14] I. Horcas, R. Fernandez, J.M. Gomez-Rodriguez, J. Colchero, J. Gomez-Herrero, and A.M. Baro, “WSXM: A soft-ware for scanning probe microscopy and a tool for nanotechnology”, Rev. Sci. Instrum. 78, 013705 (2007). http://dx.doi.org/10.1063/1.243241010.1063/1.2432410Search in Google Scholar PubMed

[15] D.Y. Kwok and A.W. Neumann, “Contact angle measurement and contact angle interpretation”, Adv. Colloid. Interfac. 81, 167–249 (1999). http://dx.doi.org/10.1016/S0001-8686(98)00087-610.1016/S0001-8686(98)00087-6Search in Google Scholar

[16] W.C. Oliver and G.M. Pharr, “A new improved technique for determining hardness and elastic modulus using load and sensing indentation experiments”, J. Mater. Res. 7, 1564–1582 (1992). http://dx.doi.org/10.1557/JMR.1992.156410.1557/JMR.1992.1564Search in Google Scholar

[17] M.F. Doerner and W.D. Nix, “A method for interpreting the data depth-sensing indentation instruments”, J. Mater. Res. 1, 601–609 (1986). http://dx.doi.org/10.1557/JMR.1986.060110.1557/JMR.1986.0601Search in Google Scholar

[18] U. Beck, D.T. Smith, G. Reiners, and S.J. Dapkunas, “Mechanical properties of SiO2 and Si3N4 coatings: a BAM/NIST co-operative project”, Thin Solid Films 332, 164–171 (1998). http://dx.doi.org/10.1016/S0040-6090(98)00989-410.1016/S0040-6090(98)00989-4Search in Google Scholar

[19] S. Mathur and P. Kuhn, “CVD of titanium oxide coatings: Comparative evaluation of thermal and plasma assisted processes”, Surf. Coat. Tech. 201, 807–814 (2006). http://dx.doi.org/10.1016/j.surfcoat.2005.12.03910.1016/j.surfcoat.2005.12.039Search in Google Scholar

[20] M.D. Michel, A. Mikowski, C.M. Lepienski, C.E. Foerster, and F.C. Serbena, “High temperature microhardness of soda—lime glass”, J. Non-Cryst. Solids 348, 131–138 (2004). http://dx.doi.org/10.1016/j.jnoncrysol.2004.08.13810.1016/j.jnoncrysol.2004.08.138Search in Google Scholar

[21] E. Sharfrin and W.A. Zisman, “Constitutive relations in the wetting of low energy surfaces and the theory of the retraction method of preparing monolayers”, J. Phys. Chem. 64, 519–524 (1960). http://dx.doi.org/10.1021/j100834a00210.1021/j100834a002Search in Google Scholar

Published Online: 2013-3-15
Published in Print: 2013-6-1

© 2013 SEP, Warsaw

This work is licensed under the Creative Commons Attribution-NonCommercial-NoDerivatives 3.0 License.

Downloaded on 29.3.2024 from https://www.degruyter.com/document/doi/10.2478/s11772-013-0085-7/html
Scroll to top button