Delamination of impacted composite structures by cohesive zone interface elements and tiebreak contact


Maximising impact protection of fibre reinforced plastic (FRP) laminated composite structures and predicting and preventing the negative effects of impact on these structures are paramount design criteria for ground and space vehicles. In this paper the low velocity impact response of these structures will be investigated. The current work is based on the application of explicit finite element software for modelling the behaviour of laminated composite plates under low velocity impact loading and it explores the impact, post impact and failure of these structures. Three models, namely thick shell elements with cohesive interface, solid elements with cohesive interface, and thin shell elements with tiebreak contact, were all developed in the explicit nonlinear finite element code LS-DYNA. The FEA results in terms of force and energy are validated with experimental studies in the literature. The numerical results are utilized in providing guidelines for modelling and impact simulation of FRP laminated composites, and recommendations are provided in terms of modelling and simulation parameters such as element size, number of shell sub-laminates, and contact stiffness scale factors.

If the inline PDF is not rendering correctly, you can download the PDF file here.

  • [1] Hadavinia H., Dogan F, Elmarakbi A., Khalili M., Modelling of low velocity impact of laminated composite substructures. International Journal of Vehicle Structures and Systems, 2011, 3(2), 96–106

  • [2] Lau S.T.W., Said M.R., Yaako M.Y., On the effect of geometrical designs and failure modes in composite axial crushing: A literature review, Composite Structures, 2012, 94, 803–812

  • [3] England J., Hadavinia H., Marchant D.R., Aboutorabi A., Design of Automotive Metal and Composite Chassis Structures, Recent Patents on Mechanical Engineering, Bentham Science, 2010, 3(3), pp. 211–225

  • [4] Dehkordi M.T., Nosraty H., Shokrieh M.M., Minak G., Ghelli D., Low velocity impact properties of intra-ply hybrid composites based on basalt and nylon woven fabrics, Materials & Design. 2010; 31(8), 3835–3844.

  • [5] Heimbs S., Heller S., Middendorf P., Hähnel F., Weiße J., Low velocity impact on CFRP plates with compressive preload: Test and modelling., International Journal of Impact Engineering, 2009, 36(10–11), 1182–1193

  • [6] Chang F.-K., Chang K.-Y., A progressive damage model for laminated composites containing stress concentrations. J. Compos. Mater. 1987, 21, 834–855

  • [7] Choi H.Y., Wu H.-Y.T.. Chang F.K., A new approach toward understanding damage mechanisms and mechanics of laminated composites due to low-velocity impact: Part II-Analysis, J. Compos. Mater. 1991, 25, 1012–1038

  • [8] Choi H.-Y., Wang H.S., Chang F.-K., Effect of laminate configuration and impactor’s mass on the initial impact damage of graphite/epoxy composite plates due to line loading impact, J. Compos. Mater. 1992, 26(6), 804–827

  • [9] LS-DYNA Theory Manual, Livermore Software Technology Corporation, California, USA, LS-DYNA 971 R6; 2006

  • [10] Hellen T.K., On the method of the virtual crack extension, Int. J. Numer. Meth. Eng., 1975, 9:187–207

  • [11] Rice J.R., A path independent integral and the approximate analysis of strain concentration by notches and cracks, J. Appl. Mech., 1968, 35:379–386

  • [12] Rybicki E.F., Kanninen M.F., A finite element calculation of stress intensity factors by a modified crack closure integral, Eng. Fract. Mech., 1977, 9:931–938

  • [13] Raju I.S., Calculation of strain-energy release rates with higher order and singular finite elements, Eng. Fract. Mech., 1987, 28(3), 251–274

  • [14] Parks D.M., A stiffness derivative finite element technique for determination of crack tip stress intensity factors, Int. J. Fract., 1974, 10(4), 487–502

  • [15] Griffith A.A., The phenomena of rupture and flow in solids. Philosophical Transactions of the Royal Society, London; Series A, 1921, 221, 163–198

  • [16] Gordnian K., Hadavinia H., Mason P.J., Madenci E., Determination of fracture energy and cohesive strength in Mode I delamination of angle-ply laminated composites, Compos. Struct., Vol. 82(4), 577–586, 2008

  • [17] Hillerborg A., Modeer M., Peterson P.E., Analysis of crack formation and growth in concrete by means of fracture mechanics and finite elements, Cement Concr. Res., 1976, 6, 773–782

  • [18] Needleman A., A continuum model for void nucleation by inclusion debonding, J. Appl. Mech., 1987, 54, 525–531

  • [19] Tvergaard V., Hutchinson J.W., The relation between crack growth resistance and fracture process parameters in elastic-plastic solids, J. Mech. Phys. Solid, 1992, 40, 1377–1397

  • [20] Tvergaard V., Hutchinson J.W., The influence of plasticity on mixed mode interface toughness, J. Mech. Phys. Solid, 1993, 41, 1119–1135

  • [21] Hutchinson J.W., Linking scale in fracture mechanics. In: Proceedings of the 9th International Conference on Fracture (ICF9), Sydney, 1–5 April 1997, 1–14

  • [22] Camacho G.T., Ortiz M., Computational modeling of impact damage in brittle materials, Int. J. Solid. Struct., 1996, 33, 2899–2938

  • [23] Mi Y., Crisfield M.A., Davies G.A.O., Hellweg H.B., Progressive delamination using interface elements, J. Compos. Mater., 1998, 32(14), 1246–1272

  • [24] Hillerborg A., Application of fictitious crack model to different types of materials, Int. J. Fract., 1991, 51, 95–102

  • [25] Dugdale D.S., Yielding of steel sheets containing slits, J. Appl. Mech., 1960, 8, 100–104

  • [26] Williams J.G., Hadavinia H., Analytical solution of cohesive zone models, J. Mech. Phys. Solid., 2002, 809–825

  • [27] Chen J., Crisfield M., Kinloch A.J., Busso E.P., et al., Predicting progressive delamination of composite materials specimens via interface elements, Mech. Compos. Mater. Struct., 1999, 6, 1–17

  • [28] Blackman B.R.K., Hadavinia H., Kinloch A.J., Williams J.G., The use of cohesive zone model to study the fracture of fibre composites and adhesively-bonded joints, Int. J. Fract., 2003, 119(1), 25–46

  • [29] Elmarakbi A.M., Hu N., Fukunaga H., Finite element simulation of delamination growth in composite materials using LS-DYNA, Compos. Sci. Tech., 2009, 69(14), 2383–2391

  • [30] Barenblatt G.I., The formation of equilibrium cracks during brittle fracture. General ideas and hypotheses: axially-symmetric cracks, J. Appl. Math. Mech. (PMM), 23, 434–444, 1959

  • [31] Rice J.R., Wang J-S., Embrittlement of interfaces by solute segregation, Mat. Sci. Eng. A, 1989, 107, 23–40

  • [32] Xu X.P., Needleman A., Numerical simulation of fast crack growth in brittle solids, J. Mech. Phys. Solid., 1994, 42, 1397–1434

  • [33] Geubelle P.H., Baylor J., Impact-induced delamination of laminated composites: a 2D simulation, Compos. B Eng., 1998, 29, 589–602

  • [34] Pandya K., Williams J.G., Measurement of cohesive zone parameters in tough polyethylene, Polymer Engineering and Science, 2000, 40(8), 1765–1776

  • [35] Mohammed I., Leichti K.M., Cohesive zone modelling of crack nucleation at bimaterial corners, J. Mech. Phys. Solid., 2000, 48, 735–764

  • [36] Hughes T.J.R., Taylor R.L., Sackman J.L., Curnier A.C., et al., A Finite Element Method for a Class of Contact-Impact Problems, 1976

  • [37] Belytschko T., Yeh I. S., The splitting pinball method for contact-impact problems, Comput. Meth. Appl. Mech. Eng., 1993, 105(3), 375–393

  • [38] Burton D.E., Physics and Numerics of the TENSOR Code, Lawrence Livermore National Laboratory, Internal Document, UCID-19428, 1982

  • [39] Wilkins M. L., Calculations of Elastic-Plastic Flow, 1964


Journal + Issues

Open Engineering publishes research results of wide interest in emerging interdisciplinary and traditional engineering fields, including: electrical and computer engineering, civil and environmental engineering, mechanical and aerospace engineering, material science and engineering.