Miniaturization of electronic and opto-electronic semiconductor devices has been happening ever since the first such devices appeared. Eventually, one can envision a device that is composed of just a few atoms. As these atoms ideally should not float in free space, but should be embedded in a solid-state matrix, this naturally brings one to the concept of a point defect (an impurity atom or complex of atoms) as the ultimate electronic or opto-electronic device. At such tiny length scales the behavior of physical systems is governed by the laws of quantum mechanics. Therefore, it is no surprise that an increasing number of point defects are being considered as building blocks for various applications in the field of quantum information science; more specifically, in quantum sensing, quantum communication, and quantum computing , , , . We refer to these desirable defects as quantum point defects (QPDs). Prominent examples include the nitrogen-vacancy (NV) center in diamond, the silicon-vacancy (SiV) center in diamond, the divacancy in silicon carbide, and rare-earth impurities in complex oxides; see Figure 1.
The number of possible QPDs is extremely large, and each defect system has its own unique set of properties. Some properties arise directly from the defect’s chemical structure, whereas others stem from characteristics of its host material; together, these properties determine a defect’s quantum functionality. Despite continued advances in theoretical understanding, accurate first-principles calculations, and experimental capabilities, an exhaustive search remains impractical. Therefore, a deep understanding of these property-function relationships is essential to developing efficient, heuristic screening criteria that guide exploration through a large materials parameter space.
The purpose of this article is to contemplate this challenge in the context of current experimental and theoretical capabilities. It is organized as follows. After reviewing the current role of defects in quantum science and technology in Section 2, we highlight the potential for identifying QPDs in new materials systems and present a vision for application-driven discovery in Section 3. As a counterpoint to this vision, Section 4 features a brief historical overview of a prototypical QPD – the diamond NV center – highlighting how new applications continue to emerge from investigations of the defect’s fundamental properties. This historical perspective acknowledges the role of serendipity in scientific discovery. Ultimately, we hope that a design-driven approach can supplement the traditional modes of investigation. Towards that end, we reflect on the opportunities for exploration of new materials systems in Section 5, and review the main criteria one must consider in designing quantum defects. Finally, Section 6 discusses several key challenges in theoretical prediction, materials synthesis, and experimental characterization. We highlight promising new directions in these domains and consider what is needed to achieve the goal of quantum defects by design.
2 Why defects?
Defects are ubiquitous in all materials. They can dramatically modify a material’s electrical, optical, and mechanical properties, enabling widely tunable responses and new functionality (e.g. for transistors and lasers). At concentrations where defects do not interact with one another, they are analogous to trapped atoms or molecules, with individual electronic states isolated within the host material’s band gap – the semiconductor vacuum  – with orbital and spin degrees of freedom that can be controlled using electromagnetic fields.
Especially in wide-bandgap materials, where deep defect levels are characterized by tightly bound electronic wavefunctions, a defect’s electronic structure is determined by its symmetry and chemical composition in direct analogy to individual molecules. Indeed, molecular orbital theory is the prevailing tool to achieve qualitative – and sometimes quantitative – understanding of a defect’s electronic structure and optical dynamics , .
In certain configurations, the orbital or spin degrees of freedom of electrons and nuclei associated with a defect are sufficiently isolated from environmental perturbations (including thermal phonons, electromagnetic noise, free carriers, and other defects in the material) that quantum-mechanical superpositions of these states can be prepared and maintained for periods of time that enable their practical use for quantum information science. The prototypical and most well-studied QPD is the diamond NV center (Figure 1A), whose electronic spin state can be initialized, controlled, and read out at room temperature using optical pumping, microwave spin resonance, and photoluminescence, respectively . The sensitivity of these spins to local fields (e.g. electric, magnetic, thermal, and strain) and the ability to embed the defects in nanostructures facilitate revolutionary modalities of nanoscale sensing for physics , , , , chemistry , , , and biology , . Each NV center also constitutes a quantum register of electron and nuclear spins that can be individually controlled , , , entangled , , stored coherently for several seconds , , and used to perform quantum operations including teleportation  and error correction , , . At liquid helium temperatures, NV-center electronic spins couple coherently to light , , , , and they can be remotely entangled through photonic channels , , , forming the basis for distributed quantum networks , .
However, the diamond NV center is by no means unique nor the optimal QPD for many situations. Spurred by the potential to identify other spin qubits with improved properties and new functionalities, exploration of semiconductor defects has grown rapidly in recent years to include additional systems in diamond , , , , , ,  (see Figure 1B) and SiC , ,  (see Figure 1C), rare-earth ions in oxide crystals , , ,  (see Figure 1D), as well as wide-bandgap group II–VI and III–V materials such as ZnO , ,  and GaN , , , and low-dimensional van der Waals materials such as the transition metal dichalcogenide (TMD) WSe2 , , , ,  and hexagonal boron nitride (hBN) , , , , . A theoretical understanding of many of these systems is still lacking, and in some cases even the defect’s chemical structure remains unknown. Nonetheless, they offer potential advantages over NV centers including optical indistinguishability , , high brightness , , improved performance in nanophotonic devices , , and incorporation in a more technologically mature semiconductor host .
3 Defects by design
Historically, the discovery and development of semiconductor defects – either as spin qubits or for other purposes – has been a sequential process focused on the specific properties of individual materials. Experimental observation of a new phenomenon, such as a prominent spectral line or a strong magneto-optical response, motivated the construction of theoretical models and numerical calculations to establish the electronic structure. This, in turn, motivated the identification and development of potential applications. The throughput of this sequential approach is fundamentally limited, because it is impractical to experimentally measure or computationally model all possible defects in one material host, let alone in all possible hosts.
Ultimately, it would be desirable to complement this historical approach with an inverted discovery paradigm, as shown in Figure 2. Beginning with scientific or application goals, one would assess the relevant requirements and figures of merit, demarcate a range of crystal hosts and defects that should exhibit the required properties, screen the candidates, and only then initiate targeted research to engineer the materials and refine experimental techniques. Lessons can be drawn from past research that concentrated on the properties of individual defects, but addressing this challenge requires considerations of broader questions including: What is the ideal QPD electronic structure for a particular application? What defects within which crystal hosts would exhibit the required properties? Which systems from the selected hosts are most feasible from the experimental and engineering standpoint? In addition to electronic structure, how precisely can we predict complex QPD properties such as optical lineshapes, quantum efficiency, spin coherence, and fidelities for initialization and readout?
Given the complex interdependence of host material characteristics, defect properties, and quantum functionality (see Section 5), it is unlikely that we will converge on a single “best” QPD; more likely, development of new QPDs will yield varied systems that are optimized for particular applications. The rich history of the diamond NV center’s development as a platform for quantum science (see Section 4) provides abundant examples of unanticipated applications that emerged from fundamental investigations, so one can reasonably anticipate that many new applications will similarly sprout from research on QPD systems with different properties. In this way, as with any research endeavor, the actual progression of QPD knowledge will always be a combination of the serendipitous historical approach and the systematic design paradigm illustrated in Figure 2. Nonetheless, with continued progress in computational models that enable quantitative theoretical prediction of QPD properties, as well as efficient experimental techniques for synthesis and screening of QPD candidates, it should be possible to significantly accelerate the discovery process.
4 A brief history of the NV center, a prototypical QPD
Here, we take a short historical tour to illustrate the interplay between our physical understanding of a quantum defect, the drive toward a given quantum technology, and materials advancements in the field of QPDs. We utilize the negatively-charged NV center in diamond, already introduced, but note that parallel histories could be constructed for other quantum defects. For example, the QPD timeline for phosphorous donors in silicon  could start from the Kane proposal for a silicon quantum computer , while a timeline for rare-earth doped crystals ,  could start from the first demonstration of electromagnetically-induced transparency . Fantastic in-depth reviews on the fundamental properties ,  and applications , , ,  of NV centers already exist in the literature. Here we focus on a few key, enabling discoveries.
The turning point, which eventually led to the realization of the NV center as a QPD, was the optical detection of single centers via confocal microscopy of a bulk diamond sample by Gruber et al. in 1997 . In contrast to various reports today of QPDs of as yet unknown origin , , , , , , , Gruber et al. purposefully synthesized a previously identified defect at concentrations low enough for single center isolation. NV-center formation was reported as early as 1965 , with the atomic structure of the defect confirmed by the 1970s . Optical spin polarization (or optical pumping) was reported in electron-spin-resonance measurements in 1977  and optically-detected magnetic resonance (ODMR), a key spectroscopic technique to access spin dynamics, had been reported at low temperature for NV-center ensembles in 1990 . Thus, in some sense, the stage was set for rapid development with respect to quantum technologies once single-center isolation was achieved. In fact, in the first demonstration of single-NV-center isolation, Gruber et al. also demonstrated single-center ODMR at room temperature. The application of NV centers in quantum technology was not yet on the radar. The main motivation for Gruber et al. was to allow “detailed material characterization at a local level that is otherwise masked by ensemble averaging” .
Within several years of Gruber et al.’s seminal work, the utilization of the NV center as a single-photon source had been demonstrated , , again with synthesized centers. The next major developments were single electron spin control , single nuclear spin control, and spin-spin quantum gates , all enabled by optical pumping and ODMR techniques developed a decade earlier. Yet quantum coherence times were short, limited by the high nitrogen content of the type Ib synthetic diamond. The use of NV centers unintentionally incorporated in type IIa natural diamond enabled long room-temperature coherence times, elucidating the rich dynamics between the NV electronic spin and the nuclear spin bath , which further enabled multi-qubit registers , . The combination of spin control and long room-temperature spin coherence led to theoretical proposals to utilize the NV center as a nanoscale magnetic sensor in 2008 , , followed almost immediately by experimental demonstrations , .
A proliferation of NV-center-based research over the next decade in both quantum information and quantum sensing can be attributed to the combination of these seminal demonstrations and the commercial availability of “electronic grade” diamond , , with nitrogen concentration of less than 1 part per billion (ppb), from the company Element Six around 2007. These high-purity diamond substrates host unintentionally-incorporated NV centers with quantum properties on par with the best natural diamond samples  and at concentrations suitable for single NV-center isolation using basic confocal microscopy. Additionally, electronic-grade substrates facilitated experiments to improve the quantum properties of single, near-surface NV centers formed via N+ ion implantation , , .
As key technologies, such as single-shot single-spin readout , remote spin-spin entanglement , , and single protein magnetic resonance spectroscopy ,  were demonstrated, the limitations of the NV center for each particular application became more apparent. These limitations motivated further research and discovery in the fundamental understanding of the specific physics that limits the NV center’s performance in order to engineer methods to overcome the limitation. We next use the specific example of the NV center’s inter-system crossing (ISC) and its role in spin readout to illustrate this process.
High-performance spin readout  is essential for spin-based quantum information protocols and for high-sensitivity sensing. The NV center’s spin-dependent ISC enables room-temperature single-spin detection via photoluminescence intensity. However, whereas high-fidelity readout can be achieved at cryogenic temperatures using resonant optical pumping , the transience and low contrast of the ISC-mediated spin-dependent photoluminescence has prevented single-shot spin measurement at room temperature. This limitation, as well as the need to understand the fundamentals of NV centers, motivated the development of the theory (including ab initio theory) for the radiative and non-radiative transition rates , , . It also motivated the development of an alternative method for spin read-out: high-fidelity charge state readout  and spin-to-charge conversion , . This second approach can improve the experimental signal-to-noise ratio for single-shot spin readout by over an order of magnitude . The development of spin-to-charge conversion further motivated theoretical work on the photoionization properties of the NV center . Finally, the relatively low speed and high complexity of optical readout, requiring optics and detectors to collect single photons, combined with advances in photoionization theory, has led to the demonstration of photoelectrically-detected magnetic resonance (PDMR) , , including recently of single spins .
The connection between a physical property of a QPD (in this case the ISC), the physics behind the property, the challenges it presents, and the opportunities it enables (e.g. with respect to mitigating the challenges and enabling new applications), can be made again and again for different properties. Several examples of this rich interplay for the NV center are given in Table 1. While performance in NV-center-based applications continues to increase, performance is alternatively limited or facilitated by the defect’s basic properties. Starting with defects with different properties will drastically increase the quantum-enabled application space. We thus need an efficient way to find these defects.
Connections between the physical properties of a defect, in this case the NV center, and potential applications.
|Inter-system crossing (ISC) , ||Spin-orbit coupling, phonon interactions, excited state structure||Spin-readout SNR||Alternative readout strategies||Optical readout |
|Ground-state response to local fields , ||Ground-state electronic structure||Inhomogeneous broadening, sensor stability||Double quantum magnetometry, active control||Sensors |
|Phonon-assisted/phonon-broadened transitions , ||Excited-state structure, Jahn-Teller interactions||Photon indistinguishability, ZPL efficiency||Photonic cavities||Off-resonant spin readout , thermometry |
|13C nuclear bath ||Central spin model, non-Markohvian dynamics||Spin decoherence||Isotope purification dynamic decoupling||Qubit registers , |
|Multiple charge states ||Charge capture, nonlinear and non-equilibrium effects||Stabilization of desired charge state||Optical charge control Fermi-level control||Enhanced readout schemes , free carrier spin bus |
5 Opportunities in a complex parameter space
In expanding the QPD parameter space beyond traditional hosts, such as group IV materials, it is crucial to realize that each potential application poses a unique set of requirements on QPD functionality, which are in turn related in complex ways to the structural and functional properties of the defect and its host. The interconnected network of property-function relationships is qualitatively depicted in Figure 3, where lines indicate connections that are important for determining particular properties or functionality of QPDs, and the size of each circle is proportional to the number of connections it involves. The diagram is far from exhaustive and does not capture information regarding the relative importance of different properties; rather, it shows how myriad features collectively give rise to specific quantum functionality. For example, an application for single-photon sources might require bright, high-purity emission in a specific, narrow spectral band with a well-defined optical polarization axis, whereas the main criteria for a quantum sensor is the signal-to-noise ratio for spin readout. In the latter case, the key property is a strong spin-dependent optical signal, and a wider emission bandwidth might actually be preferable in order to simplify isolation of the signal from the excitation background.
Identifying novel QPDs is a combinatorial problem. Even if one considers just three QPD classes – substitutional dopants, native vacancies, and dopant-vacancy complexes – in commercially available wide-bandgap hosts, there are millions of potential host-defect combinations. Clearly, this massive parameter space precludes an exhaustive search by detailed calculations or experimentation.
Systematic discovery of new QPDs thus requires the development of heuristics to efficiently screen this parameter space. Weber et al.  took a key step in this direction, showing how independent consideration of host properties (e.g. band gap, nuclear spin isotopes, and spin-orbit coupling) can guide the identification of QPDs analogous to the diamond NV center. In particular, this analysis elevated the profile of SiC as a QPD host, spurring efforts to identify and control single spins in that material – especially the divacancy and silicon vacancy , , . As in the case of the diamond NV center, key features of the divacancy and silicon-vacancy defects in SiC were already established , , and high-quality substrates were commercially available. For these reasons, and leveraging experience gained from the diamond NV center, SiC QPDs have seen rapid development . Ultimately, it should be possible to extend Weber et al.’s methodology to a higher level of abstraction, combining analytical and computational theory to predict how host symmetry, defect configuration, and chemical composition couple to produce the desired electronic structure for a given application. In the sections that follow, we discuss some general considerations to guide investigations of new materials, especially considering the role of the host material’s dimensionality and symmetry in constraining defect properties.
5.1 Guiding criteria for exploration
Excellent rationale underlies the field’s current emphasis on group IV hosts, and these materials will surely remain prominent as the field expands. Nonetheless, many other materials have properties conducive to hosting QPDs, but are largely unexplored. Whereas group IV materials are mainly available as bulk crystals, many other compound semiconductors are amenable to sophisticated synthesis via molecular beam epitaxy (MBE) or synthetic chemistry and are available in various morphologies such as epitaxial thin films, nanocrystals, and nanowires. Such materials offer potential advantages for applications through their tailored electronic, optical, or chemical properties. Given the large parameter space, however, it is best to proceed beyond group IV systematically with clear goals in mind.
We can lay out several guiding criteria based on basic material properties. The criteria are reminiscent of those articulated by Weber et al. , albeit informed by recent developments in the field and with a somewhat more general context, as we are not only interested in analogs to the diamond NV center. We also emphasize that these are guidelines, not rules; often there are competing effects, and application-specific considerations may lead to choices that violate the criteria.
5.1.1 Band gap
Generally, QPDs feature highly isolated states deep within the semiconductor’s band gap, such that they are spatially confined and energetically isolated from direct interactions with delocalized charge carriers. If a localized optical excited state is also desired within the band gap, e.g. for optical spin initialization or coherent interactions with photons in the visible-to-near-infrared range, then the host material’s band gap should be at least 2 eV. Larger band gaps provide additional room to accommodate multiple charge states or even different defect configurations in order to achieve the desired spin structure. For example, diamond’s large band gap has facilitated exploration of the entire QPD family of group IV-vacancy complexes (SiV, GeV, SnV, PbV), all of which have the structure shown in Figure 1B; these defects have similar electronic structures but differ in their optical transition energies and spin-orbit coupling . Similarly, wide-bandgap hosts of transition-metal and rare-earth ions exhibit defect families associated with impurity atoms from same row of the periodic table, whose spin and optical properties are determined by the electrons in the ion’s d- or f-shell orbitals, respectively.
The choice is not always simple, however. It is difficult to control the Fermi level of wide bandgap materials, and challenging to realize electronically active devices. Indeed, a large band gap is less important for paradigms where optical excitations are not required, e.g. for electrically controlled phosphorus-donor qubits in silicon. Even for optical QPDs, it is not always essential for states to be completely isolated from the band edges. Donor-bound excitons feature optical transitions that are close to the bandgap energy , , and the resulting hybridization with delocalized electron-hole pairs increases the donors’ optical cross section and determines their selection rules.
5.1.2 Nuclear spin bath
Nuclear spins generally remain unpolarized at experimentally accessible temperatures and magnetic fields, and random fluctuations in this bath induce decoherence for QPDs. Nuclear spins are not always detrimental, and in the proper configuration they offer additional quantum degrees of freedom for applications. Nonetheless, it is usually desirable to choose materials with a dilute nuclear bath. Elements in groups II, IV, and VI possess spinless nuclear isotopes, whereas all elements in odd groups exhibit nonzero nuclear spin.
One can assess the natural abundance of spinless isotopes for a quick evaluation of a material’s nuclear spin bath in the absence of isotopic purification, however, the actual effect of this bath on QPD spin coherence is somewhat more difficult to estimate. For example, the isotopic abundance of spinful isotopes in SiC (2.9%) is more than twice that of diamond (1.1%). Nevertheless, divacancies in naturally isotopic SiC exhibit spin coherence times that are comparable to or even longer than those for diamond NV centers . One needs to account for the details of the hyperfine coupling and spin-bath dynamics that cause decoherence; in the case of SiC, a larger lattice spacing and weak coupling between nuclear species with different gyromagnetic ratios in SiC mitigates the effect of a higher spin density compared to diamond , . Furthermore, the application of dynamical decoupling techniques for cancelling low-frequency noise and dynamical nuclear polarization for cooling the spin bath mitigates many of the detrimental effects of nuclear spins ; this can make materials like group III–V semiconductors a viable option, especially to leverage the advanced synthesis and nanofabrication capabilities associated with these materials to realize integrated electronic and photonic devices.
5.1.3 Spin-orbit coupling
The fundamental attraction of spins as qubit degrees of freedom is that they respond mainly to magnetic fields and are relatively immune to environmental noise from fluctuating charges and phonons. Orbital degrees of freedom, by contrast, respond directly to these pervasive sources of noise. Therefore, low spin-orbit coupling is usually desirable in order to achieve long spin coherence times. As spin-orbit coupling generally scales with atomic number Z, this can be accomplished by choosing materials composed of light elements.
Again, however, the choice is not always straightforward. Spin-orbit coupling is the fundamental mechanism responsible for coherent spin-light interactions – it limits the rate at which spins can be controlled using light , , , sets the selection rules for generation of spin-photon entanglement , and underlies the ISC transitions that mediate spin initialization and readout for the diamond NV center ,  and other defects . Spin-orbit coupling further enables control of spins using mechanical waves , , and potentially the use of phonons as a quantum bus between spatially separated spins , , . Moreover, depending on the system and experimental parameters, spin decoherence can be dominated by different effects, including hyperfine coupling to the nuclear spin bath or various spin-lattice relaxation processes , , . Therefore, one should not assume that spin-orbit coupling should always be minimized; rather, it is a crucial tuning parameter that should be carefully considered in the context of a given application. One attractive way to achieve such tuning is to study families of defects with similar electronic structures, composed from impurity atoms drawn from the same group, as for the group IV-vacancy defects in diamond, where the spin-orbit coupling increases for elements of increasing atomic number .
5.1.4 Crystal symmetry
In a first approximation, a defect’s orbital and spin structure derives directly from its spatial symmetry. The point group determines the multiplicity of each level according to molecular orbital theory , . Generally, higher symmetry allows for degenerate orbitals. Degenerate orbital levels are important, since, as per Hund’s rule, they will give rise to high spin states (S>1/2) in the electronic ground state. High spin states are often desirable for QPDs, as they exhibit zero-field splitting parameters in the spin Hamiltonian; this decouples the QPD from background electronic impurities in the material with S=1/2 and allows for coherent spin control even at zero magnetic field. Orbital degeneracies also give rise to various spin-orbit combinations with definite symmetry in the electronic ground or excited state that can produce spin-photon entanglement .
As prototypical defect models, let us consider two types of lattice imperfections. One type is a simple vacancy or a substitutional impurity, whereby only one lattice site is affected (e.g. the Pr defect in YAG, Figure 1D). The other type is a complex between a vacancy and an impurity, two impurities, or a divacancy (Figure 1A–C). In a given material, the point group with the highest symmetry belongs to the first type of defect, whereas the second type transforms according to subgroups with lower symmetry. In some cases, a defect’s symmetry is different than one might naïvely predict due to lattice distortions; for example, the static Jahn-Teller effect generally lowers the symmetry whereas the split-vacancy configuration – where the impurity sits between two vacancies – can have higher symmetry than the traditional vacancy-impurity complex.
Table 2 shows point groups of the two basic types of defects in five different crystal lattices: diamond, zinc-blende, rock-salt (cubic crystal system), hBN, and TMD (hexagonal crystal system). In the case of cubic crystals, the first type of defect has either the Td or Oh symmetry, both of which allow the existence of doubly and triply degenerate single-particle levels. In these materials, defects of the second type have symmetries C3v, D3d, or C4v, all of which similarly allow the existence of doubly degenerate single-particle levels.
Selected properties of two types of defects in various crystals.
|Crystal (space group)||Vacancy/substitutional impurity||Impurity-vacancy complex/divacancy/double substitutional impurity/impurity-split-vacancy complex|
|Point group||Degenerate levels||Point group||Degenerate levels|
|Diamond (Fd3̅m, No. 227)||Td||Yes||C3v D3d (split vacancy)||Yes|
|Zinc-blende (F4̅3m, No. 216)||Td||Yes||C3v||Yes|
|Rock-salt (Fm3̅m, No. 225)||Oh||Yes||C4v||Yes|
|hBN (P63/mmc, No. 194)||D3h||Yes||C2v||No|
|TMDs (P63/mmc, No. 194)||D3h (cation site)|
C3v (anion site)
The situation is different in the case of layered hexagonal materials. Defects of the first type have symmetry D3h (hBN or cation-site defects in TMDs) or C3v (anion-site defects in TMDs), both of which allow for the existence of doubly-degenerate states. However, defects of the second type possess symmetry C2v, which does not have degenerate levels. This makes the occurrence of high spin states in the electronic ground state less likely. When there are no degenerate levels, the condition for the occurrence of high-spin states (e.g. a triplet state) is that the exchange coupling between electrons in different defect states is larger than the single-particle energy splitting between those states. This condition is fulfilled, for example, in the case of a complex between the boron vacancy and substitutional oxygen, VB−ON, in hBN . While this example shows that high spin states are possible, generally they are expected to be less frequent in layered materials like hBN or TMDs.
Overall, this analysis suggests it is preferable to start with a host material with high symmetry, in order to have design flexibility in the defects’ electronic structure. In practice, it is challenging to initialize spin systems with S>1 using optical pumping, as multiple pumping pathways need to be considered. Moreover, for odd-electron systems the spin levels form Kramers doublets characterized by the same irreducible representation, such that one level cannot be selectively populated on the basis of symmetry through ISC dynamics. This implies that orbital doublets with S=1 are generally desirable, as occur for most axially-symmetric systems such as divacancies or vacancy-impurity complexes in cubic binary crystals. However, even if a defect does not have a high spin state in the electronic ground state, it can still have a high spin state in the electronically excited state, as was demonstrated for defects in hBN . This is in complete analogy with closed-shell molecular systems which possess a metastable triplet manifold besides the singlet manifold. Such a configuration can actually be an advantage for quantum sensing applications, as the QPD system can be pumped to the triplet state when sensing of the target is desired, while the nonmagnetic singlet ground-state configuration eliminates back-action at other times.
Depending on the application, inversion symmetry can also be desirable, for both the host crystal and the defect itself. Inversion-symmetric defects cannot feature a permanent electric dipole, which makes them insensitive to external electric fields to leading order, reducing inhomogeneous broadening and spectral diffusion of optical transitions. Similarly, crystals without inversion symmetry are generally piezoelectric, and this introduces additional vibronic couplings between photons and phonons that can broaden the emission lines. Of the crystals listed in Table 2, the diamond and rock-salt structures are inversion symmetric, whereas zinc-blende is not. HBN and TMDs also exhibit inversion symmetry in the bulk limit of many layers, but not as a monolayers. Layered materials derive many of their characteristics from the properties of single sheets, and although this means they have lower symmetry than their three-dimensional counterparts, it also makes them extremely interesting for defect engineering for other reasons, as we discuss next.
5.1.5 Dimensionality and morphology
Low-dimensional materials offer interesting opportunities as well as challenges as hosts of QPDs. By low-dimensional materials, we mean both nanoscale morphologies of three-dimensional crystals, such as nanocrystals (zero-dimensional) or nanowires (one-dimensional), as well as layered van der Waals crystals, such as hBN or TMDs, as mono-to-few-layer systems (two-dimensional).
For deep defects in wide-bandgap materials, the material’s morphology has little effect on the defect’s electronic structure, as even nanostructures with dimensions below 10 nm are generally much larger than the size of the defect’s wavefunction which extends over only a few angstroms. However, semiconductor nanostructures have profound effects on electromagnetic interactions, and they can be integrated with other optical or electronic structures in order to tailor the QPD’s properties or enable new control protocols. One-dimensional nanowires act as natural optical waveguides, directing emission into a well-defined spatial mode. Both nanowires and nanocrystals can be combined with plasmonic or dielectric elements that modify the QPD’s optical absorption or emission properties. Whereas diamond and SiC nanoparticles are typically produced by etching or milling bulk crystals, nanowires and nanocrystals of many group II–VI and III–V semiconductors can be directly synthesized using MBE or colloidal chemistry, which offer improved control over size, shape, and composition. Some materials can also be synthesized as core-shell heterostructures, which offers additional design flexibility in controlling the electronic and optical functionality.
For QPDs in low-dimensional materials, the presence of nearby surfaces or interfaces affects the defect’s spin and charge dynamics. This is often a problem that leads to decoherence if the surface is uncontrolled, as is the case for diamond and SiC. The influence of surfaces is a crucial consideration for nanoscale sensing applications, where the goal is to locate the QPD as near as possible to a target outside the material. It is therefore crucial to understand the surface chemistry and to pursue strategies for effective surface termination or passivation. In contrast to three-dimensional crystals, surfaces of van der Waals-bonded crystals do not have unsaturated dangling bonds. Therefore, at least in principle, their surfaces should contain fewer unpaired spins and charge traps compared to materials with covalent (or partially covalent) bonding. This potentially makes layered materials more suitable as QPD hosts for quantum sensing applications.
Along with their atomic thinness, the unique mechanical, electronic, and optical properties of layered materials offer the potential for dramatic physical effects. In particular, the ability to stack van der Waals materials into heterostructures allows the mixing of dissimilar materials irrespective of lattice matching or other typical requirements of epitaxially-grown heterostructures . QPDs confined to monolayers should be considerably more tunable than in bulk crystals, through the intrinsic tunability of the host two-dimensional crystal and the proximity to other materials. For example, the Fermi level and carrier concentration of two-dimensional materials can be tuned with electrostatic gates to control a QPD’s charge and spin state , and strain tuning can modify the optical emission properties or enable optomechanical coupling , . With a growing library of layered materials that includes conductors, semiconductors, superconductors, topological materials, and magnetic solids, the paradigm of van der Waals heterostructures is a rich landscape for QPD engineering. QPD-based sensors in layered materials will be a powerful tool for studying fundamental physical phenomena. Moreover, proximity-induced quantum mechanical interactions such as exchange and orbital hybridization between adjacent layers could allow for dramatic modification of spin-photon selection rules and the realization of hybrid quantum systems that link localized QPD degrees of freedom using collective quantum states.
5.2 Practical considerations and promising materials
Alongside all these idealized material properties, equally important criteria for choosing a QPD host are the most practical ones: the availability of pure starting material and knowledge of the defect chemistry. The starting material can take different forms, including bulk single crystals, thin films, or nanocrystals, however there should be a pathway towards producing material in the required morphology and purity for relevant applications. A material’s defect chemistry gets more complicated as the number of elements and inequivalent sites increases; for this reason it makes sense to begin with elemental or binary compounds with simple unit cells.
The binary oxide materials MgO and SrO exhibit inversion symmetry and can be synthesized via MBE. ZnO is an attractive material with a moderate band gap and low spin-orbit coupling. Other group II–VI materials like ZnS, ZnSe, CdS, and CdSe are well-known optically active semiconductors and can be chemically synthesized as nanowires or nanocrystals with precisely tailored size, shape, and composition. Despite the lower symmetry of layered van der Waals materials, the potential for cleaner surfaces and novel functionality motivates efforts to identify QPDs in these systems. Certain complex oxides such as YAG and yttrium orthosilicate (YSO) are also attractive hosts, especially to accommodate larger impurities like rare-earth ions. These materials are available as relatively pure bulk crystals through their development for laser crystals, and some (YSO especially) exhibit long spin coherence times due to a dilute nuclear spin environment . Despite an unavoidable nuclear spin bath, wide-bandgap group III–V materials such as GaN and AlN are attractive for their technological sophistication, especially in optoelectronics and electromechanics. Ultimately, more complex materials such as perovskites can also be of interest, since they feature widely tunable electronic, optical, and magnetic properties. Some of these materials can be synthesized with sufficient purity to explore quantum effects . Nevertheless, it remains a major challenge to engineer QPDs in such complex materials, and success likely requires advances in both theory and experiment, as we consider in Section 6.
6 State of the field and challenges
Efficiently predicting, creating, and characterizing new quantum defects will require simultaneous advancements in defect theory, materials and QPD synthesis, and experimental characterization. In this section we summarize the state of the field, highlighting the outstanding challenges in each of the three areas.
We will focus here on ab initio theory, as its predictive power is especially important in the discovery of novel QPDs. This theory is no substitute for the classic theoretical machinery of solid-state physics , , ; rather, it complements analytical theory and allows for the quantitative calculation of parameters that can be used in modeling various phenomena. While in certain situations qualitative understanding of defects is sufficient, a quantitative description is key for applications in quantum technologies. There is substantial difference if a QPD’s quantum efficiency is, e.g. 95% or 5%, or whether the energy of the zero phonon line (ZPL) falls within one of the telecommunications bands or outside them.
The past few decades have seen tremendous progress in the quantitative description of the electronic structure of solids in general, mainly due to developments in the field of density functional theory (DFT) . While DFT is in principle an exact reformulation of the many-body quantum mechanical problem, it relies on the so-called exchange-correlation functional, the explicit form of which is unknown. A huge research effort, continuing to this day, has produced different generations of functionals of increasing sophistication (the so-called “Jacobs’s ladder”). Simultaneously, tremendous advances in computational algorithms and computer hardware has driven the boom of electronic structure calculations of materials .
For the application of DFT to the calculation of point defects in solids, we refer to excellent reviews by Freysoldt et al. and Dreyer et al. , . The latter specifically focuses on QPDs. Here, our goal is to assess the level of accuracy and computational ease with which different properties of QPDs can be modeled. To this avail, we divide properties of point defects into three major categories, as summarized in Table 3 and described in detail:
Categories of point-defect properties organized according to the development of theoretical methodology for quantitative calculations.
|Brief description of properties||Defect properties||Status of development|
|(i) Basic ground-state properties||Geometries, defect formation energies, charge-state transition levels, ionization levels, ground-state spin multiplicity, vibrational modes and frequencies||Methodology well-developed and accepted, widely implemented and tested, ready for high-throughput calculations|
|(ii) Specific ground-state properties||Magnetic interactions (zero-field splitting, spin-orbit, hyperfine), electron-phonon coupling, spin-phonon coupling||No principle difficulties, may be practical difficulties, not widely implemented yet, developments and testing taking place|
|(iii) Excited-state properties||Excited-state energies and geometries, multiplet structure, transition dipole moments, radiative rates, optical lineshapes, nonraditative transitions||Principle difficulties persist, rigorous approaches computationally very expensive, need for approximate methods that have to be tested more systematically|
- Basic ground-state properties. When initially considering the defect chemistry in any material or analyzing a new class of defects, several key parameters need to be established: defect formation energies, charge-state transition, and ionization levels, defect geometries in different charge states, ground-state spin configurations, and vibrational properties in the ground state. Most of the major developments in the electronic structure calculations of point defects in the past decades addressed one of these properties in one way or another. The existing methodology to calculate these properties is sound and nearly universally accepted . The most important aspect of theory needed to reliably describe these properties is the correct description of the host’s atomic and electronic structure (including the band gap), as well as the correct description of charge localization. So-called hybrid density functionals  that incorporate a fraction of exact (Fock) exchange perform well on both fronts. Calculations of the basic properties using these functionals have become routine, and they can be even done in a high-throughput manner , . Continued progress in developing new functionals with improved accuracy is also expected.
- Specific ground-state properties. This category comprises properties that are not yet routinely calculated, but of which the calculation in principle poses no fundamental problems. They mainly involve the spin structure and magnetic interactions of the ground state, as well as electron-phonon and spin-phonon interaction in the ground state. Many of these properties are crucial for QPDs, but not necessarily for other areas of defect physics (e.g. they are not needed for understanding doping, defect compensation, Fermi-level pinning, or material growth). As such, methodological developments to calculate these properties have been relatively more recent.Spin properties and magnetic interactions are paramount for many QPD applications. One such property is the spin-spin interaction that leads to the zero-field splitting (ZFS) between spin sub-levels . The calculation of the ZFS is currently implemented in several major electronic structure codes , and recent developments focused on improvements in accuracy . Similarly, the calculation of spin-orbit interactions are also currently possible for point defects in solids . Spin-orbit interactions contribute to the ZFS in certain defects (e.g. the SiV center) and are very important for various other processes, for example, the ISC. Hyperfine interactions between the QPD’s electron spin and the surrounding nuclear spins also play a crucial role for qubits and quantum memory applications. First-principles calculations of hyperfine couplings have been possible for some time , and the accuracy of such calculations continues to improve through the use of hybrid functionals .A few recent studies have used hyperfine coupling calculations to study the behavior of entire systems of coupled spins, demonstrating the power of first-principles methods. Ivady et al.  introduced a method to model dynamic nuclear polarization, i.e. polarization transfer from the electron to nuclear spins. Seo et al.  showed how the knowledge of hyperfine parameters can be used to calculate spin decoherence times of qubits in SiC. These examples represent first steps towards addressing properties of an entire interacting many-body spin system using first-principles methods.First-principles methods have been also useful in calculating various manifestations of electron-phonon coupling at defects, for example, the temperature shift of defect levels . The interaction of spins with phonons, for example, the calculation of the intrinsic longitudinal spin relaxation time, can be also addressed  with first-principles methods.
- Excited state properties. Finally, some defect properties still pose considerable fundamental and practical hurdles. Most importantly, these are properties related to excited states. DFT is, at its core, a ground-state theory. To access electronically excited states, one needs to go beyond DFT in one way or another. The problems of excited states are not restricted to point defects, but are a general problem of many-body quantum mechanics. The peculiarity of point defects is that they are intrinsically non-periodic systems involving a very large number of coupled ions and electrons.On the one hand, approaches developed for periodic solids, such as many-body perturbation theory, i.e. the GW approximation for the quasiparticle band structure and the subsequent solution of the Bethe-Salpeter equation for optical excitations , could be also applied to point defects , . However, these approaches are computationally expensive, especially for large systems, and therefore they are too demanding for a systematic study of many defects. Furthermore, the GW approach itself suffers from core deficiencies even for periodic solids , and the practical application of the improved method (the so-called GWΓ approximation ) will not be computationally feasible in the near future .On the other hand, there have been significant advances in methods that split the electronic system into a local sub-system that describes active electrons at or near the defect, and the bulk sub-system which provides electronic screening. One example is an approach based on parameterizing the Hubbard-type electronic Hamiltonian , and another example is the constrained-RPA method . These approaches are promising. However, it is not clear whether they always converge to the correct result, and in our opinion their predictive power is yet to be demonstrated. Serious work on these many-body methods is still needed.Given the state of affairs regarding these many-body approaches, approximate methods to calculate excited states are very important. One such approach is the constrained DFT method . An example of this method is the ΔSCF (delta-self consistent field) scheme, whereby electronic excitation is modeled within DFT by constraining orbital occupations . When optical excitations occur between single-Slater-determinant states of different spatial symmetry, the ΔSCF approach yields good results . However, defect states are often made of a few Slater determinants (multi-determinant states). Proposals for how to address these states within the ΔSCF approach exist , but work in this area targeting point defects has been sporadic and inconclusive. More research is needed on this front.Once the excited state wavefunction is obtained within a certain approach, then one can calculate important properties related to optical transitions, in particular the polarization of emitted light, transition dipole moments, and thus also radiative lifetimes. In addition, by studying lattice relaxation due to optical excitation, one can calculate Huang-Rhys factors that quantify electron-phonon coupling during optical transitions , . With additional effort, one can explicitly compute photoluminescence lineshapes . Absorption and photo-ionization cross sections can also be calculated rather straightforwardly . Studies of nonradiative transitions, including carrier capture rates that are important for understanding QPD charge dynamics, are now feasible as well . Apart from difficulties in describing the excited state itself, the subsequent calculation of properties described in the current paragraph poses practical rather than fundamental problems. These calculations could therefore be also ascribed to category (ii).Success in the calculation of magnetic interactions as well as of optical and vibrational properties has recently enabled the ab initio study of the whole spin initialization cycle for NV centers in diamond . These are still early days for such calculations, but it is clear that they will become more wide-spread in the near future, as the methodolgy continues to improve.Computation of excited-state properties for point defects will benefit from ongoing efforts within the entire field of electronic structure calculations. Nonetheless, accurate and systematic methods will likely remain computationally demanding, and further work on various approximate methods is currently of high priority.
The discussion above is our subjective view on the status of theory regarding the three categories of properties of isolated point defects. In particular, categories (ii) and especially (iii) require further development. Not discussed in our brief overview are theoretical approaches to deal with finite-temperature effects. Neither did we touch on a huge area related to the kinetics of defect creation under non-equilibrium conditions. Another, closely related topic for the theory is the effect of a defect’s environment, by which we mean the variation of defect properties in the vicinity of surfaces, the effects of strain and external fields, interactions of point defects with other point and line defects, etc. (see, e.g. ) Many of these effects can be studied explicitly using a combination of analytical approaches, electronic structure calculations, and atomistic modeling. Understanding these aspects is essential for many QPD applications, so this represents fertile ground for theoretical work.
With respect to synthesis, advancements are needed regarding the availability of suitable host materials, the purity of those materials, and methods for defect creation.
6.2.1 Host materials
As discussed in Section 4, early efforts to identify, isolate, and reproducibly create NV centers in diamond were propelled by commercially available high-purity material. The semiconductor industry similarly provides the infrastructure for pure Si and SiC crystals on which QPD development has piggy-backed. The past decade has seen an explosion of commercial offerings of potential QPD host materials and morphologies, driven by new technologies in energy, solid-state lighting, and nanotechnology. For example, colloidal semiconductor quantum dots are now widely used in display technologies , , and the emergence of graphene-based technologies has elevated the profile of many complementary layered materials such as TMDs and hBN . Some of these materials are attractive QPD hosts, as discussed in Section 5.2. However, the level of materials purity required for QPD research often exceeds the demands of these other applications.
Study of new QPDs requires a sample containing either individual defects that can be studied in isolation, or a homogeneous ensemble that can be isolated from other defect signals. Single QPD isolation via confocal microscopy typically requires defect densities less than 1011 cm−3. This concentration is exceedingly small by typical synthesis standards; in Si, an impurity density of 1011 cm−3 corresponds to two parts per trillion. Additionally, unwanted photoluminescence from the host material due to other unintentional defects or surface states must be low enough to enable detection of the single QPD of interest. This is one reason for the field’s focus on defect complexes (e.g. NV and SiV centers in diamond, divacancies in SiC) over single-site defects. Complexes typically have larger formation energies, and therefore smaller concentrations, than single-site defects. This extreme purity requirement can be relaxed somewhat in the case where inhomogeneous broadening of the optical transitions allows one to spectrally filter the signal from a single defect ,  or in cases where nanoparticles or nanoscale devices are utilized for defect isolation , , . Ensemble studies can also be useful for characterizing the basic properties of new QPDs , , . Nevertheless, there should be an eventual pathway towards isolation of individual defects in high-purity, single-crystal substrates.
The most ubiquitous synthesis technique is chemical vapor deposition (CVD); it is the preferred technique for growing high-quality diamond and is widely employed for the investigation of semiconductor materials in non-QPD research. However, CVD usually leads to larger defect concentrations than the part-per-trillion levels discussed above. Alternative methods for synthesis and sample preparation that offer potential advantages for QPD studies should be further developed. These methods include melt-based bulk crystalization methods such as the Czochralski, Bridgeman, and float-zone processes; epitaxial growth techniques such as MBE and atomic layer deposition (ALD); direct exfoliation of bulk layered crystals; and wet chemical synthesis. Each of these approaches is only suitable for a subset of possible materials. Epitaxial techniques such as MBE and ALD are advantageous with regards to achieving high purity and precise control over layer thickness, however they are exceedingly slow.
In two-dimensional systems, the purity requirement for accessing individual defects via confocal microscopy (in terms of the bulk defect density), can be significantly relaxed as the materials are thin. For example, achieving a lateral defect density below 108 cm−2 in a monolayer of hBN requires a concentration below 20 parts per billion. However, the synthesis of many two-dimensional materials remains underdeveloped, and challenges remain, especially with respect to generating large-scale single-crystal samples . Further obstacles exist in reducing contamination and damage during post-growth transfer processes onto other substrates, as the predominant CVD techniques use metal foils as growth substrates. A variety of transfer and post-transfer healing methods have been reported, and work is ongoing to address these challenges , . Nonetheless, alternatives to CVD methods are still of significant interest in these lower-dimensional systems.
Developing ultrapure, single-crystal growth for a new QPD host will require significant investment. Promise for the defect must already be assured. We should thus seriously consider how to facilitate QPD discovery in materials with lower purity. Nanoscale materials platforms, in the form of nanoparticles, wires, and films, are a potential solution. Due to their restricted size, nanocrystal morphologies can facilitate isolation of single QPDs to enable rapid and efficient exploration of basic properties such as energy-level structure and quantum efficiency, facilitate structural characterization, and explore the effect of various synthesis and sample treatment techniques. Whereas the purity, size uniformity, and surface chemistry of diamond nanostructures are notoriously uncontrolled, many other semiconductors can be colloidally synthesized at the nanoscale with precise control over size, shape, and surface termination . In addition to their utility for exploratory studies, nanomaterials are also ideally suited to quantum sensing and nanophotonics applications.
6.2.2 Defect creation
Historically, in situ incorporation during growth ,  and ion implantation/irradiation , , , , , ,  have proven to be effective means of synthesizing QPDs. In situ growth incorporation typically has the advantage of higher crystal quality, but it severely limits the types of defects that can be incorporated and offers no control over lateral defect placement. Ion implantation provides some degree of spatial localization, though at the cost of material damage. Additionally, there still remains statistical uncertainty in defect formation  as well as uncertainty in defect placement (typically tens of nanometers) .
Research to broaden and increase the control of defect incorporation through in situ growth and implantation should continue. Improved understanding of defect energetics (e.g. formation energies) and kinetics is critical to designing precise synthesis strategies. Experimental results can inform theoretical calculations, and vice versa, with recent examples including the preferential orientation of NV centers during CVD growth , ,  and the re-orientation of NV centers at elevated temperatures .
It is also important to develop more precise techniques. MBE allows for impurities to be introduced at precise depths, however, it is does not immediately provide control over lateral positioning. Defect fabrication by scanning tunneling microscopy (STM), followed by material overgrowth, has been used to create single-site dopants in Si . Not only can this technology enable near atomic-scale placement, it might also provide a route toward controlled fabrication of multi-qubit registers , . However, STM placement has not been successfully demonstrated in QPD systems apart from Si. Scanning transmission electron microscopy (STEM) offers a precise way to create and visualize single vacancies , , , , and it could potentially be adapted for creating two-site defects in combination with dopant incorporation. Two-dimensional host materials provide an ideal platform for exploring the potential of STEM-based techniques.
6.3 Characterization and identification
The identification of QPDs requires the correlation of many complementary measurements, as depicted in Figure 4. Individually, different techniques reveal information about a defect’s electronic or chemical structure, and crucially for QPDs, about its spin and optical dynamics. Only together, supported by understanding and control over the material synthesis, the role of treatments such as irradiation and annealing, and through comparisons with theory, do such measurements yield a comprehensive picture.
This approach is supported by a long history in the identification of optically active defects in solids , . Traditionally, experiments were performed on defect ensembles, typically using a combination of optical spectroscopy, elemental analysis, and magnetic resonance. In contrast, recent investigations of QPDs in new and emerging materials have predominantly focused on optical spectroscopy . The reason for this focus is the need to detect extremely low impurity concentrations – eventually the signal from a single defect – which exceeds the limits of many traditional techniques.
For example, consider studies on the recently (2016) discovered single-photon emitters in hBN, emitting in the ~2 eV range. Initial reports provided significant data characterizing the electronic structure and optical dynamics , , , . Subsequent studies explored the role of strain , electric , and magnetic ,  fields on the optical emission properties, along with various methods for creating defects , , . As of July 2019, over 70 papers have appeared on the subject, and yet the defects’ chemical structure remains unresolved. Progress has been limited by a lack of high-purity host material and limited understanding of hBN’s defect chemistry, as well as an absence of correlative measurements such as optically detected magnetic resonance. A similar situation exists for QPDs in WSe2 and other two-dimensional materials . These examples highlight the need for new experimental approaches to characterize and identify QPDs more efficiently.
6.3.1 Existing approaches
Optical measurements yield a wealth of information. A defect’s photoluminescence signal, especially in the presence of applied magnetic, electric, and strain fields, contains information about its electronic Hamiltonian and environmental interactions , . Spectral decomposition of the emission identifies the ZPL and phonon contributions , . Measurements of the optical polarization dependence for excitation and emission yield information regarding the defect’s symmetry and optical dipole configurations , . Time-resolved photoluminescence measurements reveal excited state lifetimes and dynamics , . Under steady-state illumination, measurements of the photon emission statistics provide valuable information about optical dynamics; photon antibunching at zero delay confirms single-photon emission, whereas photon bunching over longer delays implies the existence of metastable states and ionization dynamics , . Even for inhomogeneously broadened defect ensembles, variations in the spectral lineshape or polarization in response to applied electric, magnetic, or strain fields reveals information about the ground and excited-state electronic structure, including clues about the spin Hamiltonian , .
While these optical techniques are powerful, they are typically not enough to positively identify an unknown defect as they provide limited ground-state, structural, and chemical information. Some well-established defect characterization techniques that could provide this information are rarely utilized by the QPD community. These include secondary ion mass spectrometry (SIMS), X-ray absorption spectrocopy (XAS), and X-ray photoelectron spectroscopy (XPS) to quantify impurity concentrations and – in the case of XAS and XPS – chemical bonding information. Vibrational probes such as Raman and Fourier-transform infrared (FTIR) spectroscopy also reveal structural and chemical information. Optoelectronic techniques such as photoconductivity measurements and deep level transient spectroscopy (DLTS) probe electronically active defects and charge transfer mechanisms. Finally, electron paramagnetic resonance (EPR), nuclear magnetic resonance (NMR), and their variants including double electron-electron resonance (DEER) and electron nuclear double resonance (ENDOR) are essential tools for studying spin properties, and they can also yield clues about a defect’s structure (e.g. through its hyperfine spectrum) as well as interactions between different defect species.
The primary reason the QPD community has not adopted these techniques is that they are all ensemble characterization methods with a limit of detection (LOD) significantly higher than the level targeted for single defects, ≲1011 cm−3. In some cases, the LOD can potentially be improved. In other cases, new techniques are required, and we consider some possibilities below. Nevertheless, the characterization techniques listed above should not be ignored as they characterize a material’s purity and – even when they cannot resolve a population of QPDs – they provide valuable information about other coexisting defect populations that might be optically inactive and yet present at far greater concentrations than the QPD of interest.
6.3.2 Advances in measurement to facilitate discovery
As experimental capabilities improve, new approaches that could circumvent the QPD characterization bottleneck are becoming viable. Keeping in mind the need to access and correlate the four quadrants depicted in Figure 4, we highlight in particular the need for (i) further emphasis on defect ensemble measurements, (ii) lowering the LOD for traditional characterization techniques, and (iii) innovating new cross-correlative measurements.
- Ensemble measurements. While it is necessary for most QPD applications to isolate single defects, any scalable technology also requires the ability to create many homogeneous defects. Advances in our ability to synthesize high-quality hosts and homogeneous defect ensembles, discussed in Section 6.2, will facilitate the adoption of non-optical techniques by the QPD community. Ensemble measurements also enable higher-throughput defect characterization in the optical domain.The ensemble approach is complementary to the prevalent modern approach based on observations of single defects. While single defect spectroscopy will still be required when synthesis of homogenous QPD ensembles is not possible, non-optical characterization of host materials can elucidate the properties of optically inactive defect species  that can influence a QPD’s charge or spin dynamics. Moreover, optically dark defects can have desirable quantum properties. For example, the record 39 min quantum memory time of the phosphorous donor nucleus in silicon was measured using ensemble techniques . These non-optical QPDs, optimized for memory or coupling , could be coupled to optically active defects in hybrid qubit platforms.
- Improving the LOD. Many of the non-optical defect characterization techniques were developed for applications that did not require ppb- or ppt-level detection. The need for lower LODs to address emerging applications in quantum science can spur further investment in these techniques. In some cases, advances have already been made. For example, ODMR, a type of EPR, can be realized at the single-defect limit; however determining whether or not a defect can exhibit ODMR is currently a challenge for theory (see Section 6.1), and brute-force experiments on single defects require time-consuming experimental parameter sweeps.
- New techniques. Advances in atomic-resolution imaging techniques provide new opportunities to directly characterize the chemical structure of individual QPDs. These techniques are ideally suited to low-dimensional materials and nanomaterials, which are often more difficult to study using traditional approaches. Atom probe tomography provides sub-nanometer spatial information of the chemical composition, although sample preparation can be prohibitive, and the measurement technique is destructive. Improvements in the resolution and detection efficiency for STEM imaging and spectroscopy at low beam energy has enabled the characterization of individual defects in hBN , , , , , although beam-induced damage remains a challenge. Atomic electron tomography (AET), based on STEM, can determine the precise location of every atom in a material, however it is currently limited to very small particles (<10 nm)  or very thin samples  consisting of heavy elements.Ideally, these structural imaging techniques can be directly correlated with measurements of the orbital and spin structure. Recent efforts attempt to bridge the gap between atomic-resolution imaging and optical spectroscopy , , , , although sample preparation and measurements remain extremely challenging. Another intriguing possibility is to use QPDs themselves as probes for materials exploration. Shallow NV centers in diamond are extremely sensitive probes of nanoscale materials , , , and they can be employed to study surface states, interfaces, and even other individual defects . While much of this correlative work is still in its nascent stage, it moves the field in a direction towards a common set of characterization tools that can be leveraged, along with theory, to identify, manipulate, and control QPDs for quantum technologies.
We hope that these new and emerging characterization techniques can expand from their current status as specialized tools scattered in individual research labs to become more pervasive in the overall QPD research community. In some cases, where experimental hardware is the main obstacle, opportunities exist for companies to develop upgrades or add-ons for existing equipment. One example would be specialized STEM sample probes that facilitate correlated optical and structural measurements. In other cases, techniques can be disseminated by sharing experimental acquisition routines and technical know-how between labs.
One cannot measure everything, and it is essential to consider the application criteria when designing a measurement scheme, following the guidelines laid out in Section 5. High-throughput schemes can be considered for some techniques (e.g. optical spectroscopy), whereas others are inherently limited in terms of sample throughput (e.g. STM or STEM imaging). For this reason, it will be especially valuable to combine several complementary techniques in a system that facilitates rapid iterations between materials synthesis, treatment under various conditions, and comprehensive characterization of QPD-relevant quantities, in order to direct and optimize the search and development of new QPD systems within a large parameter space.
In a letter to Rudolph Peierls from 1931, Wolfgang Pauli pronounced: “One shouldn’t work on semiconductors; that is a filthy mess. 1 Who knows if they really exist?” Pauli was responding to the difficulty at the time in making sense of various conflicting measurements on semiconductor materials, including strange changes in Hall voltages – and their signs – as a function of temperature, along with apparently random variations between samples. Today we know that the source of that “filthy mess” was in fact defects. Just as it must have been nearly impossible in 1931 to anticipate how early experiments on semiconductors would lead to the age of integrated circuits, it is foolish to assume in the present day that we understand the full scope of future quantum technologies. What seems clear is that Pauli’s filthy mess will continue to drive scientific discovery and technological innovation, as semiconductor devices finally reach the ultimate scale of individual atoms.
LCB acknowledges support from the National Science Foundation, Funder Id: http://dx.doi.org/10.13039/100000078, under Grant No. DMR-1922278. AA acknowledges funding from the European Union’s Horizon 2020 research and innovation programme, Funder Id: http://dx.doi.org/10.13039/100010661, under grant agreement No. 820394 (project A steriqs). KMF acknowledges support from the National Science Foundation, Funder Id: http://dx.doi.org/10.13039/100000001, under Grant No. 1807566. We thank D. Twitchen and M. Markham for discussions on the history of electronic-grade diamond, M. Mackoit-Sinkevičienė for preparing Figure 1, and R. Zia for lively discussions regarding the quantum defects by design paradigm and the idea of Figure 2.
Awschalom DD, Bassett LC, Dzurak AS, Hu EL, Petta JR. Quantum spintronics: engineering and manipulating atom-like spins in semiconductors. Science 2013;339:1174–9.
Gao WB, Imamoglu A, Bernien H, Hanson R. Coherent manipulation, measurement and entanglement of individual solid-state spins using optical fields. Nat Photonics 2015;9:363–73.
Atatüre M, Englund D, Vamivakas N, Lee S-Y, Wrachtrup J. Material platforms for spin-based photonic quantum technologies. Nat Rev Mater 2018;3:38–51.
Steger M, Saeedi K, Thewalt MLW, et al. Quantum information storage for over 180 s using donor spins in a 28Si “semiconductor vacuum”. Science 2012;336:1280–3.
Beall Fowler W, editor. Physics of color centers. New York, NY: Academic Press, 1968.
Stoneham AM. Theory of defects in solids. Oxford: Oxford University Press, 1975.
Doherty MW, Manson NB, Delaney P, Jelezko F, Wrachtrup J, Hollenberg LCL. The nitrogen-vacancy colour centre in diamond. Phys Rep 2013;528:1–45.
Thiel L, Wang Z, Tschudin MA, et al. Probing magnetism in 2D materials at the nanoscale with single-spin microscopy. Science 2019;364:973–6.
Andersen TI, Dwyer BL, Sanchez-Yamagishi JD, et al. Electron-phonon instability in graphene revealed by global and local noise probes. Science 2019;364:154–7.
Ariyaratne A, Bluvstein D, Myers BA, Bleszynski Jayich AC. Nanoscale electrical conductivity imaging using a nitrogen-vacancy center in diamond. Nat Commun 2018;9:2406.
Shi F, Zhang Q, Wang P, et al. Single-protein spin resonance spectroscopy under ambient conditions. Science 2015;347:1135–8.
Lovchinsky I, Sushkov AO, Urbach E, et al. Nuclear magnetic resonance detection and spectroscopy of single proteins using quantum logic. Science 2016;351:836–41.
Aslam N, Pfender M, Neumann P, et al. Nanoscale nuclear magnetic resonance with chemical resolution. Science 2017;357:67–71.
Schirhagl R, Chang K, Loretz M, Degen CL. Nitrogen-vacancy centers in diamond: nanoscale sensors for physics and biology. Annu Rev Phys Chem 2014;65:83–105.
Childress L, Gurudev Dutt MV, Taylor JM, et al. Coherent dynamics of coupled electron and nuclear spin qubits in diamond. Science 2006;314:281–5.
Gurudev Dutt MV, Childress L, Jiang L, et al. Quantum register based on individual electronic and nuclear spin qubits in diamond. Science 2007;16:1312–6.
Neumann P, Mizuochi N, Rempp F, et al. Multipartite entanglement among single spins in diamond. Science 2008;320:1326–9.
Dolde F, Jakobi I, Naydenov B, et al. Room-temperature entanglement between single defect spins in diamond. Nat Phys 2013;9:139–43.
Maurer PC, Kucsko G, Latta C, et al. Room-temperature quantum bit memory exceeding one second. Science 2012;336:1283–6.
Abobeih MH, Cramer J, Bakker MA, et al. One-second coherence for a single electron spin coupled to a multi-qubit nuclear-spin environment. Nat Commun 2018;9:2552.
Pfaff W, Hensen BJ, Bernien H, et al. Unconditional quantum teleportation between distant solid-state quantum bits. Science 2014;345:532–5.
Waldherr G, Wang Y, Zaiser S, et al. Quantum error correction in a solid-state hybrid spin register. Nature 2014;506:204–7.
Taminiau TH, Cramer J, van der Sar T, Dobrovitski V, Hanson R. Universal control and error correction in multi-qubit spin registers in diamond. Nat Nanotechnol 2014;9:171–6.
Cramer J, Kalb N, Rol MA, et al. Repeated quantum error correction on a continuously encoded qubit by real-time feedback. Nat Commun 2016;7:11526.
Buckley BB, Fuchs GD, Bassett LC, Awschalom DD. Spin-light coherence for single-spin measurement and control in diamond. Science 2010;330:1212–5.
Togan E, Chu Y, Trifonov AS, et al. Quantum entanglement between an optical photon and a solid-state spin qubit. Nature 2010;466:730–4.
Yale CG, Buckley BB, Christle DJ, et al. All-optical control of a solid-state spin using coherent dark states. Proc Natl Acad Sci U S A 2013;110:7595–600.
Bassett LC, Heremans FJ, Christle DJ, et al. Ultrafast optical control of orbital and spin dynamics in a solid-state defect. Science 2014;345:1333–7.
Bernien H, Hensen B, Pfaff W, et al. Heralded entanglement between solid-state qubits separated by three metres. Nature 2013;497:86–90.
Kalb N, Reiserer AA, Humphreys PC, et al. Entanglement distillation between solid-state quantum network nodes. Science 2017;356:928–32.
Humphreys PC, Kalb N, Morits JPJ, et al. Deterministic delivery of remote entanglement on a quantum network. Nature 2018;558:268–73.
Awschalom DD, Hanson R, Wrachtrup J, Zhou BB. Quantum technologies with optically interfaced solid-state spins. Nat Photonics 2018;12:516–27.
Neu E, Steinmetz D, Riedrich-Möller J, et al. Single photon emission from silicon-vacancy colour centres in chemical vapour deposition nano-diamonds on iridium. New J Phys 2011;13:025012.
Pingault B, Becker JN, Schulte CHH, et al. All-optical formation of coherent dark states of silicon-vacancy spins in diamond. Phys Rev Lett 2014;113:263601.
Hepp C, Müller T, Waselowski V, et al. Electronic structure of the silicon vacancy color center in diamond. Phys Rev Lett 2014;112:036405.
Rogers LJ, Jahnke KD, Metsch MH, et al. All-optical initialization, readout, and coherent preparation of single silicon-vacancy spins in diamond. Phys Rev Lett 2014;113:263602.
Green BL, Mottishaw S, Breeze BG, et al. Neutral silicon-vacancy center in diamond: spin polarization and lifetimes. Phys Rev Lett 2017;119:096402.
Rose BC, Huang D, Zhang Z-H, et al. Observation of an environmentally insensitive solid-state spin defect in diamond. Science 2018;361:60–3.
Koehl WF, Buckley BB, Heremans FJ, Calusine G, Awschalom DD. Room temperature coherent control of defect spin qubits in silicon carbide. Nature 2011;479:84–7.
Christle DJ, Falk AL, Andrich P, et al. Isolated electron spins in silicon carbide with millisecond coherence times. Nat Mater 2015;14:160–3.
Widmann M, Lee S-Y, Rendler T, et al. Coherent control of single spins in silicon carbide at room temperature. Nat Mater 2015;14:164–8.
Kolesov R, Xia K, Reuter R, et al. Mapping spin coherence of a single rare-earth ion in a crystal onto a single photon polarization state. Phys Rev Lett 2013;111:120502.
Xia K, Kolesov R, Wang Y, et al. All-optical preparation of coherent dark states of a single rare earth ion spin in a crystal. Phys Rev Lett 2015;115:093602.
Morfa AJ, Gibson BC, Karg M, et al. Single-photon emission and quantum characterization of zinc oxide defects. Nano Lett 2012;12:949–54.
Jungwirth NR, Chang H-S, Jiang M, Fuchs GD. Polarization spectroscopy of defect-based single photon sources in ZnO. ACS Nano 2016;10:1210–5.
Linpeng X, Viitaniemi MLK, Vishnuradhan A, et al. Coherence properties of shallow donor qubits in ZnO. Phys Rev Appl 2018;10:064061.
Koehl WF, Diler B, Whiteley SJ, et al. Resonant optical spectroscopy and coherent control of Cr4+ spin ensembles in SiC and GaN. Phys Rev B 2017;95:035207.
Zhou Y, Wang Z, Rasmita A, et al. Room temperature solid-state quantum emitters in the telecom range. Sci Adv 2018;4:eaar3580.
Berhane AM, Jeong K-Y, Bodrog Z, et al. Bright room-temperature single-photon emission from defects in gallium nitride. Adv Mater 2019;29:1605092.
Chakraborty C, Kinnischtzke L, Goodfellow KM, Beams R, Vamivakas AN. Voltage-controlled quantum light from an atomically thin semiconductor. Nat Nanotechnol 2015;10:507.
Koperski M, Nogajewski K, Arora A, et al. Single photon emitters in exfoliated WSe2 structures. Nat Nanotechnol 2015;10:503.
He Y-M, Clark G, Schaibley JR, et al. Single quantum emitters in monolayer semiconductors. Nat Nanotechnol 2015;10:497.
Srivastava A, Sidler M, Allain AV, Lembke DS, Kis A, Imamoģlu A. Optically active quantum dots in monolayer WSe2. Nat Nanotechnol 2015;10:491.
Tonndorf P, Schmidt R, Schneider R, et al. Single-photon emission from localized excitons in an atomically thin semiconductor. Optica 2015;2:347–52.
Tran TT, Bray K, Ford MJ, Toth M, Aharonovich I. Quantum emission from hexagonal boron nitride monolayers. Nat Nanotechnol 2016;11:37–41.
Jungwirth NR, Calderon B, Ji Y, Spencer MG, Flatté ME, Fuchs GD. Temperature dependence of wavelength selectable zero-phonon emission from single defects in hexagonal boron nitride. Nano Lett 2016;16:6052–7.
Chejanovsky N, Rezai M, Paolucci F, et al. Structural attributes and photodynamics of visible spectrum quantum emitters in hexagonal boron nitride. Nano Lett 2016;16: 7037–45.
Exarhos AL, Hopper DA, Grote RR, Alkauskas A, Bassett LC. Optical signatures of quantum emitters in suspended hexagonal boron nitride. ACS Nano 2017;11:3328–36.
Exarhos AL, Hopper DA, Patel RN, Doherty MW, Bassett LC. Magnetic-field-dependent quantum emission in hexagonal boron nitride at room temperature. Nat Commun 2019;10:222.
Sipahigil A, Jahnke KD, Rogers LJ, et al. Indistinguishable photons from separated silicon-vacancy centers in diamond. Phys Rev Lett 2014;113:113602.
Rogers LJ, Jahnke KD, Teraji T, et al. Multiple intrinsically identical single-photon emitters in the solid state. Nat Commun 2014;5:4739.
Sipahigil A, Evans RE, Sukachev DD, et al. An integrated diamond nanophotonics platform for quantum-optical networks. Science 2016;354:847–50.
Evans RE, Bhaskar MK, Sukachev DD, et al. Photon-mediated interactions between quantum emitters in a diamond nanocavity. Science 2018;362:662–5.
Koehl WF, Seo H, Galli G, Awschalom DD. Designing defect spins for wafer-scale quantum technologies. MRS Bull 2015;40:1146–53.
Sangouard N, Simon C, de Riedmatten H, Gisin N. Quantum repeaters based on atomic ensembles and linear optics. Rev Mod Phys 2011;83:33–80.
Thiel CW, Böttger T, Cone RL. Rare-earth-doped materials for applications in quantum information storage and signal processing. J Lumin 2011;131:353–61.
Ham BS, Hemmer PR, Shahriar MS. Efficient electromagnetically induced transparency in a rare-earth doped crystal. Opt Commun 1997;144:227–30.
Gali Á. Ab initio theory of the nitrogen-vacancy center in diamond. Nanophotonics 2019;8:1907–43.
Rondin L, Tetienne J-P, Hingant T, Roch JF, Maletinsky P, Jacques V. Magnetometry with nitrogen-vacancy defects in diamond. Rep Prog Phys 2014;77:056503.
Gruber A, Dräbenstedt A, Tietz C, Fleury L, Wrachtrup J, von Borczyskowski C. Scanning confocal optical microscopy and magnetic resonance on single defect centers. Science 1997;276:2012–4.
Du Preez L. Electron paramagnetic resonance and optical investigations of defect centres in diamond. PhD thesis, University of Witwatersrand, Johannesburg, 1965.
Davies G, Hamer MF, Charles PW. Optical studies of the 1.945 eV vibronic band in diamond. Proc R Soc London Ser A 1976;348:285.
Loubser JHN, Van Wyk JA. Optical spin-polarisation in a triplet state in irrdiated and annealed type 1b diamonds. Diamond Res 1977;9:11.
van Oort E, Stroomer P, Glasbeek M. Low-field optically detected magnetic resonance of a coupled triplet-doublet defect pair in diamond. Phys Rev B 1990;42:8605–8.
Brouri R, Beveratos A, Poizat J-P, Grangier P. Photon antibunching in the fluorescence of individual color centers in diamond. Opt Lett 2000;25:1294–6.
Kurtsiefer C, Mayer S, Zarda P, Weinfurter H. Stable solid-state source of single photons. Phys Rev Lett 2000;85:290–3.
Jelezko F, Gaebel T, Popa I, Gruber A, Wrachtrup J. Observation of coherent oscillations in a single electron spin. Phys Rev Lett 2004;92:076401.
Jelezko F, Gaebel T, Popa I, Domhan M, Gruber A, Wrachtrup J. Observation of coherent oscillation of a single nuclear spin and realization of a two-qubit conditional quantum gate. Phys Rev Lett 2004;93:130501.
Taylor JM, Cappellaro P, Childress L, et al. High-sensitivity diamond magnetometer with nanoscale resolution. Nat Phys 2008;4:810–6.
Maze JR, Stanwix PL, Hodges JS, et al. Nanoscale magnetic sensing with an individual electronic spin in diamond. Nature 2008;455:644–7.
Balasubramanian G, Chan IY, Kolesov R, et al. Nanoscale imaging magnetometry with diamond spins under ambient conditions. Nature 2008;455:648–651.
Balasubramanian G, Neumann P, Twitchen D, et al. Ultralong spin coherence time in isotopically engineered diamond. Nat Mater 2009;8:383–7.
Fu K-MC, Santori C, Barclay PE, Rogers LJ, Manson NB, Beausoleil RG. Observation of the dynamic Jahn-Teller effect in the excited states of nitrogen-vacancy centers in diamond. Phys Rev Lett 2009;103:256404.
Isberg J, Hammersberg J, Johansson E, et al. High carrier mobility in single-crystal plasma-deposited diamond. Science 2002;297:1670–2.
Meijer J, Burchard B, Domhan M, et al. Generation of single color centers by focused nitrogen implantation. Appl Phys Lett 2005;87:261909.
Toyli DM, Weis CD, Fuchs GD, Schenkel T, Awschalom DD. Chip-scale nanofabrication of single spins and spin arrays in diamond. Nano Lett 2010;10:3168–72.
Chu Y, de Leon NP, Shields BJ, et al. Coherent optical transitions in implanted nitrogen vacancy centers. Nano Lett 2014;14:1982–6.
Robledo L, Childress L, Bernien H, Hensen B, Alkemade PFA, Hanson R. High-fidelity projective read-out of a solid-state spin quantum register. Nature 2011;477:574–8.
Hopper DA, Shulevitz HJ, Bassett LC. Spin readout techniques of the nitrogen-vacancy center in diamond. Micromachines 2018;9:437.
Goldman ML, Sipahigil A, Doherty MW, et al. Phonon-induced population dynamics and intersystem crossing in nitrogen-vacancy centers. Phys Rev Lett 2015;114:145502.
Siyushev P, Pinto H, Vörös M, Gali A, Jelezko F, Wrachtrup J. Optically controlled switching of the charge state of a single nitrogen-vacancy center in diamond at cryogenic temperatures. Phys Rev Lett 2013;110:167402.
Thiering G, Gali A. Theory of the optical spin-polarization loop of the nitrogen-vacancy center in diamond. Phys Rev B 2018;98:085207.
Waldherr G, Neumann P, Huelga SF, Jelezko F, Wrachtrup J. Violation of a temporal Bell inequality for single spins in a diamond defect center. Phys Rev Lett 2011;107:090401.
Shields BJ, Unterreithmeier QP, de Leon NP, Park H, Lukin MD. Efficient readout of a single spin state in diamond via spin-to-charge conversion. Phys Rev Lett 2015;114:136402.
Hopper DA, Grote RR, Exarhos AL, Bassett LC. Near-infrared-assisted charge control and spin readout of the nitrogen-vacancy center in diamond. Phys Rev B 2016;94:241201.
Bourgeois E, Londero E, Buczak K, et al. Enhanced photoelectric detection of NV magnetic resonances in diamond under dual-beam excitation. Phys Rev B 2017;95:041402.
Bourgeois E, Jarmola A, Siyushev P, et al. Photoelectric detection of electron spin resonance of nitrogen-vacancy centres in diamond. Nat Commun 2015;6:8577.
Hrubesch FM, Braunbeck G, Stutzmann M, Reinhard F, Brandt MS. Efficient electrical spin readout of NV− centers in diamond. Phys Rev Lett 2017;118:037601.
Siyushev P, Nesladek M, Bourgeois E, et al. Photoelectrical imaging and coherent spin-state readout of single nitrogen-vacancy centers in diamond. Science 2019;363:728–31.
Plakhotnik T, Doherty MW, Cole JH, Chapman R, Manson NB. All-optical thermometry and thermal properties of the optically detected spin resonances of the NV-center in nanodiamond. Nano Lett 2014;14:4989–96.
Mizuochi N, Neumann P, Rempp F, et al. Coherence of single spins coupled to a nuclear spin bath of varying density. Phys Rev B 2009;80:041201.
Doherty MW, Meriles CA, Alkauskas A, Fedder H, Sellars MJ, Manson NB. Towards a room-temperature spin quantum bus in diamond via electron photoionization, transport, and capture. Phys Rev X 2016;6:041035.
Baranov PG, Il’in IV, Mokhov EN, Muzafarova MV, Orlinskii SB, Schmidt J. EPR identification of the triplet ground state and photoinduced population inversion for a Si-C divacancy in silicon carbide. Jetp Lett 2005;82:441–3.
Janzén E, Gali A, Carlsson P, Gällström A, Magnusson B, Son NT. The silicon vacancy in SiC. Phys B 2009;404: 4354–4358.
Thiering A, Gali G. Ab initio magneto-optical spectrum of group-IV vacancy color centers in diamond. Phys Rev X 2018;8:021063.
Linpeng X, Karin T, Durnev MV, et al. Longitudinal spin relaxation of donor-bound electrons in direct band-gap semiconductors. Phys Rev B 2016;94:125401.
Yang L-P, Burk C, Widmann M, Lee S-Y, Wrachtrup J, Zhao N. Electron spin decoherence in silicon carbide nuclear spin bath. Phys Rev B 2014;90:241203.
Seo H, Falk AL, Klimov PV, Miao KC, Galli G, Awschalom DD. Quantum decoherence dynamics of divacancy spins in silicon carbide. Nat Commun 2016;7:12935.
Gangloff DA, Éthier-Majcher G, Lang C, et al. Quantum interface of an electron and a nuclear ensemble. Science 2019;364:62–6.
Dong W, Doherty MW, Economou SE. Spin polarization through intersystem crossing in the silicon vacancy of silicon carbide. Phys Rev B 2019;99:184102.
MacQuarrie ER, Gosavi TA, Jungwirth NR, Bhave SA, Fuchs GD. Mechanical spin control of nitrogen-vacancy centers in diamond. Phys Rev Lett 2013;111:227602.
Lee KW, Lee D, Ovartchaiyapong P, Minguzzi J, Maze JR, Bleszynski Jayich AC. Strain coupling of a mechanical resonator to a single quantum emitter in diamond. Phys Rev Appl 2016;6:034005.
Schuetz MJA, Kessler EM, Giedke G, Vandersypen LMK, Lukin MD, Cirac JI. Universal quantum transducers based on surface acoustic waves. Phys Rev 2015;X 5:031031.
Lemonde M-A, Meesala S, Sipahigil A, et al. Phonon networks with silicon-vacancy centers in diamond waveguides. Phys Rev Lett 2018;120:213603.
Kuzyk MC, Wang H. Scaling phononic quantum networks of solid-state spins with closed mechanical subsystems. Phys Rev X 2018;8:041027.
Jarmola A, Acosta VM, Jensen K, Chemerisov S, Budker D. Temperature- and magnetic-field-dependent longitudinal spin relaxation in nitrogen-vacancy ensembles in diamond. Phys Rev Lett 2012;108:197601.
Bar-Gill N, Pham LM, Jarmola A, Budker D, Walsworth RL. Solid-state electronic spin coherence time approaching one second. Nat Commun 2013;4:1743.
Weston L, Wickramaratne D, Mackoit M, Alkauskas A, Van de Walle CG. Native point defects and impurities in hexagonal boron nitride. Phys Rev B 2018;97:214104.
Xu Z-Q, Mendelson N, Scott JA, Li C, Aharonovich I, Toth M. Charge transition levels of quantum emitters in hexagonal boron nitride. arXiv e-prints 2019;arXiv: 1907.00471.
Kumar S, Kaczmarczyk A, Gerardot BD. Strain-induced spatial and spectral isolation of quantum emitters in mono- and bilayer WSe2. Nano Letters 2015;15:7567.
Grosso G, Moon H, Lienhard B, et al. Tunable and high-purity room temperature single-photon emission from atomic defects in hexagonal boron nitride. Nat Commun 2017;8:705.
Zhong M, Hedges MP, Ahlefeldt RL, et al. Optically addressable nuclear spins in a solid with a six-hour coherence time. Nature 2015;517:177.
Utzat H, Sun W, Kaplan AEK, et al. Coherent single-photon emission from colloidal lead halide perovskite quantum dots. Science 2019;363:1068–72.
Ridley BK. Quantum processes in semiconductors. Oxford: Oxford University Press, 1993.
Martin RM. Electronic structure: basic theory and practical methods. Cambridge: Cambridge University Press, 2004.
Freysoldt C, Grabowski B, Hickel T, et al. First-principles calculations for point defects in solids. Rev Mod Phys 2014;86:253.
Dreyer CE, Alkauskas A, Lyons JL, Janotti A, Van de Walle CG. First-principles calculations of point defects for quantum technologies. Annu Rev Mater Res 2018;48:1–26.
Goyal A, Gorai P, Peng H, Lany S, Stevanovič V. A computational framework for automation of point defect calculations. Comp Mater Sci 2017;130:1–9.
Broberg D, Medasani B, Zimmermann NER, et al. PyCDT: a python toolkit for modeling point defects in semiconductors and insulators. Comp Phys Commun 2018;226:165–79.
Rayson MJ, Briddon PR. First principles method for the calculation of zero-field splitting tensors in periodic systems. Phys Rev B 2008;77:035119.
Bodrog Z, Gali A. The spin-spin zero-field splitting tensor in the projector-augmented-wave method. J Phys: Condens Matter 2013;26:015305.
Biktagirov T, Schmidt WG, Gerstmann U. Calculation of spin-spin zero-field splitting within periodic boundary conditions: towards all-electron accuracy. Phys Rev B 2018;97:115135.
Ivády V, Abrikosov IA, Gali A. First principles calculation of spin-related quantities for point defect qubit research. npj Comput Mater 2018;4:76.
Van de Walle CG. Structural identification of hydrogen and muonium centers in silicon: first-principles calculations of hyperfine parameters. Phys Rev Lett 1990;64:669–72.
Szász K, Hornos T, Marsman M, Gali A. Hyperfine coupling of point defects in semiconductors by hybrid density functional calculations: the role of core spin polarization. Phys Rev B 2013;88:075202.
Ivády V, Szász K, Falk AL, et al. Theoretical model of dynamic spin polarization of nuclei coupled to paramagnetic point defects in diamond and silicon carbide. Phys Rev B 2015;92:115206.
Wickramaratne D, Dreyer CE, Monserrat B, et al. Defect identification based on first-principles calculations for deep level transient spectroscopy. Appl Phys Lett 2018;113:192106.
Astner T, Gugler J, Angerer A, et al. Solid-state electron spin lifetime limited by phononic vacuum modes. Nat Mater 2018;17:313–7.
Onida G, Reining L, Rubio A. Electronic excitations: density-functional versus many-body Green’s-function approaches. Rev Mod Phys 2002;74:601–59.
Ma Y, Rohlfing M. Optical excitation of deep defect levels in insulators within many-body perturbation theory: the F center in calcium fluoride. Phys Rev B 2008;77:115118.
Grumet M, Liu P, Kaltak M, Klimeš J, Kresse G. Beyond the quasiparticle approximation: fully self-consistent GW calculations. Phys Rev B 2018;98:155143.
Choi S, Jain M, Louie SG. Mechanism for optical initialization of spin in NV− center in diamond. Phys Rev B 2012;86:041202.
Bockstedte M, Schütz F, Garratt T, Ivády V, Gali A. Ab initio description of highly correlated states in defects for realizing quantum bits. Npj Quantum Mater 2018;3:31.
Slater JC. Quantum theory of molecules and solids, vol. 1–4. New York, McGraw-Hill, 1963–1974.
Gali A, Janzén E, Deák P, Kresse G, Kaxiras E. Theory of spin-conserving excitation of the NV− center in diamond. Phys Rev Lett 2009;103:186404.
Alkauskas A, Lyons JL, Steiauf D, Van de Walle CG. First-principles calculations of luminescence spectrum line shapes for defects in semiconductors: the example of GaN and ZnO. Phys Rev Lett 2012;109:267401.
Alkauskas A, McCluskey MD, Van de Walle CG. Tutorial: defects in semiconductors – combining experiment and theory. J Appl Phys 2016;119:181101.
Alkauskas A, Buckley BB, Awschalom DD, Van de Walle CG. First-principles theory of the luminescence lineshape for the triplet transition in diamond NV centres. N J Phys 2014;16:073026.
Alkauskas A, Yan Q, Van de Walle CG. First-principles theory of nonradiative carrier capture via multiphonon emission. Phys Rev B 2014;90:075202.
Lindner S, Bommer A, Muzha A, et al. Strongly inhomogeneous distribution of spectral properties of silicon-vacancy color centers in nanodiamonds. New J Phys 2018;20:115002.
Shirasaki Y, Supran GJ, Bawendi MG, Bulović V. Emergence of colloidal quantum-dot light-emitting technologies. Nat Photonics 2012;7:13–23.
Kagan CR, Lifshitz E, Sargent EH, Talapin DV. Building devices from colloidal quantum dots. Science 2016;353:aac5523.
Gammon D, Snow ES, Shanabrook BV, Katzer DS, Park D. Homogeneous linewidths in the optical spectrum of a single gallium arsenide quantum dot. Science 1996;273:87.
Zhong T, Kindem JM, Bartholomew JG, et al. Optically addressing single rare-earth ions in a nanophotonic cavity. Phys Rev Lett 2018;121:183603.
Cai Z, Liu B, Zou X, Cheng H-M. Chemical vapor deposition growth and applications of two-dimensional materials and their heterostructures. Chem Rev 2018;118:6091–133.
Dean CR, Young AF, Meric I, et al. Boron nitride substrates for high-quality graphene electronics. Nat Nanotechnol 2010;5:722.
Castellanos-Gomez A, Buscema M, Molenaar R, et al. Deterministic transfer of two-dimensional materials by all-dry viscoelastic stamping. 2D Mater 2014;1:011002.
Müller T, Hepp C, Pingault B, et al. Optical signatures of silicon-vacancy spins in diamond. Nat Commun 2014;5:3328.
Pezzagna S, Wildanger D, Mazarov P, et al. Nanoscale engineering and optical addressing of single spins in diamond. Small 2010;6:2117–21.
Jamieson DN, Lawrie WIL, Hudson FE, et al. Deterministic atom placement by ion implantation: few and single atom devices for quantum computer technology. In 2016 21st International Conference on Ion Implantation Technology (IIT). Tainan, Taiwan, IEEE, 2016:1–6.
Pacheco JL, Singh M, Perry DL, et al. Ion implantation for deterministic single atom devices. Rev Sci Instrum 2017;88:123301.
Edmonds AM, D’Haenens-Johansson UFS, Cruddace RJ, et al. Production of oriented nitrogen-vacancy color centers in synthetic diamond. Phys Rev B 2012;86:035201.
Michl J, Teraji T, Zaiser S, et al. Perfect alignment and preferential orientation of nitrogen-vacancy centers during chemical vapor deposition diamond growth on (111) surfaces. Appl Phys Lett 2014;104:102407.
Fukui T, Doi Y, Miyazaki T, et al. Perfect selective alignment of nitrogen-vacancy centers in diamond. Appl Phys Exp 2014;7:055201.
Chakravarthi S, Moore C, Opsvig A, et al. A window into NV center kinetics via repeated annealing and spatial tracking of thousands of individual NV centers. arXiv e-prints 2019;arXiv:1907.07793.
Simmons MY, Schofield SR, O’Brien JL, et al. Towards the atomic-scale fabrication of a silicon-based solid state quantum computer. Surf Sci 2003;532–535:1209–18.
Wolfowicz G, Mortemousque P-A, Guichard R, et al. 29Si nuclear spins as a resource for donor spin qubits in silicon. N J Phys 2016;18:023021.
Liu Z, Suenaga K, Wang Z, Shi Z, Okunishi E, Iijima S. Identification of active atomic defects in a monolayered tungsten disulphide nanoribbon. Nat Commun 2011;2:213.
Susi T, Kepaptsoglou D, Lin Y-C, et al. Towards atomically precise manipulation of 2D nanostructures in the electron microscope. 2D Mater 2017;4:042004.
Mishra R, Ishikawa R, Lupini AR, Pennycook SJ. Single-atom dynamics in scanning transmission electron microscopy. MRS Bull 2017;42:644–52.
Noh G, Choi D, Kim JH, et al. Stark tuning of single-photon emitters in hexagonal boron nitride. Nano Lett 2018;18: 4710–5.
Li X, Shepard GD, Cupo A, et al. Nonmagnetic quantum emitters in boron nitride with ultranarrow and sideband-free emission spectra. ACS Nano 2017;11:6652–60.
Choi S, Tran TT, Elbadawi C, et al. Engineering and localization of quantum emitters in large hexagonal boron nitride layers. ACS Appl Mater Interfaces 2016;8:29642–8.
Proscia NV, Shotan Z, Jayakumar H, et al. Near-deterministic activation of room-temperature quantum emitters in hexagonal boron nitride. Optica 2018;5:1128–34.
Toth M, Aharonovich I. Single photon sources in atomically thin materials. Annu Rev Phys Chem 2019;70:123–42.
Epstein RJ, Mendoza FM, Kato YK, Awschalom DD. Anisotropic interactions of a single spin and dark-spin spectroscopy in diamond. Nature Phys 2005;1:94.
Rogers LJ, Jahnke KD, Doherty MW, et al. Electronic structure of the negatively charged silicon-vacancy center in diamond. Phys Rev B 2014;89:235101.
Liaugaudas G, Collins AT, Suhling K, Davies G, Heintzmann R. Luminescence-lifetime mapping in diamond. J Phys: Condens Matter 2009;21:364210.
Fuchs GD, Dobrovitski VV, Toyli DM, et al. Excited-state spin coherence of a single nitrogen-vacancy centre in diamond. Nature Phys 2010;6:668–72.
Neu E, Agio M, Becher C. Photophysics of single silicon vacancy centers in diamond: implications for single photon emission. Opt Express 2012;20:19956.
Berhane AM, Jeong K-Y, Bradac C, et al. Photophysics of GaN single-photon emitters in the visible spectral range. Phys Rev B 2018;97:165202.
Saeedi K, Simmons S, Salvail JZ, et al. Room-temperature quantum bit storage exceeding 39 minutes using ionized donors in silicon-28. Science 2013;342:830.
Yao NY, Jiang L, Gorshkov AV, et al. Scalable architecture for a room temperature solid-state quantum information processor. Nat Commun 2012;3:800.
Alem N, Erni R, Kisielowski C, Rossell MD, Gannett W, Zettl A. Atomically thin hexagonal boron nitride probed by ultrahigh-resolution transmission electron microscopy. Phys Rev B 2009;80:155425.
Jin C, Lin F, Suenaga K, Iijima S. Fabrication of a freestanding boron nitride single layer and its defect assignments. Phys Rev Lett 2009;102:195505.
Wong D, Velasco Jr J, Ju L, et al. Characterization and manipulation of individual defects in insulating hexagonal boron nitride using scanning tunnelling microscopy. Nat Nanotechnol 2015;10:949.
Lin W-H, Brar VW, Jariwala D, et al. Atomic-scale structural and chemical characterization of hexagonal boron nitride layers synthesized at the wafer-scale with monolayer thickness control. Chem Mater 2017;29:4700–7.
Ahmadpour Monazam MR, Ludacka U, Komsa H-P, Kotakoski J. Substitutional Si impurities in monolayer hexagonal boron nitride. Appl Phys Lett 2019;115:071604.
Yang Y, Chen C-C, Scott MC, et al. Deciphering chemical order/disorder and material properties at the single-atom level. Nature 2017;542:75.
Tian X, Kim DS, Yang S, et al. Correlating 3D atomic defects and electronic properties of 2D materials with picometer precision. arXiv e-prints 2019;arXiv:1901.00633.
Govyadinov AA, Konečná A, Chuvilin A, et al. Probing low-energy hyperbolic polaritons in van der Waals crystals with an electron microscope. Nat Commun 2017;8:95.
Feng J, Deschout H, Caneva S, et al. Imaging of optically active defects with nanometer resolution. Nano Lett 2018;18:1739–44.
Kianinia M, Bradac C, Sontheimer B, et al. All-optical control and super-resolution imaging of quantum emitters in layered materials. Nat Commun 2018;9:874.
Hayee F, Yu L, Zhang JL, et al. Revealing multiple classes of stable quantum emitters in hexagonal boron nitride with correlated cathodoluminescence, photoluminescence, and strain mapping. arXiv e-prints 2019;arXiv:1901.05952.
Sushkov AO, Lovchinsky I, Chisholm N, Walsworth RL, Park H, Lukin MD. Magnetic resonance detection of individual proton spins using quantum reporters. Phys Rev Lett 2014;113:197601.
Actually, the original German quotation was even more colorful. Pauli called semiconductors a “Schweinerei” – a pigsty.